| Research Progress on Failure Analysis and Protective Measures of Ship Hull Materials |
WANG Deling1, LIU Yijun2, GUO Zhangwei2, LIU Tao2( ) |
1.School of Law, Shanghai Maritime University, Shanghai 201306, China
2.College of Marine Science and Engineering, Shanghai Maritime University, Shanghai 201306, China |
|
Cite this article:
WANG Deling, LIU Yijun, GUO Zhangwei, LIU Tao. Research Progress on Failure Analysis and Protective Measures of Ship Hull Materials. Journal of Chinese Society for Corrosion and protection, 2025, 45(3): 611-619.
|
|
|
Abstract During the service process of a ship, of which different parts encounter different conditions of multi-factor coupling in the real service, which can lead to the premature failure of some materials, posing significant safety hazards to the ship's service life. This article provides an overview of common material failure modes for different parts of ships, with a focus on corrosion failure. It elaborates on the failure locations, forms, and causes of ship hull materials, as well as failure detection methods, and proposes corresponding protective measures.
|
|
Received: 12 August 2024
32134.14.1005.4537.2024.250
|
|
|
Corresponding Authors:
LIU Tao, E-mail: liutao@shmtu.edu.cn
|
| [1] |
Zhang D, Miao B B. Research on key technologies of ship intelligent navigation [J]. Mar. Equip. Mater. Market., 2024, 32(7): 4
|
|
张 帝, 苗保彬. 船舶智能航行关键技术研究 [J]. 船舶物资与市场, 2024, 32(7): 4
|
| [2] |
Liu Y, Pan Z T, Zhang H, et al. Thermal-mechanical coupling in drilling high-performance CFRP: scale-span modeling and experimental validation [J]. Compos. Struct., 2024, 331: 117903
|
| [3] |
Li H J, Huang J J, Xu X P. Research on the reliablity of ship material quality inspection [J]. GSI Shipbuild. Technol., 2023, 43(3): 87
|
|
李红菊, 黄佳建, 徐晓萍. 船舶材料质量检测可靠性的探讨 [J]. 广船科技, 2023, 43(3): 87
|
| [4] |
Lin Y, Liu T, Guo Y B, et al. Research and development of welding materials for low-temperature steel and corrosion evaluation methods [J]. J. Chin. Soc. Corros. Prot., 2024, 44: 957
|
|
林 一, 刘 涛, 郭彦兵 等. 船用低温钢焊接材料的研发与腐蚀方法评价 [J]. 中国腐蚀与防护学报, 2024, 44: 957
|
| [5] |
Xing S H, Peng W S, Qian Y, et al. Effect of seawater flow velocity on pitting corrosion of 2205 stainless steel with different surface treatments [J]. J. Chin. Soc. Corros. Prot., 2024, 44: 658
|
|
邢少华, 彭文山, 钱 峣 等. 海水流速对经抛光和钝化表面处理的2205不锈钢点蚀的影响 [J]. 中国腐蚀与防护学报, 2024, 44: 658
doi: 10.11902/1005.4537.2023.208
|
| [6] |
Sun J Y, Peng W S, Xing S H. Combined effect of stress and dissolved oxygen on corrosion behavior of Ni-Cr-Mo-V high strength steel [J]. J. Chin. Soc. Corros. Prot., 2024, 44: 755
|
|
孙佳钰, 彭文山, 邢少华. 应力-溶解氧耦合对Ni-Cr-Mo-V高强钢腐蚀行为的影响 [J]. 中国腐蚀与防护学报, 2024, 44: 755
