离子轰击镀对铀上铝镀层组织及防腐蚀性能的影响
吕学超;鲜晓斌;汪小琳
中国工程物理研究所
EFFECT OF ION BOMBARDMENTS ON MICROSTRUCTURESAND CORROSION RESISTANCE OF ALUMINUMCOATINGS ON URANIUM SUBSTRATE
Xuechao Lv;Xiaobin Xian;Xiaolin wang
中国工程物理研究所
全文: PDF(278 KB)  
摘要: 研究了偏压镀、循环氩离子轰击镀和间歇式镀对铀上铝镀层 组织及防腐蚀性能的影响.结果表明,3种离子轰击镀方法对铝镀层的组织产生强烈影响,且 组织的致密程度与其防腐蚀性能呈现了较好的一致性.在-100 V、-200 V和-500 V偏压条件 下,镀层组织致密、防腐蚀性好;在-300 V偏压下,镀层的致密性和防腐蚀性均差,未加偏压(0 V) 的次之;循环氩离子轰击镀和间歇式镀对提高镀层的致密性和防腐蚀性更为显著.离子轰击镀 沉积的铝镀层均可不同程度地为铀提供好的保护效果.
关键词 离子轰击镀镀层组织防腐蚀性能    
Abstract:Effect of three kinds of ion bombardments,including deposited with d.c.bias voltages,circulated-argon ion bombardment,and at in tervals on microstructures and corrosion resistance of aluminum coatings on uranium substrate was investigated.The results show that coating microstructu res are influenced strongly by ion bombardment methods,of which coating microstr uctures correspond to their different corrosion resistance to uranium. The microstructures are much more closely packed and the corrosion resistance ar e much better at -100 V,-200 V and -500 V than those of at -300 V,0 V .The microstructures and corrosion resistance of aluminum coatings ca n also be improved remarkably by both circulated-argon ion bombardment and at in tervals deposition.All of aluminum coatings can provide protection for uranium t o different extent.
Key wordsion bombardment    coatings    microstructure    corrosion resi stance
收稿日期: 2002-05-14     
ZTFLH:  TL214.6  
通讯作者: 吕学超   
Corresponding author: Xuechao Lv   

引用本文:

吕学超; 鲜晓斌; 汪小琳 . 离子轰击镀对铀上铝镀层组织及防腐蚀性能的影响[J]. 中国腐蚀与防护学报, 2003, 23(5): 299-303 .
Xuechao Lv, Xiaobin Xian, Xiaolin wang. EFFECT OF ION BOMBARDMENTS ON MICROSTRUCTURESAND CORROSION RESISTANCE OF ALUMINUMCOATINGS ON URANIUM SUBSTRATE. J Chin Soc Corr Pro, 2003, 23(5): 299-303 .

链接本文:

https://www.jcscp.org/CN/      或      https://www.jcscp.org/CN/Y2003/V23/I5/299

[1]QianMG ,YaoSS ,ZhangSZ .ModernSurfaceTechnology[M ].Beijing:MechanicalIndustryPress.1994:217(钱苗根,姚寿山,张少宗.现代表面技术[M ].北京:机械工业出版社,1994:217)
[2]GreenwoodRC ,RitchieAG ,SrandlesJ,etal.Preparation.Charac teristicandcorrosionresistanceofuraniumion-platedwithalu minum[R].ResearchReportNo.023/82,1983
[3]ChangF ,LevyM ,JackmanB .Assessmentofcorrosion-resistantcoatingsforadepleteduranium-0.75titaniumalloy[J].Surf.Coat.Technol.,1991,48:31
[4]RavehA ,ArkushR ,ZalkindS .Passivationofuraniummetalbyra dio-frequencyplasmanitridingagainstgasphase(H2,H2O)corro sion[J].Surf.Coat.Technol.,1996,82:38.
[5]WangHH ,TianMB .SurfaceStrengtheningbyIonBeam[M ].Beijing:MechanicalIndustryPress,1992:152(汪宏泓,田民波.离子束表面强化[M ].北京:机械工业出版社,1992:152)
[6]HurkmansT ,LewisDB ,ParitongH ,etal.Influenceofionbom bardmentonstructureandpropertiesofunbalancedmagnetrongrownCrxNcoatings[J].Surf.Coat.Technol.,1999,114:52
[7]EgertCM .ScottDG .Studyofionplatingparameters,coatingstructureandcorrosionprotectionforaluminumcoatingsonurani um[J].J.Vac.Sci.Technol.,1987,5A :2724
[8]SongSZ .MethodsinInvestigationofCorrosionElectrochemistry[M].Beijing:ChemicalIndustryPress.1994:100(宋诗哲.腐蚀电化学研究方法[M ].北京:化学工业出版社,1994:100)
[9]McGilivrayGW ,GeesonDA ,GreenwoodRC .Studiesoftheki neticsandmechanismoftheoxidationofuraniumbydryandmoistair[J].J .Nucl.Mater.,1994,208:81
[1] 李聪玮, 杜双明, 曾志琳, 刘二勇, 王飞虎, 马付良. 电流密度对Ni-Co-B镀层微观结构及磨蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(5): 439-447.
[2] 孙硕, 杨杰, 钱薪竹, 常人丽. Ni-Cr-P化学镀层的制备与电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(3): 273-280.
[3] 杨寅初,傅秀清,刘琳,马文科,沈莫奇. 喷射电沉积Ni-P-BN(h)-Al2O3复合镀层的耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 57-62.
[4] 袁玮,黄峰,甘丽君,戈方宇,刘静. 显微组织对X100管线钢氢致开裂及氢捕获行为影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 536-542.
[5] 付安庆,赵密锋,李成政,白艳,朱文军,马磊,熊茂县,谢俊峰,雷晓维,吕乃欣. 激光表面熔凝对超级13Cr不锈钢组织与性能的影响研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 446-452.
[6] 丰涵,宋志刚,吴晓涵,李惠,郑文杰,朱玉亮. 022Cr25Ni7Mo4N双相不锈钢选择性腐蚀行为与两相组织的关系研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 138-144.
[7] 蒋斌, 曾利兰, 梁涛, 潘浩波, 乔岩欣, 张竞, 赵颖. 316L不锈钢表面超疏水微纳镍镀层定向电沉积工艺优化研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 438-446.
[8] 王凯, 易耀勇, 卢清华, 易江龙, 江泽新, 马金军, 张宇. 基于窄间隙焊接的热模拟峰值温度对Q690高强钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(5): 447-454.
[9] 常亮, 师超, 邵亚薇, 王艳秋, 刘斌, 孟国哲. 植酸转化膜对环氧清漆防腐性能的影响[J]. 中国腐蚀与防护学报, 2018, 38(3): 265-273.
[10] 蒋光锐, 刘广会. Zn-Al-Mg合金的凝固组织及其耐腐蚀性能[J]. 中国腐蚀与防护学报, 2018, 38(2): 191-196.
[11] 牛振国, 郭浦山, 叶宏, 杨丽景, 许赪, 宋振纶. Zn-7Mg合金热处理显微组织演变及耐蚀性能研究[J]. 中国腐蚀与防护学报, 2017, 37(4): 347-353.
[12] 蒋光锐, 王海全, 黎敏, 刘广会, 谢春乾. 锌基合金镀层钢板的耐蚀性研究[J]. 中国腐蚀与防护学报, 2017, 37(4): 354-359.
[13] 滕彧,陈旭,何川,王义闯,王冰. 显微组织对X70钢在含有硫酸盐还原菌的3.5%NaCl溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2017, 37(2): 168-174.
[14] 胡骞,刘静,王玉昆,黄峰,戴明杰,侯阳来. 不同组织A710钢在NaCl溶液中耐蚀性对比研究[J]. 中国腐蚀与防护学报, 2016, 36(6): 611-616.
[15] 周琼宇,王小芬,钟庆东,王操,胡一峰. 镀液pH值对电沉积Ni-W合金镀层结构及其耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2016, 36(5): 457-462.