STUDY ON EVALUATION FOR UNDER-FILM CORROSION OFCOATED 2024T3 ALUMINUM ALLOY WITH EIS BY TIME DOMAIN METHOD
Yanling Hu;Di Li;Baolan Guo
北京航空航天大学材料工程系
Download:  PDF(218KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  In this article,EIS by Laplace transform time domai n method was used to evaluate under-film corrosion of coated 2024T3 aluminum all oy.EXCO immersion test,optical microscope observation and statistic method were also employed. Results show that EIS by time domain method is a quick,nondestructive and quanti tative method to detect under-film corrosion of 2024T3 Al alloy.The low frequenc y impedance (Rd),high frequency capacitance (Cg) can be treated as i ndicators of under-film corrosion.Correlation was established between Rd a nd Cg and corrosion states.Statistical analysis show that log(Rd) ma tch Gumbel distribution and log(Cg) correspond to normal distribution. Investigations show that different corrosion states have different dynamic rules .If only pitting occurs on the specimen,Rd and Cg fluctuates.When th e exfoliation happens,Rd will decrease and Cg will increase with tim e.Log(Rd),which reflect the most severe corrosion in large-scale specimen, will decrease exponentially with time in EXCO solution.
Key words:  aluminum alloy      coating      corrosion      electrochemical imped ance spectroscopy      statistics      
Received:  20 September 2000     
ZTFLH:  TG174.3  
  V250.2  
Corresponding Authors:  Yanling Hu   

Cite this article: 

Yanling Hu; Di Li; Baolan Guo. STUDY ON EVALUATION FOR UNDER-FILM CORROSION OFCOATED 2024T3 ALUMINUM ALLOY WITH EIS BY TIME DOMAIN METHOD. J Chin Soc Corr Pro, 2002, 22(1): 8-13 .

URL: 