doi: 10.11902/1005.4537.2023.213
|
| [7] |
Bai X H, Ding K K, Zhang P H, et al. Accelerated corrosion test of AH36 ship hull steel in marine environment [J]. J. Chin. Soc. Corros. Prot., 2024, 44: 187
|
|
白雪寒, 丁康康, 张彭辉 等. AH36船用钢海水加速腐蚀试验研究 [J]. 中国腐蚀与防护学报, 2024, 44: 187
|
| [8] |
Zhang J H, Xu Y C, Jia X Y, et al. Preparation and corrosion resistance of Superamphiphobic surface on B10 Cu-alloy [J]. J. Chin. Soc. Corros. Prot., 2024, 44: 909
|
|
张吉昊, 徐亚程, 贾学远 等. B10铜合金超双疏表面的制备及其性能研究 [J]. 中国腐蚀与防护学报, 2024, 44: 909
doi: 10.11902/1005.4537.2023.290
|
| [9] |
Wang X, Li M, Liu F, et al. Effect of temperature on erosion-corrosion behavior of B10 Cu-Ni alloy pipe [J]. J. Chin. Soc. Corros. Prot., 2023, 43: 1329
|
|
王 晓, 李 明, 刘 峰 等. 温度对B10铜镍合金管冲刷腐蚀行为影响规律研究 [J]. 中国腐蚀与防护学报, 2023, 43: 1329
|
| [10] |
Yang X Y, Li Z, Duan T G, et al. Erosion corrosion behavior in flowing seawater for 70Cu-30Ni alloy pipelines with chemical conversion film preformed in flowing FeSO4 solution [J]. J. Chin. Soc. Corros. Prot., 2023, 43: 561
|
|
杨新宇, 李 祯, 段体岗 等. 70Cu-30Ni合金管FeSO4预成膜及冲刷腐蚀行为分析 [J]. 中国腐蚀与防护学报, 2023, 43: 561
doi: 10.11902/1005.4537.2022.156
|
| [11] |
Peng W S, Xing S H, Qian Y, et al. Effect of flowing seawater on corrosion characteristics of passivation film on TA2 Pure-Ti pipes [J]. J. Chin. Soc. Corros. Prot., 2024, 44: 1038
|
|
彭文山, 邢少华, 钱 峣 等. 流动海水冲刷下TA2纯钛管路钝化膜腐蚀特性研究 [J]. 中国腐蚀与防护学报, 2024, 44: 1038
doi: 10.11902/1005.4537.2023.292
|
| [12] |
Wang Z H, Bai Y, Ma X, et al. Numerical simulation of galvanic corrosion for couple of Ti-alloy with Cu-alloy in seawaters [J]. J. Chin. Soc. Corros. Prot., 2018, 38: 403
|
|
王振华, 白 杨, 马 晓 等. 钛合金和铜合金管路电偶腐蚀数值仿真 [J]. 中国腐蚀与防护学报, 2018, 38: 403
doi: 10.11902/1005.4537.2017.113
|
| [13] |
Jiang C. Effect of magnetic field on marine magnesium alloy in simulated seawater [J]. Int. Comb. Eng. Parts, 2020, (2): 107
|
|
姜 超. 磁场对船用镁合金在模拟海水中的研究 [J]. 内燃机与配件, 2020, (2): 107
|
| [14] |
Mao Y C, Zhu Y, Sun S K, et al. Localized corrosion of 5083 Al-alloy in simulated marine splash zone [J]. J. Chin. Soc. Corros. Prot., 2023, 43: 47
|
|
毛英畅, 祝 钰, 孙圣凯 等. 5083铝合金在模拟海洋浪花飞溅区的局部腐蚀行为 [J]. 中国腐蚀与防护学报, 2023, 43: 47
doi: 10.11902/1005.4537.2022.162
|
| [15] |
Deng C M, Liu Z, Xia D H, et al. Localized corrosion mechanism of 5083-H111 Al alloy in simulated dynamic seawater zone [J]. J. Chin. Soc. Corros. Prot., 2023, 43: 683
|
|
邓成满, 刘 喆, 夏大海 等. 5083-H111铝合金在模拟动态海水环境中的局部腐蚀机制 [J]. 中国腐蚀与防护学报, 2023, 43: 683
doi: 10.11902/1005.4537.2023.140
|
| [16] |
Yang X, Shi W B, Pan H P, et al. Design and establishment of typical material failure analysis case database for marine system [J]. Phys. Test. Chem. Anal., 2023, 59A(1) : 31
|
|
