米糠提取液作为盐酸酸洗缓蚀剂的研究

中国腐蚀与防护学报

2009, Vol. 29

Issue (2): 149-153

研究报告

本期目录 | 过刊浏览

米糠提取液作为盐酸酸洗缓蚀剂的研究

胡胜;康笑阳;付朝阳

华中科技大学化学与化工学院材料化学与服役失效湖北省重点实验室武汉 430074

RICE BRAN EXTRACTION USED AS PICKLING INHIBITOR IN HYDROGEN CHLORIDE ACID

HU Sheng; KANG Xiaoyang; FU Chaoyang

Hubei Key Laboratory of Materials Chemistry and Service Failure; Department of Chemistry;Huazhong University of Science and Technology; Wuhan 430074

全文: PDF(644 KB)

摘要:

用盐酸酸化浸取法从米糠中提取植酸，并将其作为盐酸酸洗缓蚀剂的主要成分；采用失重挂片、线性极化和电化学阻抗等方法评价该缓蚀剂的缓蚀效率，并初步探讨其缓蚀机理。结果表明：该缓蚀剂对碳钢在1 mol/L HCl 溶液中有良好的缓蚀效果，且缓蚀效率受温度影响较小，属于阴极型缓蚀剂。

关键词 ：米糠, 植酸, 盐酸, 酸洗, 缓蚀剂, 缓蚀机理

Abstract：

Phytic acid was abstracted from the rice bran by hydrochloric acid leaching method and used as main component of corrosion inhibitor for hydrochloric acid pickling. Its inhibiting behavior on carbon steel in hydrochloric acid was investigated by means of mass loss, polarization curves and electrochemical impedance spectroscopy (EIS) methods. The results show that the corrosion inhibitor exhibits good inhibition effect for carbon steel in 1mol/L hydrochloric acid and inhibition efficiency is less affected by temperature. The results of polarization curves indicate that the corrosion inhibitor mainly prohibits the cathodic process.

Key words： rice bran phytic acid hydrochloric acid pickling corrosion inhibitor inhibition mechanism

收稿日期: 2007-05-29

ZTFLH:

TG174.42

基金资助:

华中科技大学研究生创新基金（HF04112006013）

通讯作者: 付朝阳 E-mail: cyfu@mail.hust.edu.cn

Corresponding author: FU Chaoyang E-mail: cyfu@mail.hust.edu.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	付朝阳
	胡胜
	康笑阳
44.8K

引用本文:

胡胜康笑阳付朝阳. 米糠提取液作为盐酸酸洗缓蚀剂的研究[J]. 中国腐蚀与防护学报, 2009, 29(2): 149-153.
FU Zhao-Yang, HU Qing, KANG Xiao-Yang. RICE BRAN EXTRACTION USED AS PICKLING INHIBITOR IN HYDROGEN CHLORIDE ACID. J Chin Soc Corr Pro, 2009, 29(2): 149-153.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2009/V29/I2/149

[1] Zhang C F, Feng B. The study and application of corrosion inhibitors to acid pickling at home[J]. Hunan Electr. Power, 2000, 20(2): 1-2
   (张玉福,冯斌.国内酸洗缓蚀剂研制及应用[J].湖南电力 ,2000, 20(2): 1-2)
[2] Tang B, Chen X Y. Study of corrosion inhibitors acid pickling[J]. Clean. World, 2006, 22(2): 22-28
     (汤兵,陈欣义.酸洗过程中的缓蚀剂[J].清洗世界,2006,22(2): 22-28)
[3] Zhang T S. Corrosion Inhibitors [M]. Beijing: Chemical Industry Press, 2001
     (张天胜. 缓蚀剂[M]. 北京:化学工业出版社, 2001)
[4] Zhou X X. Present state of the application of corrosion inhibitors to acid pickling and its development trend[J]. Ind. Water Treat., 2002, 22(1): 16-19
    (周晓湘. 酸洗缓蚀剂的应用研究现状及发展趋势[J ]. 工业水处理,2002, 22(1): 16-19)
[5] Ao J P, Sun G Z. The study development of corrosion inhibitors to acid pickling[J]. Mater.Prot., 2000, 33(9): 1-3
    (敖建平, 孙国忠.盐酸清洗缓蚀剂的研究进展[J]. 材料保护, 2000, 33(9): 1-3)
[6] Meligh E L, T S. A A Effect of corrosion inhibitors on scale removal during pickling of mild steel [J]. Br. Corros. J.,2000, 35: 75-76
[7] Zhang W Y, Chen Y F, Li X. Inhibitive effect of some natural-occurring substance on dissolution of A3 steel in HCl solution[J]. North Chin. Electr. Power, 2002, 1:9-11
     (张万友, 陈月芳, 李洵.复配型绿色植物缓蚀剂对盐酸溶液中A3钢的缓蚀作用[J]. 华北电力技术,2002, 1: 9-11)
[8] Wang H, Zhu Z L. Review on the research of environmentally benign green agents.[J] Clean. World, 2004,20(3): 28-30
     (王慧, 朱志良.环境友好绿色清洗剂的研究进展[J]. 清洗世界, 2004, 20(3): 28-30)
[9] Chen X N. The environmentally cleaning agents[J]. New Chem. Mater., 1998, 26(12): 37-38
     (陈湘宁.环保型清洗剂[J]. 化工新型材料, 1998, 26(12): 37-38)
[10] Li Y T, Hou B R. Progress on natural environmental friendly corrosion inhibitors for metals[J]. Corros.Sci. Prot. Technol.,2006, 18(1): 37- 40
    (李言涛, 侯保荣.天然环保型缓蚀剂近期研究进展[J]. 腐蚀科学与防护技术, 2006, 18(1):37-40)
[11] Bo D. The influence of pH to complex ability of phytic acid[J]. J. Shandong Norm. Univ. (Nat. Sci.), 2004, 19(6): 104-109
       (柏冬. pH值对植酸络合能力的影响[J].山东师范大学学报(自然科学版), 2004, 19(6): 104-109)
[12] Feng P, Feng X B, Xu Y P. Complex of phytic acid with metal ions[J]. Chin. Oils Fans, 2006, 31(8): 63-66
        (冯屏, 冯小兵,徐玉佩. 植酸与金属离子络合的研究[J]. 中国油脂, 2006, 31(8):63-66)
[13] Cao C N. Corrosion Electrochemistry [M].Beijing: Chemical Industry Press, 2004
       (曹楚南.腐蚀电化学原理[M]. 北京: 化学工业出版社, 2004)

