表面状态对690TT合金腐蚀及应力腐蚀行为的影响

张志明,王俭秋,韩恩厚,柯伟

中国科学院金属研究所金属腐蚀与防护重点实验室沈阳 110016

EFFECTS OF SURFACE CONDITION ON CORROSION AND STRESS CORROSION CRACKING OF ALLOY 690TT

ZHANG Zhiming, WANG Jianqiu,HAN En-Hou, KE Wei

State Key laboratory for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016

全文: PDF(1113 KB)

摘要: 采用扫描电镜、原子力显微镜和表面粗糙度测量仪对具有不同表面状态的690TT合金表面形貌进行了表征与比较。采用零电荷电位测量、动电位扫描和电化学快慢扫描等方法对不同的690TT合金的腐蚀行为进行了比较。结果表明，与机械抛光样品相比较，打磨样品表面起伏较严重，拥有更大的表面粗糙度值；在相同的腐蚀环境中，打磨样品比机械抛光样品表现出更大的腐蚀速度和更高的应力腐蚀开裂敏感性。分析认为，单纯的表面较大粗糙度和残余应变均能够促进690TT合金的腐蚀。实验中打磨690TT样品表现出的较高腐蚀速度和应力腐蚀开裂敏感性是由其较大的表面粗糙度和表面残余应变综合影响结果。

关键词 ： 690TT合金, 表面状态, 应力腐蚀, 电化学

Abstract：The scanning electron microscopy (SEM), atomic force microscopy (AFM) and surface profilometry were employed to characterize the surface conditions of Alloy 690TT samples. The corrosion behaviors of Alloy 690TT samples with different surface conditions were compared by potential of zero charge (PZC), potentiodynamic polarization curves and electrochemical fast and slow scan. The experiment results showed that the surfaces ground to 400# were much rougher than the mechanically polished surfaces and surface roughness of the former was bigger than the latter. The corrosion rate of the ground surfaces was bigger and the ground surfaces were more sensitive to stress corrosion cracking (SCC), compared with the mechanically polished surfaces in the same corrosive environment. That corrosion of Alloy 690TT could be accelerated by single surface roughness or single surface residual strain. The difference of corrosion rate and the sensitivity of SCC in this experiment were affected by surface roughness and surface residual strain simultaneously.

Key words： alloy 690TT surface condition stress corrosion cracking (SCC) electrochemistry

收稿日期: 2010-08-23

ZTFLH:

TG174.1

基金资助:

国家重点基础研究发展计划项目(G2006CB60500)资助

通讯作者: 王俭秋 E-mail: wangjianqiu@imr.ac.cn

Corresponding author: WANG Jianqiu E-mail: wangjianqiu@imr.ac.cn

作者简介: 张志明，男，1983年生，博士生，研究方向为核电关键材料的力学与化学交互作用

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	张志明
	王俭秋
	韩恩厚
	柯伟
44.8K

引用本文:

张志明,王俭秋,韩恩厚,柯伟. 表面状态对690TT合金腐蚀及应力腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2011, 31(6): 441-445.
ZHANG Zhi-Meng, YU Jian-Qiu, HAN En-Hou, KE Wei. EFFECTS OF SURFACE CONDITION ON CORROSION AND STRESS CORROSION CRACKING OF ALLOY 690TT. J Chin Soc Corr Pro, 2011, 31(6): 441-445.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2011/V31/I6/441

[1] Dutta R S. Corrosion aspects of Ni-Cr-Fe based and Ni-Cu based steam generator tube materials [J]. J. Nucl. Mater., 2009,393: 343-349

[2] MacDonald P E, Shah V N, Ward L W, et al. Steam generator tube failures [R]. NUREG/CR-6365

[3] Staehle R W, Gorman J A. Quantitative assessment of submodes of stress corrosion cracking on the secondary side of steam generator tubing in pressurized water reactors: Part1 [J].Corrosion, 2003, 59(11): 931-994

