多层复合渗镀TiN耐蚀性的研究

刘燕萍;徐晋勇;隗小云;王建忠;高原;徐重

太原理工大学表面工程研究所

CORROSION PROPERTY OF TiN MULTI-PERMEATED LAYERS

yanping Liu;;;;;

太原理工大学表面工程研究所

全文: PDF(319 KB)

摘要: 采用双层辉光渗金属技术，在碳钢表面形成具有扩散层和沉积层的TiN复合渗镀层.对复合渗镀、PVD以及复合渗镀＋PVD三种工艺制备的TiN层表面形貌、成分及在10%H2SO4和35%NaCl〖JP2〗溶液中的耐蚀性能进行了对比试验研究.结果表明：复合渗镀＋PVD法沉积的TiN薄膜呈较为均匀、致密、细小的组织，Ti和N原子由表层呈梯度向内分布.与PVD法沉积的TiN层不同，是属于冶金扩散结合层，渗镀层厚度可达10 μm以上.在10%H2SO4和35%NaCl溶液中，渗镀层的腐蚀速度分别为0.156 g/(m2·h)和0.025 g/(m2·h)，显示出了优异的耐蚀性.

关键词 ：辉光等离子, PVD, TiN层, 结构, 耐蚀性

Abstract：TiN multi-permeated layers were formed on the steel surface with diffusion layer and deposition layer by means of both double glow-discharge surface alloying process and reactive sputtering.The surface appearances and composition and its corrosion-resistance in 10% H2SO4 and 3.5% NaCl of TiN multi-permeated layers by using different processes were investigated.The results indicated that the TiN multi-permeated layer was uniform and compact,th e content of atom Ti,N gradually decreased with increasing distance from the surface.The adhesion of the TiN coating was very strong,its thickness was more than 10 μm.The corrosion resistance of the TiN multi-permeated layer in 10% H2SO4 and 3.5% NaCl was excellent,the corrosion rate was only 0.156 g/(m2·h) and 0.025 g/(m2·),respectively.

Key words： glow-discharge plasma PVD TiN structure corrosion resistance

收稿日期: 2005-04-07

ZTFLH:

TG156.8

通讯作者: 刘燕萍

Corresponding author: yanping Liu

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	刘燕萍
	徐晋勇
	隗小云
	王建忠
	高原
	徐重
44.8K

引用本文:

刘燕萍; 徐晋勇; 隗小云; 王建忠; 高原; 徐重 . 多层复合渗镀TiN耐蚀性的研究[J]. 中国腐蚀与防护学报, 2006, 26(4): 227-231 .
yanping Liu. CORROSION PROPERTY OF TiN MULTI-PERMEATED LAYERS. J Chin Soc Corr Pro, 2006, 26(4): 227-231 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2006/V26/I4/227

[1]Beverskog B,Carlsson J O,Delblanc Bauer A,et al.Corrosion prop-erties of TiC film prepared by active reactive evaporation[J].Surf.Coat.Technol.,1990,41:221-227
[2]Rudenja S,Pan J,Odnevall Wallinder I,et al.Passivation and anodicoxidation of duplex TiN coating on stainless steel[J].Electrochem.Soc.,1999,146:4082-4089
[3]Marco J F,Agudelo A C,Gancendo J R,et al.Corrosion resistance ofsingle TiN layers,Ti/TiN bilayers and Ti/TiN/Ti/TiN multilayerson iron under a salt fog spray test:an evaluation by XPS[J].Surfaceand Interface Analysis,1999,27:71-78
[4]Chen B F,Pan W L,Yu G P,et al.On the corrosion behavior of TiN-coated AISI D2 steel[J].Surf.Coat.Technol.,1999,111:16-22
[5]Liu Q C,Liu P Y,Tao Y,et al.Investigation on TiN coating byCVD and pulsed D.C.PCVD methods[J].Mater.Eng.,2000,4:22-25(刘齐成,刘培英,陶冶等.CVD与PVD法TiN薄膜的研究[J].材料工程,2000,4:22-25)
[6]Liu Y F,Zhang G L,Wang J L,et al.Preparation of titanium nitridefilms by pulsed high energy density plasma and investigation of thetribological behavior of the film[J].Acta Physica Sinica,2004,53(2):503-507(刘元富,张谷令,王久丽等.脉冲高能量密度等离子体法制备TiN薄膜及其摩擦磨损性能研究[J].物理学报,2004,53(2):503-507)
[7]Ma D Y,Ma S L,Xu K W,et al.Tribological behavior of Ti-Si-N coatings prepared by magnetron sputtering reactivated deposition[J].Chin.J.Nonferr.Metal.,2004,14(8):1308-1312(马大衍,马胜利,徐可为等.反应磁控溅射制备Ti-Si-N薄膜的摩擦磨损性能[J].中国有色金属学报,2004,14(8):1308-1312)
[8]Xu Z.A novel plasma surface metallurgy:Xu-Tec process[J].Met-allurgical Coatings and Thin Films,1990,2:103-106
[9]Xu Z,Gu F Y.New development in ion surface alloying[J].Pro-ceedings,1986,3:20-24
[10]Zhang X,Yang Z M,Dong J X,et al.Surface metallurgy of nickelbase superalloy[J].Univ.Sci.Technol.,1999,1:47-53
[11]Hu S B,Cui K,Li Z Z.Sliding wear behavior of TiN/Ni-W com-posite coating[J].Tribology,2001,21(4):246-250(胡树兵,崔昆,李志章.TiN/Ni-W复合涂层的滑动磨损特性[J].摩擦学学报,2001,21(4):246-250)
[12]Xu Z.Development,present state and perspectives of the doubleglow surface alloying technique[J].Sur.Eng.,1997,34(1):4-10(徐重.双层辉光离子渗金属技术的发展、现状和展望[J].表面工程,1997,34(1):4-10)
[13]Li Y,Qu L,Wang F H,et al.Study on the electrochemical corro-sion behavior of TiN coating,I.Protection property and failuremechanism of TiN coating[J].J.Chin.Soc.Corros.Prot.,2003,23(2):65-69(李瑛,屈力,王福会等.TiN涂层电化学腐蚀行为研究Ⅰ.TiN涂层的保护性能与失效机制[J].中国腐蚀与防护学报,2003,23(2):65-69)

