| INFLUENCE OF SHORT-TERM IMMERSION IN SEA WATER ON FRACTURE CHARACTERISTIC OF Q235 STEEL |
| WANG Limin, WANG Dongxu, FENG Ying, HAN Minglan, HAN Daoping |
| School of Science, Qingdao Technological University, Qingdao 266033 |
|
|
|
|
Abstract In order to investigate the fracture properties of low carbon steel after seawater immersion and reloading, Q235 steel were made into a series of rectangle cross-section beams with prefabricated crack, and the specimens were divided a few group according to the history of its loading or reloading before and after soaking in room temperature seawater. The fracture behavior of specimen was analyzed in different test conditions, and their bearing capacity was compared with each other for loading before and after soaking. The length of plastic zone of specimen which was soaked in seawater for short-term after loaded into plastic zone became shorter and the material was more brittle.
|
|
Received: 19 October 2011
|
|
|
|
Corresponding Authors:
WANG Limin
E-mail: wanglimin@qtech.edu.cn
|
| [1] Fragiel A, Serna S, Perez R. Electrochemical study of two microalloyed pipeline steels in H2S environments [J]. Intern.J. Hydrogen Energy, 2005, 30: 1303-1309[2] Jia Y Z, Wang J Q, Han E H, et al. Stress corrosion cracking behavior of X100 pipeline steel in NS4 solution under constant loading test [J]. J. Chin. Soc. Corros. Prot., 2011, 31(3):184-189 (郏义征, 王俭秋, 韩恩厚等.X100管线钢在恒载荷作用下的应力腐蚀开裂[J]. 中国腐蚀与防护学报, 2011,31(3): 184-189)[3] Melchers R E, Jeffrey R. Early corrosion of mild steel in seawater [J]. Corros. Sci., 2005, 47(7): 1678-1693[4] Huang G Q. Corrosion behavior of carbon steels immersed in sea areas of China [J]. Corros. Sci. Prot. Technol., 2001, 13(2):81-88 (黄桂桥. 碳钢在我国不同海域的海水腐蚀行为[J].腐蚀科学与防护技术，2001, 13(2): 81-88)[5] Zheng Y Y, Wang J, Zou Y. Research progress on corrosion of carbon steels under rust layer in marine environment [J]. Corros. Sci. Prot.Technol., 2011, 23(1): 93-98 (郑莹莹, 王佳, 邹妍. 海洋环境中锈层下碳钢腐蚀行为的研究进展[J].腐蚀科学与防护技术, 2011, 23(1): 93-98)[6] Tang X, Wang J. Characteristics of micro area distribution of electrochemical parameters on Q235 steel under NaCl electrolyte droplet [J]. Corros. Sci. Prot. Technol., 2010, 22(4): 299-302 (唐晓，王佳. Q235钢/NaCl液滴界面微区电化学特征参数分布特征[J]. 腐蚀科学与防护技术, 2010, 22(4): 299-302)[7] Jiang L, Cao G, Mao X H, et al. Effect of Microbes on early corrosion behavior of Q235 steel in fresh water [J]. J. Chin. Soc. Corros. Prot., 2009, 29(3): 177-181 (江莉, 曹钢, 毛旭辉等. 淡水微生物对Q235钢早期腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2009, 29(3): 177-181)[8] Biezma M V. The role of hydrogen in microbiologically influenced corrosion and stress corrosion cracking [J]. Intern. J.Hydrogen Energy, 2001, 26(5): 515-520[9] Tang Z L, Song X, Zhang Y P. Control factors of time of wetness and IRP corrosion rate for Q235 steel under pure water thin film [J]. J.Chin. Soc. Corros. Prot., 2009, 29(3): 161-166 (唐子龙, 宋鑫, 张义萍.纯水薄液膜下Q235钢潮湿时间的影响因素和腐蚀速度的磁阻研究[J].中国腐蚀与防护学报, 2009, 29(3): 161-166)[10] Liu H Y, Liang X F, Shao Y W, et al.Effect of hydrostatic pressure of 3.5% NaCl solution on the corrosion behavior of epoxy coating [J].J. Chin. Soc. Corros. Prot., 2010, 30(5): 374-378 (刘浩宇, 梁小峰, 邵亚薇等. 静水压力下Q235钢环氧涂层在 3.5% NaCl 溶液中的失效过程[J]. 中国腐蚀与防护学报, 2010, 30(5): 374-378)[11] Chen H L, Li X J, Wei Y. Corrosion mechanism of carbon steel in chloride solution[J]. Corros. Prot., 2007, 28(1): 17-19 (陈惠玲, 李晓娟, 魏雨. 碳钢在含氯离子环境中腐蚀机理的研究[J].腐蚀与防护, 2007, 28(1): 17-19)[12] Cai M H, Ding H，Zhang J S, et al. Deformation and fracture characteristics of ferrite/bainite dual-phase steels [J]. Chin. J. Mater. Res., 2009, 23(1): 83-88 (蔡明辉, 丁桦, 张建苏等. 铁素体/贝氏体双相钢的变形与断裂特性[J]. 材料研究学报, 2009, 23(1): 83-88)[13] Hertzberg R W. Deformation and Fracture Mechanics of Engineering Materials [M]. New York: John Wiley & Sons Inc, 1996[14] Wang L M, Sun M Y, He G Z, et al. Electronical measurement of fracture process of cast iron incision specimen and calculation of the structure bearing capacity [J]. Acta Metall.Sin., 2008, 44(7): 853-858 (王利民, 孙明远, 贺光宗等.铸铁缺口梁断裂过程测试和承载力[J]. 金属学报, 2008, 44(7): 853-858)[15] Wang L M, Xu S L, Zhao X Q. Analysis on cohesive crack opening displacement considering the strain softening effect [J].Sci. Chin. Ser. G Phys., Mech. Astron., 2006, 49(1): 88-101[16] Tada H, Paris P C, Irwin G R. The Stress Analysis of Cracks Handbook (3rd Ed.)[M]. New York: American Society of Mechanical Engineers, 2000[17] Neman Jr J C, James M A, Zerbst U. A review of the CTOA/CTOD fracture criterion [J]. Eng. Fract. Mech., 2003, 70:371-385 |
| No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|