[4] Ahn S V, Rao S K, Kwon H S, et al. Effects of PbO on the repassivation kinetics of alloy 690 [J]. Corros. Sci., 2006, 48:1137-1153

[5] Fang Z, Staehle R W. Effects of the valence of sulfur on passivation of Alloys 600,690 and 800 at 25℃ and 95℃ [J].Corrosion, 1999, 55(4): 355-379

[6] Staehle R W. In: Scully J C, ed. Stress corrosion cracking of the Fe-Cr-Ni alloy system, in The Theory of Stress Corrosion Cracking in Alloys [M]. Brussels, Belgium: NATO Scientific Affairs Division, 1971: 223

[7] White R E, Bockris J O, Conway B E. Modern Aspects of Electrochemistry (No.33)[M]. New York: Plenum Publishers, 1999

[8] Li W, Li D Y. Influence of surface morphology on corrosion and electronic behavior [J]. Acta Mater., 2006, 54: 445-452

[9] Zhang Z Z, Wang J, Han E H, et al. Characterization of different surface state and its effect on the oxidation behaviors alloy 690TT [J]. J. Mater. Sci. Technol., Accepted

[10] Large D, Sabot R , Feaugas X. Influence of stress-strain field on the dissolution process of polycrystalline nickel in H₂SO₄ solution: An original in situ method [J].Electrochim. Acta, 2007, 52: 7746-7753

[11] Ziemniak S E., Hanson M, Sander P C. Electropolishing effects on corrosion behavior of 304 stainless steel in high temperature, hydrogenated water [J]. Corros. Sci., 2008 50:2465-2477

[12] Li W, Li D Y. Variations of work function and corrosion behaviors of deformed copper surfaces [J]. Appl. Surf. Sci., 2005,240: 388-395

[13] Gutman E M. Mechanochemistry of Solid Surfaces [M]. NewJersey/Singapore/London: World Scientific Publicaiton, 1994: 332

[1]	戴婷, 顾艳红, 高辉, 刘凯龙, 谢小辉, 焦向东. 水下摩擦螺柱焊接头在饱和CO₂中的电化学性能[J]. 中国腐蚀与防护学报, 2021, 41(1): 87-95.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[4]	白云龙, 沈国良, 覃清钰, 韦博鑫, 于长坤, 许进, 孙成. 硫脲基咪唑啉季铵盐缓蚀剂对X80管线钢腐蚀的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[5]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[6]	孙海静, 覃明, 李琳. 深海低溶解氧环境下Al-Zn-In-Mg-Ti牺牲阳极性能研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 508-516.
[7]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[8]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[9]	艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.
[10]	翟思昕, 杨幸运, 杨继兰, 顾剑锋. 淬火-配分-回火钢在模拟海水环境中的腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 398-408.
[11]	白海涛, 杨敏, 董小卫, 马云, 王瑞. CO₂腐蚀产物膜的研究进展[J]. 中国腐蚀与防护学报, 2020, 40(4): 295-301.
[12]	李清, 张德平, 李晓荣, 王薇, 孙宝壮, 艾池. TP110TS和P110钢在CO₂注入井环空环境中应力腐蚀行为比较[J]. 中国腐蚀与防护学报, 2020, 40(4): 302-308.
[13]	李清, 张德平, 王薇, 吴伟, 卢琳, 艾池. L80油管钢实际腐蚀状况评估及室内电化学和应力腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 317-324.
[14]	朱丽霞, 贾海东, 罗金恒, 李丽锋, 金剑, 武刚, 胥聪敏. 外加电位对X80管线钢在轮南土壤模拟溶液中应力腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 325-331.
[15]	付海波, 刘晓茹, 孙媛, 曹大力. 环氧树脂/重结晶碳化硅复合材料的抗腐蚀性能[J]. 中国腐蚀与防护学报, 2020, 40(4): 373-380.

Viewed

Full text

Abstract

Cited

Shared

Discussed