杨 晓, 施卫博, 潘恒沛 等. 船舶系统典型材料失效分析案例数据库的设计与建立 [J]. 理化检验-物理分册, 2023, 59A(1) : 31
|
| [17] |
Chen Z. Application and development of anti-corrosion technology for ships [J]. China Plant Eng., 2019, (4): 184
|
|
陈 智. 船舶防腐蚀技术的应用及发展 [J]. 中国设备工程, 2019, (4): 184
|
| [18] |
Wang L Q. Ship corrosion causes and protection technology [J]. China Water Transp., 2008, 8(10): 20
|
|
王来强. 船舶腐蚀成因及防护技术 [J]. 中国水运, 2008, 8(10): 20
|
| [19] |
Gu C X, Ji G J, Zhu G J, et al. Ship corrosion and anti-corrosion measures [J]. Ship Eng., 2010, 32(3): 1
|
|
顾彩香, 吉桂军, 朱冠军 等. 船舶的腐蚀与防腐措施 [J]. 船舶工程, 2010, 32(3): 1
|
| [20] |
Li J, Huang J. Genesis of the ship and its corresponding corrosion protection technology [J]. Sci. Technol. Innovat., 2014, (18): 27
|
|
李 杰, 黄 金. 探讨船舶腐蚀的成因及其相应的防护技术 [J]. 科技与创新, 2014, (18): 27
|
| [21] |
Li X J, Li H J. Ship corrosion environment analysis and protection [J]. Sci. Technol. Vis., 2016, (1): 116
|
|
李晓江, 李怀景. 船舶腐蚀环境分析及防护 [J]. 科技视界, 2016, (1): 116
|
| [22] |
Dong Y C. Ship corrosion and protection methods [J]. Chem. Ent. Manag., 2019, (6): 173
|
|
董艳冲. 船舶腐蚀与保护方法 [J]. 化工管理, 2019, (6): 173
|
| [23] |
Zhang X C. Fracture failure analysis of marine diesel engine crankshaft [J]. China Sci. Technol. Inform., 2013, (14): 122
|
|
张新春. 船舶柴油机曲轴断裂失效分析 [J]. 中国科技信息, 2013, (14): 122
|
| [24] |
Fathyunes L, Mohtadi-Bonab M A. A review on the corrosion and fatigue failure of gas turbines [J]. Metals, 2023, 13: 701
|
| [25] |
Xu X L, Yu Z W. Failure analysis of a marine intermediate shaft [J]. Eng. Fail. Anal., 2021, 126: 105464
|
| [26] |
Xiong J. Fracture failure analysis of marine diesel engine camshaft [J]. China Ship Repair, 2014, 27(1): 20
|
|
熊 军. 船用柴油机凸轮轴的断裂失效分析 [J]. 中国修船, 2014, 27(1): 20
|
| [27] |
Lu H, Sun M Z. Failure analysis of marine diesel engine cylinder pulling [J]. Phys. Test. Chem. Anal., 2022, 58A(2) : 45
|
|
陆 慧, 孙明正. 船用柴油机拉缸故障失效分析 [J]. 理化检验-物理分册, 2022, 58A(2) : 45
|
| [28] |
Wang Y H, Zhang W H, Gao X J. Early failure analysis and preventive measures of marine diesel engine bearing [J]. Appl. Energy Technol., 2003, (6): 1
|
|
王延宏, 张文华, 高宪军. 船舶柴油机轴瓦早期失效分析及防止措施 [J]. 应用能源技术, 2003, (6): 1
|
| [29] |
Zong M Z, Xiao H Z. The corrosion of vessel's sea water piping system and the improvement measures [J]. J. Ship Des., 2011, (3): 44
|
|
宗明珍, 肖海忠. 船舶海水管系腐蚀的原因及防腐蚀措施 [J]. 船舶设计通讯, 2011, (3): 44
|
| [30] |
Zhang M L. Corrosion cause and anti-corrosion measure of marine sea water piping in warship [J]. Total Corros. Control, 2010, 24(6): 5
|
|
张敏丽. 船舶海水管系腐蚀的原因及其防护 [J]. 全面腐蚀控制, 2010, 24(6): 5
|
| [31] |
Wang L, Yan X L, Liu D Q. Anti-corrosion research of marine seawater cooler [J]. Mech. Electr. Technol., 2015, (3): 111
|
|
王 龙, 闫小龙, 刘地清. 船舶海水冷却器的防腐蚀研究 [J]. 机电技术, 2015, (3): 111
