中国腐蚀与防护学报  2011, Vol. 31 Issue (2): 86-90    
  综述 本期目录 | 过刊浏览 |
湿气管线的顶部腐蚀研究概况
蒋秀,屈定荣,刘小辉
中国石油化工股份有限公司青岛安全工程研究院 青岛 266071
RESEARCH DEVELOPMENT OF TOP OF LINE CORROSION(TLC) IN WET NATURAL GAS PIPELINES
JIANG Xiu, QU Dingrong, LIU Xiaohui
Qingdao Research Institute of Safety Engineering, China Petroleum and Chemical Corporation, Qingdao 266071
全文: PDF(475 KB)  
摘要: 本文对天然气输送工业湿气管线顶部腐蚀的典型案例、顶部腐蚀的影响因素、腐蚀控制方法及研究动态进行综合回顾,介绍了国内外顶部腐蚀的研究现状,分析了国内顶部腐蚀研究较少的原因,对今后的研究工作方向提出了建议。
关键词 湿气管线顶部腐蚀影响因素腐蚀控制流态    
Abstract:Several well-known cases of top of the line corrosion(TLC) in wet natural gas pipelines was reviewed in this paper. The review covered influence factors, corrosion protection techniques and research developments about top of the line corrosion. Little research work has been done about top of the line corrosion in wet natural gas pipelines in China and the reason was discussed in detail. Some suggestion about top of the line corrosion mechanism and corrosion protection techniques was made in the paper.
Key wordswet natural gas    pipeline    top of the line corrosion    influence factor    corrosion protection technique    flow regime
收稿日期: 2010-03-09     
ZTFLH: 

TE983

 
通讯作者: 蒋秀     E-mail: xjiangjerry@gmail.com
Corresponding author: JIANG Xiu     E-mail: xjiangjerry@gmail.com
作者简介: 蒋秀,女,1976年生,博士,高级工程师,研究方向为油气系统设备腐蚀与防护

引用本文:

蒋秀,屈定荣,刘小辉. 湿气管线的顶部腐蚀研究概况[J]. 中国腐蚀与防护学报, 2011, 31(2): 86-90.
JIANG Xiu. RESEARCH DEVELOPMENT OF TOP OF LINE CORROSION(TLC) IN WET NATURAL GAS PIPELINES. J Chin Soc Corr Pro, 2011, 31(2): 86-90.

链接本文:

https://www.jcscp.org/CN/      或      https://www.jcscp.org/CN/Y2011/V31/I2/86

[1] Paillassa R, Dieumegard M, Estavoyer M M. Corrosion control in the gathering system at LACQ sour gas field [A]. NACE/1981 [C].NACE, Houston, TX, 1981: 860

[2] Estavoyer M M. Corrosion problem at LACQ sour gas field [A].NACE/1981 [C]. NACE, Houston, TX, 1981: 905

[3] Ho-Chung-Qui D F, Williamson A I. Corrosion experiences and inhibition practices in wet sour gathering systems [A]. NACE/1987 [C]. NACE, Houston, TX, 1987: 87046

[4] Bich N N, Szklarz K E. Crossfield corrosion experience [A]. NACE/1988 [C]. NACE, Houston, TX, 1988: 88196

[5] Gunaltun Y M, Supriyatman D, Achmad J. Top of line corrosion in multiphase gas lines, a case history [A]. NACE/1999 [C]. NACE,Houston, TX, 1999: 99036

[6] Edwards M A, Cramer B. Top of line corrosion-diagnosis, rooot cause analysis, and treatment [A]. NACE/2000 [C]., NACE, Houston,TX, 2000: 00072

[7] Gunaltun Y M, Larrey D. Correlation of cases of top of line corrosion with calculated water condensation rate [A]. NACE/2000 [C]. NACE, Houston, TX, 2000: 00071

[8] Chai C W, Lu M X, Zhang G A. Top of line corrosion and protection in wet gas environments [J]. Corros. Prot., 2007, 28(4): 167-170

    (柴成文, 路民旭, 张国安. 湿气管线的顶部腐蚀与防护对策 [J]. 腐蚀与防护, 2007, 28(4): 167-170)

