Ti6Al4V合金离子渗Mo组织结构及其腐蚀性能研究

范爱兰;秦妍梅;秦林;常大庆; 唐宾

太原理工大学

Study on Structure and Corrosiion Behavior of Mo Diffusion Layers on Ti-6Al-4V Alloy with Plasma Surface Alloying Technique

;;;;

太原理工大学

全文: PDF(644 KB)

摘要: 利用等离子表面合金化技术在Ti6Al4V合金基体上制备渗Mo改性层，并与Ti6Al4V基材对比考察在05 mol/L HCl溶液中的电化学腐蚀性能及在沸腾的37%HCl中的化学腐蚀性能.结果表明，与基材相比Mo改性层在05 mol/L HCl溶液中的自腐蚀电位提高，腐蚀速率增大；在37%HCl中腐蚀速率明显降低.

关键词 ： Ti6Al4V, Mo改性层, 腐蚀性能

Abstract：The Mo surface modified layer on Ti6Al4V substrate was obtained by the plasma surface alloying technique.The structure and composition of the Mo surface modified layer were investigated by X-ray diffraction (XRD) and glow discharge optical emission spectroscopy (GDOES).The duplex Mo modified layer contains a pure Mo coating on subsurface and diffusion layers between the subsurface and substrate.The X- ray diffraction analysis of the Mo modified layer reveals that a Mo phase exists in the modified layer with〈110〉and 〈211〉orientations in the subsurface.The electrochemical corrosion behavior in 0.5 mol/L HCl solution of the Mo modified layer was investigated and compared with that of Ti6Al4V substrate material.The chemical corrosion behavior in boiling 37% HCl solution of the Mo modified layer was investigated and compared with that of Ti6Al4V substrate material.Results indicate that self-corroding electric potentials and corrosion rate of the Mo modified layer are higher than those of Ti6Al4V substrate in 0.5 mol/L HCl solution.Corrosion rate of the Mo modified layer is lower than that of Ti6Al4V substrate material in 37% HCl.

Key words： Ti6Al4V Mo modified layer corrosion behaviors

收稿日期: 2005-08-12

ZTFLH:

TG115.22

通讯作者: 范爱兰 E-mail: fanailan@tyut.edu.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	范爱兰
	秦妍梅
	秦林
	常大庆
	唐宾
44.8K

引用本文:

范爱兰; 秦妍梅; 秦林; 常大庆; 唐宾 . Ti6Al4V合金离子渗Mo组织结构及其腐蚀性能研究[J]. 中国腐蚀与防护学报, 2007, 27(1): 31-34 .

链接本文:

https://www.jcscp.org/CN/Y2007/V27/I1/31

[1]Ji H B,Xia L F,Ma X X,et al.Tribological behavior of differentfilms on Ti-6Al-4Valloy prepared by plasma-based ion implan-tation[J].Trans.Nonferrous Met.Soc.China,2000,10(4):493-497
[2]Budinski K G.Tribological properties of titanium alloys[J].Wear,1991,151:203-217
[3]Liu F L,Li J G,Feng Z X.Evolution of surface technologies for tita-nium alloys[J].Corros.Prot.,2001,22(2):54-57(刘凤岭,李金桂,冯自修.钛合金表面技术的进展[J].腐蚀与防护,2001,22(2):54-57)
[4]Dong H,Bloyce A,Morton P H,et al.Surface engineering to improvetribological performance of Ti6-Al4-V[J].Surf.Eng.,1997,13(5):402-406
[5]Li X Y,Fan AL,Tang B,et al.Tribological behavior of molybdenumalloying layer on Ti6Al4V by double glow discharge technique[J].Tribology,2003,23(2):108-111(李秀燕,范爱兰,唐宾等.Ti6Al4V表面双层辉光离子渗Mo及其摩擦学性能的研究[J].摩擦学学报.2003,23(2):108-111)
[6]Tang B,Wu P Q,Li X Y,et al.Tribological behavior of plasma Mo-N surface modified Ti6-Al4-V alloy[J].Surf.Coat.Technol.,2004,179:333-339

[1]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[2]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[3]	沈树阳, 王东胜, 孙士斌, 杨剔, 赵前进, 王鑫, 张亚飞, 常雪婷. 深冷处理对EH40极寒环境船用钢板的海水腐蚀性能影响[J]. 中国腐蚀与防护学报, 2020, 40(2): 151-158.
[4]	张瑞,李雨,关蕾,王冠,王福雨. 热处理对激光选区熔化Ti6Al4V合金电化学腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 588-594.
[5]	欧阳跃军,胡婷,王佳音,谢治辉. 镁合金表面层状双氢氧化物的电化学沉积和表征[J]. 中国腐蚀与防护学报, 2019, 39(5): 453-457.
[6]	史昆玉,张进中,张毅,万毅. Nb₂N涂层制备及其耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 313-318.
[7]	常亮, 师超, 邵亚薇, 王艳秋, 刘斌, 孟国哲. 植酸转化膜对环氧清漆防腐性能的影响[J]. 中国腐蚀与防护学报, 2018, 38(3): 265-273.
[8]	蒋光锐, 刘广会. Zn-Al-Mg合金的凝固组织及其耐腐蚀性能[J]. 中国腐蚀与防护学报, 2018, 38(2): 191-196.
[9]	王越, 刘子利, 刘希琴, 章守东, 田青超. 热轧态Cr、Ni微合金化高强度耐候钢组织与耐蚀性能[J]. 中国腐蚀与防护学报, 2018, 38(1): 39-46.
[10]	耿振伟,肖代红. Zn对挤压态Mg-13Gd-2Cu合金的显微组织及腐蚀性能影响[J]. 中国腐蚀与防护学报, 2016, 36(6): 595-603.
[11]	周兵, 唐囡, 张颖君, 毛亮, 王艳秋, 邵亚薇, 孟国哲. 镀锌钢表面高附着环氧清漆的研究[J]. 中国腐蚀与防护学报, 2015, 35(5): 455-460.
[12]	刘子利, 刘希琴, 王怀涛, 胡金东, 侯志国. Ti对Zn-5Al合金组织及耐腐蚀性能的影响[J]. 中国腐蚀与防护学报, 2014, 34(6): 515-522.
[13]	张金龙, 屠礼明, 谢兴飞, 姚美意, 周邦新. Zr-1Nb-xGe合金在400 ℃过热蒸汽中耐腐蚀性能的研究[J]. 中国腐蚀与防护学报, 2014, 34(2): 171-177.
[14]	赵凯尹志民段佳琦邓英. 时效处理工艺对1975合金腐蚀性能的影响[J]. 中国腐蚀与防护学报, 2013, 33(2): 153-158.
[15]	刘子利,朱晓春,周桂斌,李健. Sb对Mg-5Al-2Sr合金耐腐蚀性能的影响[J]. 中国腐蚀与防护学报, 2012, 32(6): 478-484.

Viewed

Full text

Abstract

Cited

Shared

Discussed