中国腐蚀与防护学报  2011, Vol. 31 Issue (6): 457-461    
  研究报告 本期目录 | 过刊浏览 |
NF616和12CrMoV在模拟垃圾气化环境中的高温腐蚀
潘太军1,陈德贵1,张轲2,胡静1
1. 常州大学材料科学与工程学院 常州市高性能金属材料重点实验室常州 213164
2.沈阳师范大学化学工程学院 沈阳 110034
HIGH TEMPERATURE CORROSION OF NF616 AND 12CrMoV IN SIMULATED WASTE-GASIFICATION ENVIROMENTS
PAN Taijun1, CHEN Degui1, ZHANG Ke2, HU Jing1
1. Key Laboratory of Advanced Metallic Materials of Changzhou, School of Material Science and Engineering, Changzhou University, Changzhou 213164
2. Department of Chemistry, Shenyang Normal University, Shenyang, 110034
全文: PDF(932 KB)  
摘要: 研究比较了600℃时NF616和12CrMoV两种工业钢分别在3种还原性气氛(H2-CO2、 H2-HCl-CO2和H2--HCl-H2S-CO2)中的腐蚀行为。与在H2-CO2和H2-HCl-CO2气氛中的腐蚀相比,NF616和12CrMoV在H2-HCl-H2S-CO2气氛中发生了加速腐蚀,尤其是12CrMoV表面氧化铬膜发生退化,金属的加速腐蚀主要是由腐蚀过程中形成金属硫化物和氯化物所致,文中依据热力学相图讨论了材料发生加速腐蚀的机制。
关键词 高温腐蚀内氧化    
Abstract:The corrosion behavior of two commercial steels NF616 and 12CrMoV was comparatively investigated at 600℃ in H2-CO2, H2-HCl-CO2 and H2-HCl-H2S-CO2 reducing atmospheres. In comparison with corrosion behavior of the same-type steels in H2-CO2 and H2-HCl-CO2 reducing atmosphere, NF616 and 12CrMoV suffered from accelerated corrosion in the H2-HCl-H2S-CO2 atmosphere, particularly the degradation of chromia formed on 12CrMoV. The kind of accelerated corrosion was mainly attributed to formation of metal chlorides and sulfides during corrosion procedure. The mechanism on accelerated corrosion is illuminated on the basis of thermodynamic diagrams.
Key wordssulfur    chlorine    high temperature corrosion    internal oxidation
收稿日期: 2010-08-30     
ZTFLH: 

TG172

 
基金资助:

国家自然科学基金项目(51101023)和常州市工业科技项目(CN20100009)资助

通讯作者: 潘太军     E-mail: tjpan2005@gmail.com
作者简介: 潘太军,男,1977年生,博士,副教授,研究方向为材料腐蚀与防护

引用本文:

潘太军,陈德贵,张轲,胡静. NF616和12CrMoV在模拟垃圾气化环境中的高温腐蚀[J]. 中国腐蚀与防护学报, 2011, 31(6): 457-461.
PAN Ta-Jun. HIGH TEMPERATURE CORROSION OF NF616 AND 12CrMoV IN SIMULATED WASTE-GASIFICATION ENVIROMENTS. J Chin Soc Corr Pro, 2011, 31(6): 457-461.

链接本文:

https://www.jcscp.org/CN/      或      https://www.jcscp.org/CN/Y2011/V31/I6/457

[1] Spiegel M, Grabke H J.High temperature corrosion of high alloy steels in simulated waste incineration environments[J]. Mater. Corros., 1996,47:179-189

[2] Miller P D, Krouse H H. The mechanism in high temperature corrosion in municipal incinerators[J]. Corrosion, 1972, 28: 274-281

[3] Pan T J, Lin Y F, Hu J. Accelerated corrosion behavior of Fe-Al alloys under KCl-ZnCl2 deposits[J].J. Chin. Soc. Corros.Prot., 2010, 30: 58-61

    (潘太军, 林一凡, 胡静. Fe-Al合金在KCl-ZnCl2沉积盐作用下的加速腐蚀行为,中国腐蚀与防护学报, 2010, 30: 58-61)

[4] Li Y S,  Niu Y, Wu W T. Corrosion behavior of pure Cr and two Cr-containing alloys beneath ZnCl2 and KCl-ZnCl2 deposits [J]. J. Chin. Soc. Corros. Prot., 2002, 22: 27-31