|
| [32] |
Xu X, Wu X W, Zhang G, et al. Tightness failure analysis and protective measures of crevice corrosion for seawater piping in ships [J]. Ship Boat, 2016, 27(5): 57
|
|
徐 雄, 武兴伟, 张 刚 等. 船舶海水管路缝隙腐蚀密封性能失效分析及其防护措施 [J]. 船舶, 2016, 27(5): 57
|
| [33] |
Shen J P, Lin C. Corrosion prevention of ship seawater system [J]. Anhui Arch., 2010, 17(1): 51
|
|
沈捷攀, 林 晨. 船舶海水管系的防腐蚀探讨 [J]. 安徽建筑, 2010, 17(1): 51
|
| [34] |
Hou S F, Zhou Z J. Corrosion problems and anti-corrosion measure of marine sea water piping [J]. J. Jiangsu Shipping College, 2008, 7(4): 76
|
|
侯淑芳, 周志军. 船舶海水管系的腐蚀问题及防止措施 [J]. 南通航运职业技术学院学报, 2008, 7(4): 76
|
| [35] |
Jiang X F. Research on corrosion and anticorrosion technology of marine sea water pipeline [J]. Mar. Equip. Mater. Market., 2023, 31(9): 58
|
|
姜雪锋. 船舶海水管系管材腐蚀及防腐技术研究 [J]. 船舶物资与市场, 2023, 31(9): 58
|
| [36] |
Ren X H. Research on corrosion and monitoring technology of ship seawater pipeline [J]. Policy Res. Explor. (Middle), 2019, (9): 25
|
|
任祥华. 船舶海水管路腐蚀及监测技术研究 [J]. 决策探索(中), 2019, (9): 25
|
| [37] |
Zhang T, Yang F, Luo N Z, et al. Overview on corrosion of marine sea-water pipelines and a crucial monitoring technology [J]. Ship Sci. Technol., 2019, 41(7): 1
|
|
张 挺, 杨 锋, 罗宁昭 等. 船舶海水管路腐蚀及监测技术发展综述 [J]. 舰船科学技术, 2019, 41(7): 1
|
| [38] |
Zeng X Y, Chen Q Q. Corrosion of seawater pipeline on board and its prevention [J]. J. Shanghai Sci. Res. Inst. Shipping, 1997, 20(1): 47
|
|
曾晓燕, 陈全权. 船舶海水管系的腐蚀与防护 [J]. 交通部上海船舶运输科学研究所学报, 1997, 20(1): 47
|
| [39] |
Zhang W Y. Corrosion and protection of marine sea water pipelines [J]. Mar. Equip. Mater. Market., 2019, (10): 11
|
|
张文毓. 船舶海水管系腐蚀与防护 [J]. 船舶物资与市场, 2019, (10): 11
|
| [40] |
Sun C F, Liu Z L, Li G T. Research on failure detection technology of marine diesel engine piston [J]. Ship Sci. Technol., 2022, 44(16): 97
|
|
孙长飞, 刘昭亮, 李更天. 船舶柴油机活塞失效检测技术 [J]. 舰船科学技术, 2022, 44(16): 97
|
| [41] |
Lu H. Ship boiler corrosion and control [J]. Mar. Technol., 2003, (4): 58
|
|
陆 慧. 船舶锅炉腐蚀及控制 [J]. 航海技术, 2003, (4): 58
|
| [42] |
Xie Y C. Formation and measuresof electrochemical corrosion of marine boilers [J]. Sci. Technol. Inform. (Acad. Res.), 2006, (5): 42
|
|
谢以超. 船舶锅炉电化学腐蚀的形成与措施 [J]. 科技信息(学术版), 2006, (5): 42
|
| [43] |
Ma Q H, Fu D H, Qiu D F. Corrosion and protection for inner oil-fired tube of marine boiler [J]. China Ship Repair, 2008, 21(2): 25
|
|
马青华, 付大海, 裘达夫. 船舶锅炉燃油管内部腐蚀与防护 [J]. 中国修船, 2008, 21(2): 25
|
| [44] |
Chen Z Q. Analysis of corrosion crack defects in stern shaft and key points of ship management [J]. Mar. Technol., 2006, (2): 62
|
|
陈仲琦. 艉轴腐蚀裂纹缺陷分析及船舶管理要点 [J]. 航海技术, 2006, (2): 62
|
| [45] |
Guo Y B. Cause analysis and recommended measures for stern shaft corrosion of coastal small ships [J]. Mar. Technol., 2007, (suppl.1) : 60
