Cr颗粒尺寸对Ni-Cr复合镀层氧化行为的影响

张艳;张春林;彭晓;王福会

EFFECT OF Cr PARTICLE SIZE ON THE OXIDATION BEHAVIOUR OF ELECTRODEPOSITED Ni-Cr COMPOSITE COATINGS

;;;

全文: PDF(174 KB)

摘要: 利用Ni与不同粒度的Cr颗粒通过复合电镀的方法分别制备了Ni-7.5Cr (平均粒度为21nm)、Ni-10.9Cr (平均粒度为39nm) 和Ni-12.4Cr (平均粒度为2.4µm)的复合镀层。Ni-Cr纳米复合镀层与Ni-Cr微米颗粒镀层相比，其颗粒分布更为均匀，颗粒间距减少2—3个数量级。900℃恒温氧化实验结果表明：复合微米颗粒的Ni-Cr镀层只形成NiO膜，不能形成连续的Cr2O3膜，氧化速率很快；而Ni-Cr纳米复合镀层，由于能形成连续的Cr2O膜，氧化速率显著降低，并且这种颗粒尺寸效应随粒度越细越明显。文中对颗粒尺寸效应进行了探讨。

关键词 ：电沉积, Ni-Cr复合镀层, 纳米颗粒效应, 氧化

Abstract：Ni-7.5Cr,、Ni-10.9Cr、Ni-12.4Cr composites were prepared by means of co-electrodeposition of Ni matrix with three kinds of Cr particles in average size of 21 nm,39 nm, and 2.4µm, respectively. Compared to the electrodeposited microparticles-dispered composite coating (EMCC), the electrodeposited nanoparticles-dispered nanocomposite coatings (ENNCs) exhibits more homogeneous distribution of Cr particles and the interparticle spacing is approximately two orders of magnitude lower. The ENNCs have a very low oxidation rate at 900℃, due to the rapid formation of a continuous and compact chromia scale, whereas the EMCC exhibits a very poor oxidation resistance, due to the formation of porous NiO scale. For the ENNCs, the finer the Cr particles codeposited, the better the oxidation performance. The particles size effect on the oxidation behaviour of electrodeposited Ni-Cr composites is also discussed.

Key words： Electrodeposition Ni-Cr composite coating particle size effect oxidation

收稿日期: 2005-03-16

ZTFLH:

TG174.44

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	张艳
	张春林
	彭晓
	王福会
44.8K

引用本文:

张艳; 张春林; 彭晓; 王福会 . Cr颗粒尺寸对Ni-Cr复合镀层氧化行为的影响[J]. 中国腐蚀与防护学报, 2006, 26(2): 85-88 .
. EFFECT OF Cr PARTICLE SIZE ON THE OXIDATION BEHAVIOUR OF ELECTRODEPOSITED Ni-Cr COMPOSITE COATINGS. J Chin Soc Corr Pro, 2006, 26(2): 85-88 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2006/V26/I2/85

[1]Atkinson H V.A review of the role of short-circuit diffusion inthe oxidation of nickel,chromium and nickel-chromium alloys[J].Oxid.Met.,1985,24:177-197
[2]Goward G W.Overview protective coatings-purpose role and de-sign[J].Mater.Sci.Technol.,1986,2:194-199
[3]Peng X,Ping D,Li T,et al.Oxidation behaviour of a Ni-La2O3codeposited film on nickel[J].J.Electrochem.Soc.,1998,145:389-398
[4]Goward G W,Boone D H.Mechansims of formation of diffusionaluminide coatings on nickel-base superalloys[J].Oxid.Met.,1971,3:475-481
[5]Nicholls J R,Hancocl P,Al-Yasiri L H.Optimising oxidation re-sistance of MCrAl coating systems using vapour phase alloy design[J].Mater.Sci.Technol.,1989,5:799-808
[6]Wang F,Lou H.Oxidation behaviour and scale morphology of nor-mal-grained CoCrAl alloy and its sputtered microcrystalline coat-ing[J].Mater.Sci.Eng.,1990,A129:279-285
[7]Lou H,Zhu S,Wang F,et al.Rehealing ability of oxide scaleformed on microcrystalline K38G coating[J].Oxid.Met.,1995,43:317-329
[8]Zhang Y,Peng X,Wang F.Development and oxidation at 800℃ofa novel electrodeposited Ni-Cr nanocomposite film[J].Mater.Lett.,2004,58:1134-1138
[9]Zhou Y,Peng X,Wang F.Oxidation of a novel electrodeposited Ni-Al nanocomposite film at 1050℃[J].Scr.Mater.,2004,50:1429-1423