[1]	黄鹏, 高荣杰, 刘文斌, 尹续保. 盐溶液刻蚀-氟化处理制备X65管线钢镀镍超双疏表面及其耐蚀性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 96-100.
[2]	包任, 周根树, 李宏伟. 恒电位脉冲电沉积高锡青铜耐蚀镀层工艺研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 585-591.
[3]	于浩冉, 张文丽, 崔中雨. 4种镁合金在Cl^--NH₄⁺-NO₃^-溶液体系中的腐蚀行为差异研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 553-559.
[4]	刘海霞, 黄峰, 袁玮, 胡骞, 刘静. 690 MPa级高强贝氏体钢在模拟乡村大气中的腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(5): 416-424.
[5]	李聪玮, 杜双明, 曾志琳, 刘二勇, 王飞虎, 马付良. 电流密度对Ni-Co-B镀层微观结构及磨蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(5): 439-447.
[6]	闻洋, 熊林, 陈伟, 薛刚, 宋文学. 干湿循环下聚乙烯醇纤维混凝土抗Cl^-渗透性能研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 381-388.
[7]	曹京宜, 方志刚, 陈晋辉, 陈志雄, 殷文昌, 杨延格, 张伟. 5083铝合金表面单致密微弧氧化膜的制备及其性能研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[8]	王英君, 刘洪雷, 王国军, 董凯辉, 宋影伟, 倪丁瑞. 新型高强稀土Al-Zn-Mg-Cu-Sc铝合金的阳极氧化及其抗腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 131-138.
[9]	王乐,易丹青,刘会群,蒋龙,冯春. Ru对Ti-6Al-4V合金腐蚀行为的影响及机理研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 25-30.
[10]	武栋才,韩培德. 中温时效处理对SAF2304双相不锈钢耐蚀性的影响[J]. 中国腐蚀与防护学报, 2020, 40(1): 51-56.
[11]	姜冬雪,付颖,张峻巍,张伟,辛丽,朱圣龙,王福会. 钛合金表面Al₂O₃陶瓷膜制备及性能研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 469-476.
[12]	潘成成,马超,夏大海. EBSD技术研究金属材料晶体取向对大气腐蚀萌生的影响机理[J]. 中国腐蚀与防护学报, 2019, 39(6): 495-503.
[13]	魏欣欣,张波,马秀良. FeCr₁₅Ni₁₅单晶600 ℃下热生长氧化膜的TEM观察[J]. 中国腐蚀与防护学报, 2019, 39(5): 417-422.
[14]	于美,魏新帝,范世洋,刘建华,李松梅,钟锦岩. 应力作用下2297铝锂合金腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 439-445.
[15]	史昆玉,张进中,张毅,万毅. Nb₂N涂层制备及其耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 313-318.

Viewed

Full text

Abstract

Cited

Shared

Discussed