[9] Olsen S, Dugstad A. Corrosion under dewing conditions [A].NACE/1991 [C]. NACE, Houston, TX, 1991: 91472

[10] Singer M, Nesic S. Top of the line corrosion in presence of acetic acid and carbon dioxide [A]. NACE/2004 [C]. NACE,Houston, TX, 2004: 04377

[11] Crolet J L, Bonis M. The role of acetate ions in CO2 corrosion [A]. NACE/1983 [C]. NACE, Houston, TX, 1983: 160

[12] Garsany Y, Pletcher D, Sidorin D, et al. Qualifying the acetate enhanced corrosion of carbon steel in oilfield brines [J]. Corrosion, 2004, 60(12): 1155-1167

[13] Gunaltun Y M, Belghazi A. Control of top of line corrosion by chemical treatment [A]. NACE/2001 [C]. NACE, Houston, TX, 2001: 01033

[14] Schmitt G, Scheepers M, Siegmund G. Inhibition of the top-of-the-line corrosion under strtified flow [A]. NACE/2001 [C]. NACE, Houston, TX, 2001: 01032

[15] Gunaltun Y M, Payne L. A new technique for the control of top of the line corrosion: TLCC-PIG [A]. NACE/2003 [C]. NACE,Houston, TX, 2003: 03344

[16] Mi L T, Chen R P, Li X, et al. Inhibitor continuous adding device [P]. Chinese Patent of Inventation, 200610021383,2007

     (米力田, 陈汝培, 李珣等. 缓蚀剂连续加注装置 [P], 中国发明专利, 200610021383, 2007)

[17] Singer M, Hinkson D, Zhang Z, et al. CO2 Top of line corrosion in presence of acetic acid, a parametric study [A]. NACE/2009 [C]. NACE, Houston, TX, 2009: 09292

[18] Hinkson D, Singer M, Zhang Z, et al. A study of the chemical composition and corrosivity of the condensate for top of line corrosion [A]. NACE/2008 [C]. NACE, Houston, TX, 2008: 08466

[19] Camacho A, Singer M, Brown B et al. Top of line corrosion in H2S/CO2 environment [A]. NACE/2008 [C]. NACE, Houston,TX, 2008: 08470

[20] Zhang Z, Hinkson D, Singer M, et al. Mechanistic model of top of the line corrosion [A]. NACE/2007 [C]. NACE, Houston,TX, 2007: 07556

[21] Mendez C, Singer M, Camacho A, et al. Effect of acetic acid, pH and MEG on the CO2 top of the line corrosion [A]. NACE/2005 [C]. NACE, Houston, TX, 2005: 05278

[22] Nyborg R, Dugstad A. Top of line corrosion and water condensate rates in wet gas pipelines [A]. NACE/2007 [C]. NACE,Houston, TX, 2007: 07555

[23] Nyborg R, Dugstad A. Top of line corrosion with high CO2 and traces of H2S [A]. NACE/2009 [C]. NACE, Houston,TX, 2009: 09283

[24] Jiang X. Corrosion behaviors and inhibition mechanisms for CO2 corrosion of N80 steel under flowing conditions [D]. Shenyang: Institute of Metal Research, Chinese Academy of Sciences, 2005

     (蒋秀, 流动条件下N80钢的CO2腐蚀行为及缓释机理研究 [D]. 沈阳:中国科学院金属研究所博士论文, 2005)

[25] Liu H X, Zhang G L, Zhao J M, et al. Corrosion behavior of four steels in brine solution saturated by CO$_{2 }$ [J]. Corros.Prot., 2007, 28(4): 202-204

     (刘鹤霞, 张高林, 赵景茂等. 四种钢材在含CO2盐水溶液中的腐蚀行为 [J]. 腐蚀与防护, 2007, 28(4): 202-204)

[26] Liu Z D, Gu T, Tang Y F, et al. Researches on the electrochemical corrosion of the gathering lines in sour gas fields [J]. Chem. Eng.Oil Gas, 2007, 36(1): 55-58

     (刘志德, 谷坛, 唐永帆等. 高酸性气田地面集输管线电化学腐蚀研究 [J]. 石油与天然气化工, 2007, 36(1): 55-58)