[1]	魏征, 马保吉, 李龙, 刘潇枫, 李慧. 镁合金表面超声滚压预处理对微弧氧化膜耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[2]	包任, 周根树, 李宏伟. 恒电位脉冲电沉积高锡青铜耐蚀镀层工艺研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 585-591.
[3]	刘晓, 王海, 朱忠亮, 李瑞涛, 陈震宇, 方旭东, 徐芳泓, 张乃强. 电站用奥氏体耐热钢HR3C与Sanicro25在超临界水中的氧化特性[J]. 中国腐蚀与防护学报, 2020, 40(6): 529-538.
[4]	谢冬柏, 洪昊, 王文, 彭晓, 多树旺. 模拟燃烧环境介质和温度对不锈钢表面氧化物形态的影响研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 358-366.
[5]	曹京宜, 方志刚, 陈晋辉, 陈志雄, 殷文昌, 杨延格, 张伟. 5083铝合金表面单致密微弧氧化膜的制备及其性能研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[6]	王廷勇, 董如意, 许实, 王辉. 石墨烯改性Ti/IrTaSnSb-G金属氧化物阳极在低温和低盐NaCl溶液中的电化学性能[J]. 中国腐蚀与防护学报, 2020, 40(3): 289-294.
[7]	方旭东, 刘晓, 徐芳泓, 李瑞涛, 朱忠亮, 张乃强. 超超临界电站国产奥氏体钢C-HRA-5在超临界水中的氧化特性[J]. 中国腐蚀与防护学报, 2020, 40(3): 266-272.
[8]	王英君, 刘洪雷, 王国军, 董凯辉, 宋影伟, 倪丁瑞. 新型高强稀土Al-Zn-Mg-Cu-Sc铝合金的阳极氧化及其抗腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 131-138.
[9]	秦越强, 左勇, 申淼. FLiNaK-CrF₃/CrF₂氧化还原缓冲熔盐体系对316L不锈钢耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(2): 182-190.
[10]	郑艳欣, 刘颖, 宋青松, 郑峰, 贾玉川, 韩培德. 含铁铜基陶瓷复合材料高温氧化行为与耐磨性研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 191-198.
[11]	范益,陈林恒,蔡佳兴,代芹芹,马宏驰,程学群. 热轧AH36船板钢在室内仓储条件下的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 10-16.
[12]	杨寅初,傅秀清,刘琳,马文科,沈莫奇. 喷射电沉积Ni-P-BN(h)-Al₂O₃复合镀层的耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 57-62.
[13]	徐勋虎,何翠群,向军淮,王玲,张洪华,郑晓冬. Co-20Re-25Cr-1Si合金在0.1 MPa纯O₂中的高温氧化行为[J]. 中国腐蚀与防护学报, 2020, 40(1): 75-80.
[14]	姜冬雪,付颖,张峻巍,张伟,辛丽,朱圣龙,王福会. 钛合金表面Al₂O₃陶瓷膜制备及性能研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 469-476.
[15]	王毅,张盾. 铋系可见光催化海洋防污材料研究进展[J]. 中国腐蚀与防护学报, 2019, 39(5): 375-386.

Viewed

Full text

Abstract

Cited

Shared

Discussed