电化学阻抗谱研究达克罗在海水中的腐蚀行为
胡会利;李宁;程瑾宁
哈尔滨工业大学(威海)
The Electrochemical Impedance Spectroscopy of Dacromet coating in seawater
;;
哈尔滨工业大学(威海)
全文: PDF(296 KB)  
摘要: 测量了达克罗涂层在海水中全浸不同时间的电化学阻抗谱(EIS),并用等效电路Ro(RpC)(RDQ)进行解析。结果表明:腐蚀过程中试样的极化电阻Rp、双电层电容C、扩散电阻RD均不断增大,且RD/Rp也一直增大。达克罗涂层的腐蚀初期为金属Zn的溶解,随着腐蚀的进行,腐蚀产物在膜内的累积导致钝化膜的有效厚度增加,Zn粉的牺牲阳极作用受到了限制;腐蚀后期主要是机械的壁垒保护作用,直到扩散和溶解作用超过壁垒作用后,涂层以点蚀的形式发生破坏。
关键词 电化学阻抗谱达克罗腐蚀行为海水腐蚀    
Abstract:The evolution of electrochemical impedance spectroscopy(EIS)and open circuit potential were obtained from dacromet-coating mild steel, which were fully soaked in seawater. The EIS was analyzed by the equivalent circuitRO (RpC) (RDQ). The resistance showed the increasing with immersing time of the polarization resistance Rp, douible layer capacity C,diffusion resistance RD and the value of RD/RP. The conclusion was drawn that Zn dissolved at the beginning of corrosion process of dacromet and its sacrificial anode effects were limited by the accumulation of corrosion products,which thickened the thickness of passivation coating. The physical barrier action was the prominent anticorrosive mean afterqards.Dacromet coating failed to protect the base for pitting afier the cooperation of diffusion and dissolution overtook the barier effects.
Key wordselectrochemical impedance spectroscopy    dacromet    corrosion behavior    seawater corrosion    equivalent cir
收稿日期: 2006-01-09     
ZTFLH:  TQ22.122  
通讯作者: 胡会利      E-mail: whhhl@126.com

引用本文:

胡会利; 李宁; 程瑾宁 . 电化学阻抗谱研究达克罗在海水中的腐蚀行为[J]. 中国腐蚀与防护学报, 2007, 27(4): 197-201 .

链接本文:

https://www.jcscp.org/CN/Y2007/V27/I4/197

[1]Mulkin F.A new coating for corrosion and protection of metals with zinc powder passivated by chromate[P].US:3673731,1972
[2]Sun H M.Zn-Cr coating-a special newtechnique for surface treatment[J].Mater.Prot.,1994,27(18):21-23(孙贺民.锌铬膜—一种特殊的表面处理新技术[J].材料保护,1994,27(18):21-23)
[3]Su H J.The study on the formation of water-soluble coating[J].Surf.Technol.,2000,29(1):12-14(苏红军.水系锌铬膜涂层技术研究[J].表面技术,2000,29(1):12-14)
[4]Han S M,Zheng Y Z,Yu S X,et al.Study on microstructure and mechanism of zinc-aluminum-chromium conversion coating[J].J.Chin.Soc.Corros.Prot.,2002,22(5):269-273(韩树民,郑炀曾,于学升等.锌铝铬转化膜微观结构与成膜机理研究[J].中国腐蚀与防护学报,2002,22(5):269-273)
[5]Hu H L,Li N,Han J J,et al.Current status of dacromet technology[J].Electroplating and Finishing,2005,24(3):31-33(胡会利,李宁,韩家军等.达克罗的研究现状[J].电镀与涂饰,2005,24(3):31-33)
[6]GB/T18684-2002,Specification for zinc-chromium coating[S].(GB/T18684-2002,锌铬涂层技术条件[S].)
[7]Xu L C,Chen Z X,Ma Z W,et al.A study on preparation and corrosion resistance of Zn-Cr film coating[J].Corros.Prot.,1998,19(3):108-110(徐立冲,陈中兴,马志伟等.锌铬膜的制备及其耐蚀性研究[J].腐蚀与防护,1998,19(3):108-110)
[8]He J B,Lu D R,Li X L,et al.Investigation on corrosion kinetics behavior of dacromet coating[J].Chem.Res.Appl.,2002,14(1):81-83(何建波,鲁道荣,李学良等.达克罗涂层的腐蚀动力学行为研究[J].化学研究与应用,2002,14(1):81-83)
[9]Wang M,Huang X,Wang J L,et al.Dacromet and its application[J].Electroplating and Finishing,2001,20(2):65-67(王敏,黄鑫,王家禄等.达克罗技术及应用[J].电镀与涂饰,2001,20(2):65-67)
[10]Chen L,Li N,Zhou D R.Effect of chromic trioxide content in solutions on properties of sintered zinc-rich coatings[J].Chin.J.Nonferr.Metal,2001,10(Suppl.1):209-213(陈玲,李宁,周德瑞.涂料中含铬量对烧结式富锌涂层性能的影响[J].中国有色金属学报,2000,10(增刊1):209-213)
[11]Zha Q X.Kinetics in Electrode Processes[M].Beijing:Science Press,1976(查全性.电极过程动力学[M].北京:科学出版社,1976)
[12]Cao C N,Zhang J Q.Introduction of Electrochemical Impedance Spectroscope[M].Beijing:Science Press,2002(曹楚南,张鉴清.电化学阻抗谱导论[M].北京:科学出版社,2002)
[13]Han S M,Zheng Y Z,Yu S X,et al.Corrosion prevention characteristics and mechanism of zinc-aluminum-chromium coating[J].Chin.J.Nonferr.Metals,2002,12(3):619-623(韩树民,郑炀曾,于升学等.锌铝铬膜的防腐性能与机理[J].中国有色金属学报,2002,12(3):619-623
[14]Chen L,Li N,Zhou D R,et al.The study of dacromet`s microstructure and its electrochemical characteristics[J].HighTechnology Letters,2000,(10):74-76(陈玲,李宁,周德瑞等.达克罗涂层的组织结构及电化学特性研究[J].高技术通讯,2000,(10):74-76
[15]Cao C N.Principle of Corrosion Electrochemistry[M].Beijing:Chemical Industry Press,2004(曹楚南.腐蚀电化学原理[M].北京:化学工业出版社,2004)
[16]Chung S C,Cheng J R,Chiou S D,et al.EIS behavior of anodized zinc in chloride environments[J].Corros.Sci.,2000,42(7):1249-1268
[1] 李琳, 陈义庆, 高鹏, 艾芳芳, 钟彬, 伞宏宇, 杨颖. 除冰盐环境下桥梁钢的耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 448-454.
[2] 翟思昕, 杨幸运, 杨继兰, 顾剑锋. 淬火-配分-回火钢在模拟海水环境中的腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 398-408.
[3] 王玉, 吴佳佳, 张盾. 海水环境中异化铁还原菌所致金属材料腐蚀的研究进展[J]. 中国腐蚀与防护学报, 2020, 40(5): 389-397.
[4] 张欣, 杨光恒, 王泽华, 曹静, 邵佳, 周泽华. 冷拉拔变形过程中含稀土铝镁合金腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 432-438.
[5] 胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[6] 王新华, 杨永, 陈迎春, 位凯玲. 交流电流对X100管线钢在库尔勒土壤模拟液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(3): 259-265.
[7] 胡玉婷, 董鹏飞, 蒋立, 肖葵, 董超芳, 吴俊升, 李晓刚. 海洋大气环境下TC4钛合金与316L不锈钢铆接件腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 167-174.
[8] 张尧, 郭晨, 刘妍慧, 郝美娟, 成世明, 程伟丽. 挤压态Mg-2Sn-1Al-1Zn合金在模拟体液中的电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(2): 146-150.
[9] 苏小红,胡会娥,孔小东. W颗粒/Zr41.2Ti13.8Cu12.5Ni10Be22.5基非晶复合材料在3%NaCl溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 70-74.
[10] 王勤英,裴芮,西宇辰. 镍基激光熔覆层冲刷腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 458-462.
[11] 史昆玉,张进中,张毅,万毅. Nb2N涂层制备及其耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 313-318.
[12] 郭铁明,张延文,秦俊山,宋志涛,董建军,杨新龙,南雪丽. 桥梁钢Q345q在3种模拟大气环境中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 319-330.
[13] 王霞,任帅飞,张代雄,蒋欢,古月. 豆粕提取物在盐酸中对Q235钢的缓蚀性能[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.
[14] 达波,余红发,麻海燕,吴彰钰. 等效电路拟合珊瑚混凝土中钢筋锈蚀行为的电化学阻抗谱研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 260-266.
[15] 达波,余红发,麻海燕,吴彰钰. 阻锈剂的掺入方式对全珊瑚海水混凝土中钢筋锈蚀的影响[J]. 中国腐蚀与防护学报, 2019, 39(2): 152-159.