[27] Huang H B. Corrosion and glycol distribution in large wet gas pipelines [J]. Foreign Oil Gas Storage Transp., 1995, 13(3): 31-34, 39

     (黄红兵. 大型湿气管道中的腐蚀和乙二醇分配 [J]. 国外油气储运, 1995,13(3): 31-34, 39)

[28] Zheng J, Huang H B, Yao X C. Pipeline corrosion under wet gas conditions [J]. Foreign Oilfield Eng., 2002, 18(8): 46-47, 54

     (郑君, 黄红兵, 姚煦春. 湿气条件下的管道腐蚀 [J]. 国外油田工程, 2002,18(8): 46-47, 54)

[29] Lu M X, Liu W. High temperature and Pressure Simulating Device for Condensed Water Corrosion Tests [P]. Chinese Patent of Inventation, 200510011461X, 2006

     (路民旭, 柳伟. 高温高压冷凝水腐蚀模拟实验装置 [P]. 中国发明专利, 200510011461X, 2006)

[30] Zhang L, Ding G, Liu Z D, et al. Effect of temperature on CO2 corrosion for X65 pipeline steel in wet natural gas [J]. Chem. Eng. Oil Gas, 2008, 37(1): 48-51

     (张雷, 丁工, 刘志德等. 温度对X65管线钢湿气CO2腐蚀的影响 [J]. 石油与天然气化工, 2008, 37(1): 48-51)
[1] 戴婷, 顾艳红, 高辉, 刘凯龙, 谢小辉, 焦向东. 水下摩擦螺柱焊接头在饱和CO2中的电化学性能[J]. 中国腐蚀与防护学报, 2021, 41(1): 87-95.
[2] 白云龙, 沈国良, 覃清钰, 韦博鑫, 于长坤, 许进, 孙成. 硫脲基咪唑啉季铵盐缓蚀剂对X80管线钢腐蚀的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[3] 左勇, 曹明鹏, 申淼, 杨新梅. MgCl2-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[4] 戴明杰, 刘静, 黄峰, 胡骞, 李爽. 基于正交方法研究阴极保护电位波动下X100管线钢的点蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(5): 425-431.
[5] 朱丽霞, 贾海东, 罗金恒, 李丽锋, 金剑, 武刚, 胥聪敏. 外加电位对X80管线钢在轮南土壤模拟溶液中应力腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 325-331.
[6] 王新华, 杨永, 陈迎春, 位凯玲. 交流电流对X100管线钢在库尔勒土壤模拟液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(3): 259-265.
[7] 陈旭, 李帅兵, 郑忠硕, 肖继博, 明男希, 何川. X70管线钢在大庆土壤环境中微生物腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 175-181.
[8] 袁玮,黄峰,甘丽君,戈方宇,刘静. 显微组织对X100管线钢氢致开裂及氢捕获行为影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 536-542.
[9] 史显波,杨春光,严伟,徐大可,闫茂成,单以银,杨柯. 管线钢的微生物腐蚀[J]. 中国腐蚀与防护学报, 2019, 39(1): 9-17.
[10] 邓培昌, 刘泉兵, 李子运, 王贵, 胡杰珍, 王勰. X70管线钢在热带海水-海泥跃变区的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 415-423.
[11] 廖梓含, 宋博, 任泽, 何川, 陈旭. X70钢及其焊缝在Na2CO3+NaHCO3溶液中电化学腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(2): 158-166.
[12] 偶国富, 赵露露, 王凯, 王宽心, 金浩哲. 10#碳钢在HCl-H2O环境中的露点腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(1): 33-38.
[13] 任继栋,高荣杰,张宇,刘勇,丁甜. 混酸刻蚀-氟化处理制备X80管线钢双疏表面及其耐蚀性研究[J]. 中国腐蚀与防护学报, 2017, 37(3): 233-240.
[14] 张康南,吴明,谢飞,王丹,伞宇曦,江峰. 磁场对X80管线钢在沈阳草甸土中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2017, 37(2): 148-154.
[15] 魏木孟,杨博均,刘洋洋,王孝平,姚敬华,高灵清. Cu-Ni合金管海水冲刷腐蚀研究现状及展望[J]. 中国腐蚀与防护学报, 2016, 36(6): 513-521.