取代基咪唑啉分子结构与缓蚀性能的实验研究

王大喜;王兆辉

石油大学（北京）化工学

EXPERIMENTAL STUDIES OF STRUCTURE AND INHIBITION EFFICIENCY OF IMIDAZOLINE DERIVATIVES

;

石油大学（北京）化工学

全文: PDF(112 KB)

摘要: 合成了四个取代基咪唑啉化合物，并进行IR和UV分析.用电化学和失重法测试了化合物Ⅰ-Ⅳ的缓蚀率，发现四个取代基咪唑啉化合物的缓蚀率依次增大. 从实验的角度探索了取代基与缓蚀性能的关系.实验结果和理论分析表明：具有P-π共轭体系的咪唑啉化合物并同时在环上引入供电子基团，特别是具有共轭体系的取代芳烃，能增强咪唑啉型化合物的缓蚀性能.

关键词 ：咪唑啉, 合成, 结构, 缓蚀性能

Abstract：Four imidazoline inhibitors have been synthesized and determined by IR and UV spectral analyses. The inhibition efficiency was measured using weight l oss and electrochemical methods. It is found that percentage inhibition corrosio n is increased as in following order: compound I<Ⅱ<Ⅲ<Ⅵ. The relationship bet ween structure of the compounds and corrosion inhibition efficiency is explored from experiment. Through measured results and theoretical analyses, it is indica ted that imidazoline with P-π conjugated system and electron donor group, parti cularly, the substituent aromatic group, introduced to imidazoline ring can impr ove the inhibition efficiency of imidazoline derivatives.

Key words： imidazoline synthesis structure inhibition efficiency

收稿日期: 1999-12-03

ZTFLH:

TG174.42

通讯作者: 王大喜 E-mail: daxiwang@public.fhnet.cn.net

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	王大喜
	王兆辉
44.8K

引用本文:

王大喜; 王兆辉 . 取代基咪唑啉分子结构与缓蚀性能的实验研究[J]. 中国腐蚀与防护学报, 2001, 21(2): 112-116 .
. EXPERIMENTAL STUDIES OF STRUCTURE AND INHIBITION EFFICIENCY OF IMIDAZOLINE DERIVATIVES. J Chin Soc Corr Pro, 2001, 21(2): 112-116 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2001/V21/I2/112

[1]ZhengJiaxin .ThepresentsituationofresearchandapplicationofinhibitorsinChina[J].Corrosion&Protection ,1997,18(3) :132 - 136
[2 ]ZhengJiaxin ,ZhaoJG .ControlofcorrosionbyinhibitorsindrillingmudscontaininghighconcentrationofH2 S[J].Corrosion ,1993,49(2 ) :170 - 174
[3]NingSG ,ShiML ,etal.Therelationshipofcorrosioninhibitionefficiencyonsteelinacidswithelectrondensityandtheenergyoffronticalorbitalofimidzolinederivatives[J].JChineseSocietyforCorrosionandProtection ,1990 ,10 (4 ) :383- 390
[4 ]SastriVS ,PerumareddiJR .Selectionofcorrosioninhibitorsforuseinsourmedia[J].Corrosion ,1994,5 0 (6 ) :432 - 437
[5 ]ZhengJia xin ,LuZhan peng ,etal.Synthesis,identificationandinhibitorypropertyofanewimidazolinecorrosioninhibitor[J].OilfieldChemistry ,1994,11(2 ) :16 3- 16 7(ZhengJS ,LuZP ,PengFM .新型咪唑啉类缓蚀剂的合成、结构表征及缓蚀性能研 [J].油田化学 ,1994,11(2 ) :16 3-16 7)
[6 ]LiShuan ,ChenShangkai.Studyoncatalyticsynthesisofimidazolinecationicsurfactant[J].FinePetroleumChemicals ,1995 ,6 :15 - 17(China)(李树安 ,黄超 .咪唑啉型磷酸盐两性表面活性剂的合成 [J].精细石油化工 ,1996 ,(5 ) :13- 16 )
[7]WangDaxi,LiShuyuanetal.QuantumchemicalcalculationchemicaladsorptionenergyofimidazolinesandFeatom[A].Gor donResearchConferences[C],1998,7,NewLondon ,USA0

[1]	白云龙, 沈国良, 覃清钰, 韦博鑫, 于长坤, 许进, 孙成. 硫脲基咪唑啉季铵盐缓蚀剂对X80管线钢腐蚀的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[2]	于浩冉, 张文丽, 崔中雨. 4种镁合金在Cl^--NH₄⁺-NO₃^-溶液体系中的腐蚀行为差异研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 553-559.
[3]	李聪玮, 杜双明, 曾志琳, 刘二勇, 王飞虎, 马付良. 电流密度对Ni-Co-B镀层微观结构及磨蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(5): 439-447.
[4]	闻洋, 熊林, 陈伟, 薛刚, 宋文学. 干湿循环下聚乙烯醇纤维混凝土抗Cl^-渗透性能研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 381-388.
[5]	邵明鲁, 刘德新, 朱彤宇, 廖碧朝. 乌洛托品季铵盐缓蚀剂的合成与复配研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 244-250.
[6]	伊红伟, 胡慧慧, 陈长风, 贾小兰, 胡丽华. CO₂环境下油酸咪唑啉对X65钢异种金属焊缝电偶腐蚀的抑制作用研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 96-104.
[7]	姜冬雪,付颖,张峻巍,张伟,辛丽,朱圣龙,王福会. 钛合金表面Al₂O₃陶瓷膜制备及性能研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 469-476.
[8]	潘成成,马超,夏大海. EBSD技术研究金属材料晶体取向对大气腐蚀萌生的影响机理[J]. 中国腐蚀与防护学报, 2019, 39(6): 495-503.
[9]	魏欣欣,张波,马秀良. FeCr₁₅Ni₁₅单晶600 ℃下热生长氧化膜的TEM观察[J]. 中国腐蚀与防护学报, 2019, 39(5): 417-422.
[10]	于美,魏新帝,范世洋,刘建华,李松梅,钟锦岩. 应力作用下2297铝锂合金腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 439-445.
[11]	史昆玉,张进中,张毅,万毅. Nb₂N涂层制备及其耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 313-318.
[12]	刘建国,高歌,徐亚洲,李自力,季菀然. 咪唑啉类衍生物缓蚀性能研究[J]. 中国腐蚀与防护学报, 2018, 38(6): 523-532.
[13]	蒋斌, 曾利兰, 梁涛, 潘浩波, 乔岩欣, 张竞, 赵颖. 316L不锈钢表面超疏水微纳镍镀层定向电沉积工艺优化研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 438-446.
[14]	樊志民, 于锦, 宋影伟, 单大勇, 韩恩厚. 镁合金点蚀的研究进展[J]. 中国腐蚀与防护学报, 2018, 38(4): 317-325.
[15]	刘峥, 李海莹, 王浩, 赵永, 谢思维, 张淑芬. 分子动力学模拟水溶液中席夫碱基表面活性剂在Zn表面的吸附行为[J]. 中国腐蚀与防护学报, 2018, 38(4): 381-390.

Viewed

Full text

Abstract

Cited

Shared

Discussed