[1]	白云龙, 沈国良, 覃清钰, 韦博鑫, 于长坤, 许进, 孙成. 硫脲基咪唑啉季铵盐缓蚀剂对X80管线钢腐蚀的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[2]	王亚婷, 王棵旭, 高鹏翔, 刘冉, 赵地顺, 翟建华, 屈冠伟. 淀粉接枝共聚物对Zn的缓蚀性能[J]. 中国腐蚀与防护学报, 2021, 41(1): 131-138.
[3]	邵明鲁, 刘德新, 朱彤宇, 廖碧朝. 乌洛托品季铵盐缓蚀剂的合成与复配研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 244-250.
[4]	贾巧燕, 王贝, 王赟, 张雷, 王清, 姚海元, 李清平, 路民旭. X65管线钢在油水两相界面处的CO₂腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 230-236.
[5]	张晨, 陆原, 赵景茂. CO₂/H₂S腐蚀体系中咪唑啉季铵盐与3种阳离子表面活性剂间的缓蚀协同效应[J]. 中国腐蚀与防护学报, 2020, 40(3): 237-243.
[6]	吕祥鸿,张晔,闫亚丽,侯娟,李健,王晨. 两种新型曼尼希碱缓蚀剂的性能及吸附行为研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 31-37.
[7]	王霞,任帅飞,张代雄,蒋欢,古月. 豆粕提取物在盐酸中对Q235钢的缓蚀性能[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.
[8]	刘建国,高歌,徐亚洲,李自力,季菀然. 咪唑啉类衍生物缓蚀性能研究[J]. 中国腐蚀与防护学报, 2018, 38(6): 523-532.
[9]	李亚琼,马景灵,王广欣,朱宇杰,宋永发,张景丽. NaPO₃与SDBS缓蚀剂对AZ31镁合金空气电池在NaCl电解液中放电性能的影响[J]. 中国腐蚀与防护学报, 2018, 38(6): 587-593.
[10]	孔佩佩, 陈娜丽, 白德忠, 王跃毅, 卢勇, 冯辉霞. 壳聚糖及其衍生物的制备与缓蚀性能的研究进展[J]. 中国腐蚀与防护学报, 2018, 38(5): 409-414.
[11]	马景灵, 通帅, 任凤章, 王广欣, 李亚琼, 文九巴. L-半胱氨酸/ZnO缓蚀剂对3102铝合金在碱性溶液中电化学性能的影响[J]. 中国腐蚀与防护学报, 2018, 38(4): 351-357.
[12]	常亮, 师超, 邵亚薇, 王艳秋, 刘斌, 孟国哲. 植酸转化膜对环氧清漆防腐性能的影响[J]. 中国腐蚀与防护学报, 2018, 38(3): 265-273.
[13]	彭晚军, 丁纪恒, 陈浩, 余海斌. 生物基缓蚀剂糠醇缩水甘油醚的缓蚀性能及机理[J]. 中国腐蚀与防护学报, 2018, 38(3): 303-308.
[14]	钱备, 刘成宝, 宋祖伟, 任俊锋. 纳米容器改性环氧涂层对Q235碳钢的防腐蚀性能[J]. 中国腐蚀与防护学报, 2018, 38(2): 133-139.
[15]	郭娜, 类延华, 刘涛, 常雪婷, 尹衍升. 植酸水溶液中聚吡咯涂层在Cu基体上的制备及其在腐蚀防护中的应用[J]. 中国腐蚀与防护学报, 2018, 38(2): 140-146.

Viewed

Full text

Abstract

Cited

Shared

Discussed