https://www.jcscp.org/EN/     OR     https://www.jcscp.org/EN/Y2002/V22/I1/8

[1]DacresCM ,DavisGD ,KrebsLA ,etal.Theuseofelectro chemistryandellipsometryforidentifyingandevaluatingcorrosiononaircraft[A].AFOSR -TR -97/AF -A329519[C].
[2]AnthonyF .Sammells,BowersJS .Electrochemicalimpedancepat ternrecognitionfordetectionofhiddenchemicalcorrosiononair craftcomponent[A].AFOSR -94-0608TR/AD -A284998[C].
[3]ChangSW ,CaoChu′nan.ACimpedancemeasurementbyLaplacetransformtimedomainmethod[J].J .ofChineseSocietyforCorrosionandProtection,1984,4(1):1-20
(常守文,曹楚南.用拉普拉斯变换测量交流阻抗[J].中国腐蚀与防护学报,1984,4(1):1-20)
[4]WangJiangtao,LiuTingfang,GuHaoran.ElectrodeimpedancemeasurementbyFFTtimedomainmethod[J].J.ofChineseSoci etyforCorrosionandProtection,1988,8(3):173-181
(王江涛,刘挺芳,顾浩然.FFT时域法测量电极阻抗[J].中国腐蚀与防护学报,1988,8(3):173-181)
[5]HuXiche,YaoLuan,LuZongzhi.ACimpedancemeasurementbytimedomainmethod(Ⅰ)principleandtestingmethod(Ⅱ)resultsanddiscussion[J].J.ofChineseSocietyforCorrosionandProtec tion,1986,6(1):22-41
(胡细车,姚录安,鲁宗智.用时域法测量电极阻抗(Ⅰ)原理及测试方法(Ⅱ)实验结果与讨论[J].中国腐蚀与防护学报,1986,6(1):22-41)
[6]SongShizhe.MethodsinInvestigationofCorrosionElectrochemisty[M ],Beijing:ChemistryIndustryPress,1994
(宋诗哲.腐蚀电化学研究方法[M ].北京:化学工业出版社,1994)
[7]GrandleJA ,TaylorSR .Electrochemicalimpedancespectroscopyofcoatedaluminumbeveragecontainers,partⅠ—determinationofanoptimalparameterforlargesampleevaluation[J].Corrosion,1994,50(10):792-803
[8]LiFake,ZhangJiaquan,LiGuolai,etal.InvestigationfordiffusionofagentinpolymercoatingbyACimpedance[J].J .ofChineseSo cietyforCorrosionandProtection,1986,6(4):241-247
(李法科,张家权,李国莱等.交流法研究介质在高聚物涂层中的扩散行为[J].中国腐蚀与防护学报,1986,6(4):241-247)
[9]WenGuomou,CaiChangshou,LiuBihuan,etal.Evaluationforpro tectivepropertiesofcoatingswithelectrochemicalimpedancespec troscopy[J].J .ofChineseSocietyforCorrosionandProtection,1993,13(2):148-155
(温国谋,蔡长寿,刘碧环等.金属有机保护涂层的阻抗频谱评选参数[J].中国腐蚀与防护学报[J],1993,13(2):148-155)
[10]WalterGW .Areviewofimpedanceplotmethodsusedforcorro sionperformanceanalysisofpaintedmetals[J].Corros.Sci.,1986,26(9):681-703
[11]CaoChu′nan.CorrosionElectrochemistry[M ].Beijing:ChemistryIndustryPress,1994
(曹楚南.腐蚀电化学[M].北京:化学工业出版社,1994)
[12]HeGF .DataProcessforReliabilityandLifeEvaluation[M ].Bei jing:PressofBeijingUniversityofAeronauticsandAstronautics,1991
(贺国芳.可靠性数据处理与寿命评估[M ].北京:北京航空航天大学出版社,1991)
[13]HanYG .AppliedMathematicalStatistics[M ].Beijing:PressofBeijingUniversityofAeronauticsandAstronautics,1993
(韩於羹.应用数理统计[M ].北京:北京航空航天大学出版社,1993)
[14]ZhangJiuyuan,HongMinggeng,LuJianshu,etal.Acomparativestudyonthestatisticalpatternofpittingcorrosion[J].J .ofChi neseSocietyforCorrosionandProtection,1994,14(2):161-167
(张九渊,洪明庚,卢建树等.孔蚀统计规律的对比研究[J].中国腐蚀与防护学报,1994,14(2):161-167)
[15]HuYanling.CorrosionEvaluationandaMethodforLifePredictionofLY12CZAluminumAlloy[D].Beijing:GraduateSchoolofBei jingUniversityofAeronauticsandAstronautics,1999
(胡艳玲.LY12铝合金的腐蚀评估与寿命预测方法研究[D].北京:北京航空航天大学研究生院,1999)
[16]LiuDongning.Lifepredictionoffractionatingtowerformaximumpittingdepthbystatisticalmethod[J].CorrosionandProtection,1990,11(5):262-264
(刘东宁.用概率极值统计法预测分馏塔最大点蚀深度寿命[J].腐蚀与防护,1990,11(5):262-264)
[1] HUANG Peng, GAO Rongjie, LIU Wenbin, YIN Xubao. Fabrication of Superamphiphobic Surface for Nickel-plate on Pipeline Steel by Salt Solution Etching and Its Anti-corrosion Properties[J]. 中国腐蚀与防护学报, 2021, 41(1): 96-100.
[2] DONG Xucheng, GUAN Fang, XU Liting, DUAN Jizhou, HOU Baorong. Progress on the Corrosion Mechanism of Sulfate-reducing Bacteria in Marine Environment on Metal Materials[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[3] TANG Rongmao, ZHU Yichen, LIU Guangming, LIU Yongqiang, LIU Xin, PEI Feng. Gray Correlative Degree Analysis of Q235 Steel/conductive Concrete Corrosion in Three Typical Soil Environments[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[4] HAN Yuetong, ZHANG Pengchao, SHI Jiefu, LI Ting, SUN Juncai. Surface Modification of TA1 Bipolar Plate for Proton Exchange Membrane Fuel Cell[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[5] ZHANG Yuxuan, CHEN Cuiying, LIU Hongwei, LI Weihua. Research Progress on Mildew Induced Corrosion of Al-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[6] RAN Dou, MENG Huimin, LIU Xing, LI Quande, GONG Xiufang, NI Rong, JIANG Ying, GONG Xianlong, DAI Jun, LONG Bin. Effect of pH on Corrosion Behavior of 14Cr12Ni3WMoV Stainless Steel in Chlorine-containing Solutions[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[7] BAI Yunlong, SHEN Guoliang, QIN Qingyu, WEI Boxin, YU Changkun, XU Jin, SUN Cheng. Effect of Thiourea Imidazoline Quaternary Ammonium Salt Corrosion Inhibitor on Corrosion of X80 Pipeline Steel[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[8] ZUO Yong, CAO Mingpeng, SHEN Miao, YANG Xinmei. Effect of Mg on Corrosion of 316H Stainless Steel in Molten Salts MgCl2-NaCl-KCl[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[9] WANG Yating, WANG Kexu, GAO Pengxiang, LIU Ran, ZHAO Dishun, ZHAI Jianhua, QU Guanwei. Inhibition for Zn Corrosion by Starch Grafted Copolymer[J]. 中国腐蚀与防护学报, 2021, 41(1): 131-138.
[10] REN Yan, QIAN Yuhai, ZHANG Xintao, XU Jingjun, ZUO Jun, LI Meishuan. Effect of Thermal Shock on Mechanical Properties of Siliconized Graphite with ZrB2-SiC-La2O3/SiC Coating[J]. 中国腐蚀与防护学报, 2021, 41(1): 29-35.
[11] WANG Xintong, CHEN Xu, HAN Zhenze, LI Chengyuan, WANG Qishan. Stress Corrosion Cracking Behavior of 2205 Duplex Stainless Steel in 3.5%NaCl Solution with Sulfate Reducing Bacteria[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[12] SHI Kunyu, WU Weijin, ZHANG Yi, WAN Yi, YU Chuanhao. Electrochemical Properties of Nb Coating on TC4 Substrate in Simulated Body Solution[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[13] LIU Yang, WU Jinyi, YAN Xiaoyu, CHAI Ke. Effect of Bacillus flexus on Degradation of Polyurethane Varnish Coating in Marine Environment[J]. 中国腐蚀与防护学报, 2021, 41(1): 36-42.
[14] ZHENG Li, WANG Meiting, YU Baoyi. Research Progress of Cold Spraying Coating Technology for Mg-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[15] WEI Zheng, MA Baoji, LI Long, LIU Xiaofeng, LI Hui. Effect of Ultrasonic Rolling Pretreatment on Corrosion Resistance of Micro-arc Oxidation Coating of Mg-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
No Suggested Reading articles found!