    (李远士, 牛焱,吴维tao.纯Cr和两种含Cr合金在ZnCl2及KCl-ZnCl2盐膜下的腐蚀,中国腐蚀与防护学报, 2002, 22: 27-31)

[5] Zahs A, Spiegel M, Grabke H J. Chlorination and oxidation of iron, chromium, nickel, and their alloys in chloridizing and oxidizing atmospheres at 400-700℃[J]. Corros. Sci., 2000, 42:1093-1122

[6] Schulte M, Rahmel A, Schutze M. The sulfidation behavior of several commercial ferritic and austenitic steels[J]. Oxid. Met.,1998, 49: 33-70

[7] Pan T J, Al-Omary M, Zeng C L, et al. The corrosion of three commercial steels in reducing atmospheres containing HCl and H2S at 873 K[J]. High Temp. Mater. Proc., 2005, 24: 193-203

[8] Pan T J, Gesmundo F, Niu Y. Corrosion behavior of three iron based model alloys in reducing atmospheres containing HCl and H2S at 600℃[J]. Corros. Sci., 2007, 49: 1362-1377

[9] Li Y S, Niu Y, Liu G. High temperature corrosion of metallic materials in waste incineration  environment[J]. Corros. Sci. Prot. Technol., 2000, 12: 224-227

    (李远士, 牛焱, 刘刚等.金属材料在垃圾焚烧环境中的高温腐蚀, 腐蚀科学与防护技术, 2000, 12:224-227)

[10] Hou P Y, Pruner K, Fairbrother D H, et al. Sulfur segregation to deposited Al2O3 film/alloy interface at 1000SDC[J]. Scr. Mater., 1999, 40: 241-247

[11] Hou P Y, Zhang X F, Cannon R M. Impurity distribution in Al2O3 formed on an FeCrAl alloy[J]. Scr. Mater., 2004, 50:45-49
[1] 董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2] 白云龙, 沈国良, 覃清钰, 韦博鑫, 于长坤, 许进, 孙成. 硫脲基咪唑啉季铵盐缓蚀剂对X80管线钢腐蚀的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[3] 左勇, 曹明鹏, 申淼, 杨新梅. MgCl2-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[4] 王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[5] 谢冬柏, 洪昊, 王文, 彭晓, 多树旺. 模拟燃烧环境介质和温度对不锈钢表面氧化物形态的影响研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 358-366.
[6] 赵博儒, 孙志, 赵健伟, 陈智栋. 正十六硫醇分子在Ag表面的自组装动力学及其保护作用[J]. 中国腐蚀与防护学报, 2020, 40(3): 281-288.
[7] 蒋旭光, 刘晓博. 垃圾焚烧锅炉关键受热面腐蚀研究进展及方向思考[J]. 中国腐蚀与防护学报, 2020, 40(3): 205-214.
[8] 李向红, 邓书端, 徐昕. 木薯淀粉三元接枝共聚物对钢在H2SO4溶液中的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 105-114.
[9] 陈旭, 李帅兵, 郑忠硕, 肖继博, 明男希, 何川. X70管线钢在大庆土壤环境中微生物腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 175-181.
[10] 刘志峰,朱志平,石纯,黄赵鑫. 载流法制备硫酸露点腐蚀模拟气体的试验研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 1-9.
[11] 徐勋虎,何翠群,向军淮,王玲,张洪华,郑晓冬. Co-20Re-25Cr-1Si合金在0.1 MPa纯O2中的高温氧化行为[J]. 中国腐蚀与防护学报, 2020, 40(1): 75-80.
[12] 陈旭,马炯,李鑫,吴明,宋博. 温度与SRB协同作用下X70钢在海泥模拟溶液中应力腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 477-483.
[13] 戚鹏, 万逸, 曾艳, 郑来宝, 张盾. 海洋环境中硫酸盐还原菌的快速测定方法研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 387-394.
[14] 余仁强,何建军,李微,任延杰,杨旺. 火电厂循环泵叶轮材料Cr30A在脱硫浆液腐蚀环境中的交互损伤失效行为研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 353-358.
[15] 吴堂清,周昭芬,王鑫铭,张德闯,尹付成,孙成. 微生物致裂的热力学和动力学分析[J]. 中国腐蚀与防护学报, 2019, 39(3): 227-234.