|
|
郭育标. 沿海小型船舶尾轴腐蚀原因分析和建议的措施 [J]. 航海技术, 2007, (): 60
|
| [46] |
Jiang S. Corrosion causes and protective measures of stern shaft of small marine fishery ships [J]. China Fish., 2008, (4): 74
|
|
江 水. 小型海洋渔业船舶尾轴腐蚀原因及防护措施 [J]. 中国水产, 2008, (4): 74
|
| [47] |
He J F. Analysis on the causes of corrosion of swhip shafts and the problems of management [J]. China Ship Repair, 2018, 31(1): 28
|
|
何继锋. 船舶艉轴腐蚀原因及船机管理方面应注意的问题 [J]. 中国修船, 2018, 31(1): 28
|
| [48] |
Chen R. Causes of ship stern shaft corrosion and problems that should bepaid attention to in ship engine management [J]. Intell. City, 2019, (17): 188
|
|
陈 锐. 船舶艉轴腐蚀原因及船机管理方面应注意的问题 [J]. 智能城市, 2019, (17): 188
|
| [49] |
Li H. Study on corrosion causes and anticorrosive coatings of ship ballast tank [J]. China Water Transp., 2010, 10(1): 26
|
|
李 辉. 船舶压载舱腐蚀原因及防腐涂层的研究 [J]. 中国水运, 2010, 10(1): 26
|
| [50] |
Wang L W, Pang X B, Zhang Y L. Corrosion characteristics of steel vessel and protection measure [J]. China Ship Repair, 2016, 29(6): 6
|
|
王利伟, 逄喜斌, 张岳林. 钢质海船腐蚀特点与防护措施 [J]. 中国修船, 2016, 29(6): 6
|
| [51] |
Ma Z C, Xiao Q S. Effect of microbial corrosion on maintenance of ballast tank [J]. Guangdong Chem. Ind., 2019, 46(18): 87
|
|
马中存, 肖全山. 微生物腐蚀对船舶压载舱维护的影响 [J]. 广东化工, 2019, 46(18): 87
|
| [52] |
Almeida Bugio T M, Martins R F, Leal Das Neves L, et al. Failure analysis of fuel tanks of a lightweight ship [J]. Eng. Fail. Anal., 2013, 35: 272
|
| [53] |
Wang X J, Ma S J, Fang J J. The corrosion and anticorrosion technology of cargo oil tanks [J]. Shanghai Coat., 2014, 52(4): 35
|
|
王秀娟, 马胜军, 方健君. 油船货油舱腐蚀与防护技术 [J]. 上海涂料, 2014, 52(4): 35
|
| [54] |
Li K, Zhai X F, Guan F, et al. Progress on materials and protection technologies for marine propeller [J]. J. Chin. Soc. Corros. Prot., 2017, 37: 495
|
|
李 科, 翟晓凡, 管 方 等. 船用螺旋桨防护技术及其材料研究进展 [J]. 中国腐蚀与防护学报, 2017, 37: 495
|
| [55] |
Zhu J, Jiang Y J, He D C. Comparison of copper alloy for marine propeller manufacture [J]. Mar. Technol., 2019, (6): 64
|
|
朱 晶, 姜元军, 何大川. 船用螺旋桨常用铜合金材料比较 [J]. 造船技术, 2019, (6): 64
|
| [56] |
Zhu J, Jiang Y J, He D C. Research progress on corrosion and prevention measure of marine propeller [J]. Corros. Sci. Prot. Technol., 2019, 31: 443
|
|
朱 晶, 姜元军, 何大川. 船用螺旋桨典型腐蚀类型与防护措施研究进展 [J]. 腐蚀科学与防护技术, 2019, 31: 443
|
| [57] |
Zhao J. A quick anticorrosive and antifouling solution based on Nano ceramic coating technology for marine propeller [J]. Naval Arch. Ocean Eng., 2021, 37(3): 66
|
|
赵 健. 船用螺旋桨防腐防污纳米陶瓷涂层技术快速解决方案 [J]. 船舶与海洋工程, 2021, 37(3): 66
|
| [58] |
Malzbender J, Steinbrech R W. Fracture resistance of atmospheric plasma sprayed thermal barrier coatings [J]. Surf. Coat. Technol., 2012, 209: 97
