AZ31B镁合金表面硅烷处理研究

中国腐蚀与防护学报

2008, Vol. 28

Issue (3): 146-150

研究报告

本期目录 | 过刊浏览

AZ31B镁合金表面硅烷处理研究

吴超云

重庆工学院材料科学与工程学院

Study of surface treatment on the AZ31B magnesium alloys by silane agent

Chao Yun Wu

重庆工学院材料科学与工程学院

全文: PDF(1396 KB)

摘要: 采用硅烷溶液浸湿处理在AZ31B镁合金表面生成一层保护膜，采用扫描电镜、金相显微镜及体式显微镜观察试样表面形貌，并通过傅立叶红外光谱（FTIR）对硅烷膜与基体的键合进行测试分析；采用盐水浸泡、动电位极化曲线研究硅烷膜层的耐腐蚀性能，并与磷化膜层进行对比。结果表明：AZ31B镁合金经硅烷化处理，可以在其表面生成一层极薄的透明硅烷膜层，该膜层平整致密，对镁合金的自腐蚀电位影响不大，但大幅度降低了镁合金的自腐蚀电流密度，很好地抑制了镁合金的腐蚀。

关键词 ：硅烷处理, AZ31B镁合金, 耐腐蚀, 极化

Abstract：The protective film was prepared by immersion magnesium alloy AZ31B in silane solution. The surface morphologies of specimen were analyzed by using SEM、Optical Microscope. The bond adherence between silane film and substrate was researched by FTIR. The corrosion resistance of film was analyzed by salt water immersion and potentiodynamic polarization test. The results show that a very thin and transparent film that was smooth and compact was prepared on the AZ31B magnesium alloys by immersion in silane solution. The silane film has effected polarization voltage of AZ31B magnesium alloys slightly, however the polarization current decreased to 1.024 mA/cm2 for the specimen compared with the bare magnesium alloys (4.489mA/cm2). So the corrosion resistance of magnesium alloys was greatly improved by silane treatment.

Key words： silane treatment AZ31B magnesium alloys corrosion resistance polarization

收稿日期: 2007-01-17

通讯作者: 吴超云 E-mail: wchy1201@hotmail.com

Corresponding author: Chao Yun Wu E-mail: wchy1201@hotmail.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	吴超云
44.8K

引用本文:

吴超云 . AZ31B镁合金表面硅烷处理研究[J]. 中国腐蚀与防护学报, 2008, 28(3): 146-150 .
Chao Yun Wu. Study of surface treatment on the AZ31B magnesium alloys by silane agent. J Chin Soc Corr Pro, 2008, 28(3): 146-150 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2008/V28/I3/146

[1]Wu M,Lv B L,Liang P.The status of magnesium and magnesium alloys surface treatment[J].Surf.Technol.,2005,34(5):13-15(吴敏,吕柏林,梁平.镁及其合金表面处理现状[J].表面技术,2005,34(5):13-15)
[2]Zhang J,Zhang Z H.Magnesium Alloys and Their Application[M].Beijing:Chemical Industry Press,2004(张津,章宗和.镁合金及应用[M].北京:化学工业出版社,2004)
[3]Wim J van Ooij,Fairfield,Ashok Sabata,et al.Metal sheet with enhanced corrosion resistance having a silane treated silicate coat-ing[P].United States Patent,5108793,1992
[4]Wim J van Ooij,Fairfield,Ashok Sabata,et al.Metal sheet with en-hanced corrosion resistance having a silane treated aluminate coat-ing[P].United States Patent,5322713,1994
[5]Wim J van Ooij,Ricole A.Edwards,Ashok Sabata,et al.Metalliccoated sheet having a silane film providing temporary corrosionprotection and method therefore[P].United States Patent,5292549,1994
[6]Palanivel V,Wim J van Ooij,Zhu D.Nanoparticle-filled silanefilms as chromate replacements for aluminum alloys[J].Prog.Org.Coat,2003,47:384-387
[7]Liu L,Hu J M,Zhang J Q,et al.Progress in anti-corrosive treat-ment of metals by silanization[J].J.Chin.Soc.Corros.Prot.,2006,26(1):59-64(刘,胡吉明,张鉴清等.金属表面硅烷化防护处理及其研究现状[J].中国腐蚀与防护学报,2006,26(1):59-64)
[8]Wu H J,Lu J T.Properties of corrosion resistance on hot-galvaniza-tion steel surface[J].Corros.Prot.,2006,27(1):15-18(吴海江,卢锦堂.热镀锌钢表面硅烷膜耐蚀性性能的初步研究[J].腐蚀与防护,2006,27(1):15-18)
[9]Zucchi F,Grassi V.Influence of a silane treatment on the corrosion resistance of a WE43 magnesium alloy[J].Surf.Coat.Technol.,2006,200:4136-4143
[10]Hu J M,Liu J,Zhang J T,et al.Studies of surface treatment of aluminum alloys by BTSE silane agent[J].Acta Metall.Sin.,2004,40(11):1189-1194(胡吉明,刘,张金涛等.铝合金表面BTSE硅烷化处理研究[J].金属学报,2004,40(11):1189-1194)

[1]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[2]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[3]	魏征, 马保吉, 李龙, 刘潇枫, 李慧. 镁合金表面超声滚压预处理对微弧氧化膜耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[4]	张浩, 杜楠, 周文杰, 王帅星, 赵晴. 模拟海水溶液中Fe³⁺对不锈钢点蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[5]	李子运, 王贵, 罗思维, 邓培昌, 胡杰珍, 邓俊豪, 徐敬明. 热带海洋大气环境中EH36船板钢早期腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 463-468.
[6]	周宇, 张海兵, 杜敏, 马力. 模拟深海环境中阴极极化对1000 MPa级高强钢氢脆敏感性的影响[J]. 中国腐蚀与防护学报, 2020, 40(5): 409-415.
[7]	孙硕, 杨杰, 钱薪竹, 常人丽. Ni-Cr-P化学镀层的制备与电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(3): 273-280.
[8]	杨寅初,傅秀清,刘琳,马文科,沈莫奇. 喷射电沉积Ni-P-BN(h)-Al₂O₃复合镀层的耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 57-62.
[9]	张天翼,柳伟,范玥铭,李世民,董宝军,BANTHUKUL Wongpat,CHOWWANONTHAPUNYA Thee. 海洋大气环境Cu/Ni协同作用对低合金钢耐蚀性影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 511-518.
[10]	赵书彦,童鑫红,刘福春,翁金钰,韩恩厚,郦晓慧,杨林. 环氧富锌涂层防腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 563-570.
[11]	肖金涛,陈妍,邢明秀,鞠鹏飞,孟引根,王芳. 工艺参数对2195铝锂合金阳极氧化膜的耐蚀性影响[J]. 中国腐蚀与防护学报, 2019, 39(5): 431-438.
[12]	欧阳跃军,胡婷,王佳音,谢治辉. 镁合金表面层状双氢氧化物的电化学沉积和表征[J]. 中国腐蚀与防护学报, 2019, 39(5): 453-457.
[13]	史昆玉,张进中,张毅,万毅. Nb₂N涂层制备及其耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 313-318.
[14]	王标,杜楠,张浩,王帅星,赵晴. 304不锈钢点蚀产物对亚稳态点蚀萌生和稳态蚀孔生长的加速作用[J]. 中国腐蚀与防护学报, 2019, 39(4): 338-344.
[15]	王霞,任帅飞,张代雄,蒋欢,古月. 豆粕提取物在盐酸中对Q235钢的缓蚀性能[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.

Viewed

Full text

Abstract

Cited

Shared

Discussed