时效制度对Al-Zn-Mg-Cu铝合金应力腐蚀敏感性的影响

中国腐蚀与防护学报

2006, Vol. 26

Issue (4): 232-236

研究报告

本期目录 | 过刊浏览

时效制度对Al-Zn-Mg-Cu铝合金应力腐蚀敏感性的影响

孙志华;刘明辉;张晓云;高健;陆峰;汝继刚

北京航空材料研究院

Effect of Tempered Conditions on the Stress Corrosion Cracking of Al-Zn-Mg-Cu Alloy

;;;;;

北京航空材料研究院

全文: PDF(368 KB)

摘要: 采用恒载荷拉伸应力腐蚀试样、恒变形C环应力腐蚀试样以及预裂纹双悬臂(DCB)试样，对不同时效制度处理的7B04预拉伸厚板的应力腐蚀性能进行测定，并进行了扫描电镜断口形貌分析.研究表明，其抗应力腐蚀性能与时效制度密切相关，从峰值时效T6状态到过时效T74、T73状态，应力腐蚀敏感性依次降低.预拉伸厚板T6状态的应力腐蚀门槛值为120 MPa，而T74状态的应力腐蚀门槛值为300 MPa.T74状态的应力腐蚀开裂应力强度因子KISCC是T6的近2倍，且应力腐蚀裂纹扩展速率(da/dt)也明显降低.T6状态和T74状态的7B04铝合金应力腐蚀断裂为沿晶断裂，并有二次裂纹.而T73状态的断口形貌无典型的应力腐蚀沿晶断裂特征，为孔洞腐蚀特征，而且其KISCC几乎接近KIC.这说明T73状态的7B04铝合金几乎没有应力腐蚀敏感性.

关键词 ： Al-Zn-Mg-Cu铝合金, 时效制度, 应力腐蚀敏

Abstract：High strength Al-Zn-Mg-Cu aluminum alloys are widely used in airframe construction.However,this series of alloys are susceptible to stress corrosion cracking (SCC) to limit their usefulness.The tempered conditions and microstructural characteristics of Al-Zn-Mg-Cu aluminum alloys are well known to have a strong effect on SCC susceptibility.7B04 aluminum alloy belongs to Al-Zn-Mg-Cu alloys and is gained from 7A04 alloy through purification.The purpose of this investigation is to evaluate the influence of tempered conditions upon the SCC susceptibility of 7B04 alloy.The SCC behavior of 7B04 plate material was investigated in short transverse direction performing constant load test usi ng uniaxially smooth tension specimens,constant strain loaded tests using C-ring specimens and pre-cracking tests using double cantilever beam (DCB) specimens.The study also included the fractography examination by scanning electron micrograph (SEM).The results show that the resistance of SCC is much related to the tempered conditions.The SCC susceptibility of 7B04 alloy decreases from the near peak strength of T6 temper to over-aging T74 then to T73 condition.The threshold values of stress corrosion cracking (σth ) of T6 temper and T74 temperare 120 MPa and 300 MPa respectively.The threshold stress intensity factor for susceptibility to stress corrosion cracking (KISCC) of T74 temper is two times of T6 temper and the stage Ⅱ crack growth rate (da/dt)Ⅱ of T74 temper is also much lower than that of T651 temper.The fractographs of T6 temper and T74 temper reveal intergranular fracture.While the fractographs of T73 temper do not show intergranular fracture,but pitting corrosion characteristic and the KISCC is almost the same as KIC.This indicates that there is hardly SCC susceptibility for T73 temper.That is related to the microstructure difference when the temper is different.The main precipitated phases in the T6 temper are composed of G.P zone and small quantity of η′ phase,there is not the obvious precipitated free zone(PFZ),while in the T74 temper there are η′ and η phases and their sizes are getting bigger, and the precipitate free zone (PFZ) gets wider.The increasing of precipitate size and PFZ can generally improve the SCC resistance.

Key words： Al-Zn-Mg-Cu aluminum alloy stress corrosion cracking tempered conditions

收稿日期: 2005-12-20

ZTFLH:

TG172.9

通讯作者: 孙志华 E-mail: zhihua.sun@biam.ac.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	孙志华
	刘明辉
	张晓云
	高健
	陆峰
	汝继刚
44.8K

引用本文:

孙志华; 刘明辉; 张晓云; 高健; 陆峰; 汝继刚 . 时效制度对Al-Zn-Mg-Cu铝合金应力腐蚀敏感性的影响[J]. 中国腐蚀与防护学报, 2006, 26(4): 232-236 .
. Effect of Tempered Conditions on the Stress Corrosion Cracking of Al-Zn-Mg-Cu Alloy. J Chin Soc Corr Pro, 2006, 26(4): 232-236 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2006/V26/I4/232

[1]Buhl H.Stress Corrosion Cracking[M].Beijing:Internal Document,1981
[2]Tsai T C,Chuang T H.Role of grain size on the stress corrosioncracking of 7475 aluminum alloys[J].Mater.Sci.Eng.,1997,A225:135-144
[3]Liu J H,Li D,Guo B L,et al.Slow strain rate tension test of high-strength aluminum LC4[J].Mater.Sci.Technol.,2001,9(1):37-41(刘继华,李荻,郭宝兰等.LC4高强铝合金的慢应变速率拉伸试验[J].材料科学与工艺,2001,9(1):37-41)
[4]Qiang J G,Li D,Guo B L,et al.Corrosion behavior of high-strength aluminum LC4[J].Corros.Prot.,2002,23(8):340-343(钱建刚,李荻,郭宝兰等.LC4高强度铝合金的腐蚀行为研究[J].腐蚀与防护,2002,23(8):340-343)
[5]Ning A I,Zeng S M.Effect of aging system on microstructure andmechanical properties of 7B04 aluminum alloy[J].Chin.J.Nonferr.Metal.,2004,14(6):922-927
[6]Ru J G,Yi L N.The effect of high purification on the properties ofAl-Zn-Mg-Cu high strength aluminum alloy[J].J.AeronauticalMaterials,2003,23(supplement):5-7(汝继刚,伊琳娜.高纯化对Al-Zn-Mg-Cu系高强度铝合金性能的影响[J].航空材料学报,2003,23(supplement):5-7)

[1]	李仁顺;王佐义. 预温变形对2O91　Al-Li-Cu-Mg-Zr合金应力腐蚀敏感性的影响[J]. 中国腐蚀与防护学报, 1995, 15(1): 15-20.

Viewed

Full text

Abstract

Cited

Shared

Discussed