|
| [59] |
Kytopoulos V N. A viscoelastic macro-microfracture delay mechanism approach in particulate epoxy composites [J]. J. Reinf. Plast. Comp., 2004, 23: 1325
|
| [60] |
Liu W M, Xu Z Q, Liu H M, et al. Cause analysis and solution of premature fracture of suspension rod in metro gear box [J]. Metals, 2022, 12: 1426
|
| [61] |
Wurster S, Motz C, Pippan R. Characterization of the fracture toughness of micro-sized tungsten single crystal notched specimens [J]. Philos. Mag., 2012, 92: 1803
|
| [62] |
Hu Y T, Dong P F, Jiang L, et al. Corrosion behavior of riveted joints of TC4 Ti-Alloy and 316L stainless steel in simulated marine atmosphere [J]. J. Chin. Soc. Corros. Prot., 2020, 40: 167
|
|
胡玉婷, 董鹏飞, 蒋 立 等. 海洋大气环境下TC4钛合金与316L不锈钢铆接件腐蚀行为研究 [J]. 中国腐蚀与防护学报, 2020, 40: 167
doi: 10.11902/1005.4537.2018.183
|
| [63] |
Alvarães C P, Sandes S S, Jorge J C F, et al. Microstructural characterization of Inconel 625 nickel-based alloy weld cladding obtained by electroslag welding process [J]. J. Mater. Eng. Perform., 2020, 29: 3004
|
| [64] |
Wang Y L, Chen X, Wang J D, et al. Electrochemical behavior of 316L stainless steel in borate buffer solution with different pH [J]. J. Chin. Soc. Corros. Prot., 2017, 37: 162
|
|
王彦亮, 陈 旭, 王际东 等. 316L不锈钢在不同pH值硼酸溶液中的电化学行为研究 [J]. 中国腐蚀与防护学报, 2017, 37: 162
doi: 10.11902/1005.4537.2015.231
|
| [65] |
Artamonov V V, Artamonov V P. Nondestructive examination of metal microstructure in thermal power generating facilities [J]. Russ. J. Nondestruct. Test., 2002, 38: 105
|
| [66] |
Wang H, Wang Y J, Liu E Z. Hot corrosion behavior of new type Co-Al-W superalloys with different Ni contents [J]. J. Chin. Soc. Corros. Prot., 2023, 43: 1419
|
|
王 华, 王英杰, 刘恩泽. Ni含量对Co-Al-W合金热腐蚀行为的影响 [J]. 中国腐蚀与防护学报, 2023, 43: 1419
|
| [67] |
Sun S, Dai J M, Song Y W, et al. Corrosion behavior of extruded EW75 Mg-alloy in Shenyang industrial atmosphere [J]. J. Chin. Soc. Corros. Prot., 2024, 44: 141
|
|
孙 硕, 代珈铭, 宋影伟 等. 挤压态EW75稀土镁合金在沈阳工业大气环境中的腐蚀行为研究 [J]. 中国腐蚀与防护学报, 2024, 44: 141
|
| [68] |
Zhang J, Teng H P, Lu X M. Failure analysis of cracking in press-leading tube welded joint [J]. Gansu Sci. Technol., 2021, 37(21): 16
|
|
张 杰, 滕汉平, 卢雪梅. 引压管焊接接头裂纹失效分析 [J]. 甘肃科技, 2021, 37(21): 16
|
| [69] |
Jin Y F. Analysis of cracking failure cause of rolled steel plate for pressure vessel [J]. Press. Vessel Technol., 2021, 38(9): 66
|
|
金彦枫. 压力容器用钢板卷制开裂失效原因分析 [J]. 压力容器, 2021, 38(9): 66
|
| [70] |
Wang X W, Dong S J, Zhang C L, et al. Analysis of torsion bar failure occurring during the pre-strained manufacturing for heavy off-road tracked vehicles [J]. Eng. Fail. Anal., 2022, 133: 105956
|
| No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|