青铜文物表面腐蚀产物的组成及深度分布研究

中国腐蚀与防护学报

2005, Vol. 25

Issue (3): 163-166

研究报告

本期目录 | 过刊浏览

青铜文物表面腐蚀产物的组成及深度分布研究

王菊琳;许淳淳;于淼

北京化工大学

CORROSION PRODUCTION ON ARCHAEOLOGICAL BRONZE SURFACE AND ITS DISTRIBUTION WITH DEPTH

;;

北京化工大学

全文: PDF(135 KB)

摘要: 青铜在模拟环境介质中的循环伏安实验及XRD测试结果表明，氧化过程主要为生成有害锈CuCl的过程，还原过程主要为CuCl还原成纯铜晶粒的过程，并且反应电流较大，对青铜基体的破坏性较大.运用高性能二次离子质谱(SIMS)观测到不同腐蚀电位下青铜表面腐蚀产物中均含有Cu、Sn、Cl、O、C、S元素，阴离子相对含量由大到小为Cl、O、C、S；腐蚀产物层由表及里Cu/Sn值始终小于合金中Cu/Sn，并且Cu离子含量基本不变，Sn离子含量有起伏，Cl、O离子含量有所下降.

关键词 ：二次离子质谱, 青铜文物, 环境, 腐蚀

Abstract：The results of cycle voltammetry(CV) experimentation in simulated environment medium and XRD test are that main oxidation process is harmful patina CuCl formation and reduction process is CuCl reduced or deoxidised to pure Cu.The reaction current is so high that severely damages to bronze substrate.When bronze was corroded respectively at several potentials there exist elements Cu,Sn,Cl,O,C,S in corrosion production on bronze surface with SIMS observation.From high to low the relative content of anions is Cl,O,C,S.Cu/Sn value from outside and in corrosion production is always less than that in alloy.The relative content of Cu is basically stead,Sn fluctuates,Cl or O a little falls.

Key words： SIMS archaeological bronze environment corrosion

收稿日期: 2003-12-24

ZTFLH:

TG174

通讯作者: 王菊琳

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	王菊琳
	许淳淳
	于淼
44.8K

引用本文:

王菊琳; 许淳淳; 于淼 . 青铜文物表面腐蚀产物的组成及深度分布研究[J]. 中国腐蚀与防护学报, 2005, 25(3): 163-166 .

链接本文:

https://www.jcscp.org/CN/Y2005/V25/I3/163

[1]RobbiolaL,BlenginoJ,FiaudC.Morphologyandmechanismoffor mationofnaturalpatinasofarchaeologicalCu-Snalloys[J].Cor ros.Sci.,1998,40(12):2083
[2]ChenYuansheng,XieYulin.Studiesonmuseumenvironmentstan dards[J].SciencesofConservationandArchaeology,2002,14(12):152(陈元生,解玉林.博物馆文物保存环境质量标准研究[J].文物保护与考古科学,2002,14(12),152)
[3]DavidAScott.Anexaminationofthepatinaandcorrosionmorphol ogyofsomeromanbronzes[J].J.theAmericanInstituteforCon servation,1994,33(1):1
[4]BenninghovenA,RudenauderFG,WernerHW.SecondaryIonMassSpectrometry[M].JohnWiley&Sons,1987
[5]ChaLZ,LuJH,ChenCY.ModernAnalyzingTechnology[M].Beijing:QinghuaUniversityPublishingCompany,1995(查良镇,陆家和,陈长彦.现代分析技术[M].北京:清华大学出版社,1995)
[6]ChaLZ,GuiD,ZhuYJ.Latestprogressinsecondaryionmass spectroscopy[J].VacuumScienceandTechnology(China),2001,21(2):129(查良镇,桂东,朱怡静.二次离子质谱的新进展[J].真空科学与技术,2001,21(2):129)
[7]HallettK,ThickettD,McPhailDS.ApplicationofSIMStosilver tarnishattheBritishmuseum[J].AppliedSurfaceScience,2003,203-204:789
[8]GasparP,HubbardC,McPhailDS.Topographicalassessmentand comparisonofconservationcleaningtreatments[A].Acceptedfor theProceedingsofLacona(lasersinconservationofartworks)IV[C].Lacona,2001
[9]SokhanM,GasparP,McPhailDS.Initialresultsonlasercleaningat theVictoriaandAlbertmuseum,naturalhistorymuseumandtate gallery[A].AcceptedfortheProceedingsofLacona(lasersincon servationofartworks)IV[C].Lacona,2001
[10]ConstantinidesI,AdriaensA,AdamsF.Surfacecharacterizationof artificialcorrosionlayersoncopperalloyreferencematerials[J].Ap pliedSurfaceScience,2002,90-101:189
[11]XuChunchun,WangJulin.Investigationofthechemicalandelec trochemicalbehaviourofmasstransferatanarchaeologicalbronze/soilinterface[J].Anti-CorrosionMethodsandMaterials.2003,50(5):326
[12]LiangHD,YuCH,ZhouQ.SIMSstudiesonsinglegraininfur nacedustofsteelfactory[J].MiningSafetyandEnvironmentPro tection,2001,28(3):4(梁汉东,于春海,周强.钢铁厂平炉尘单颗粒物的二次离子质谱研究[J].矿业安全与环保.2001,28(3):4)
[13]ZhaoJ,LuHQ,LiXY.SIMSanalysisonTe-Cd-Hgbodyma terialinjectedbyAsion[J].J.InfraredMillim.Waves,2000,19(4):281(赵军,陆慧庆,李向阳.砷离子注入体材料碲镉汞的二次离子质谱分析[J].红外与毫米波学报,2000,19(4):281)

[1]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[4]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[5]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[6]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[7]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[8]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[9]	刘洋, 吴进怡, 闫小宇, 柴柯. 海洋环境中芽孢杆菌对聚氨酯清漆涂层分解的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 36-42.
[10]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[11]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[12]	孙海静, 覃明, 李琳. 深海低溶解氧环境下Al-Zn-In-Mg-Ti牺牲阳极性能研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 508-516.
[13]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[14]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[15]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.

Viewed

Full text

Abstract

Cited

Shared

Discussed