Effect of Heat Treatment Process on Microstructure and Corrosion Resistance of ZnAlMg Coating |
JIANG Guangrui1,2(), LIU Guanghui1, SHANG Ting1 |
1.Shougang Group Co., Ltd., Technology Research Institute, Beijing 100043, China 2.Beijing Key Laboratory of Green Recyclable Process for Iron & steel Production Technology, Beijing 100043, China |
|
Cite this article:
JIANG Guangrui, LIU Guanghui, SHANG Ting. Effect of Heat Treatment Process on Microstructure and Corrosion Resistance of ZnAlMg Coating. Journal of Chinese Society for Corrosion and protection, 2024, 44(1): 246-254.
|
Abstract ZnAlMg coated steel plates, as the substrate for anti-corrosion and decorative coatings, have to experience thermally baking in automobile manufacturing processes, which may affect the microstructure and corrosion resistance of the coating, but such effect was not studied yet. In this study, the ZnAlMg coated steel plates were heat treated at temperatures in the range of 150oC to 250oC for 10 min respectively so that to reproduce the baking effect. Then the variation of surface- and cross sectional-microstructure, phase constituents and corrosion behavior of the ZnAlMg coating before and after heating were assessed by means of scanning electron microscope (SEM), and X-ray diffractometer (XRD), as well as electrochemical technology and neutral salt spray test. The results show that with the increasing heating temperature, the eutectic structure in the ZnAlMg coating gradually coarsens, and oxides rich in aluminum and magnesium are formed on the surface of the coating. When heating at 175oC, a large number of oxygen is detected on the eutectic structure and surface of the coating. When heating at 250oC, the surface of the initial solidification structure of the coating becomes rough, while the gray phase in the eutectic structure gradually evolves from lamellar structure to granular structure, and a large number of oxidation products of Al, Mg and Zn appear on the surface, among which the oxides of Mg and Al are the main ones. The electrochemical test results show that with the increasing heating temperature, the polarization resistance and charge transfer resistance of the ZnAlMg coating increase but the corrosion current density decreases continuously. The results of neutral salt spray test show that the corrosion mass loss of the ZnAlMg coating decreases gradually with the increasing heating temperature. Compared with the as received ones, the corrosion mass loss of the ZnAlMg coating heat treated at 250oC decreased by 17%. It was indicated that the improvement of corrosion resistance of the ZnAlMg coating may be related to the coarsening of eutectic structure and the formation of oxides rich in Al and Mg on the surface.
|
Received: 20 March 2023
32134.14.1005.4537.2023.073
|
|
Corresponding Authors:
JIANG Guangrui, E-mail: guangrui82@qq.com
|
1 |
Komatsu A, Izutani H, Tsujimura T, et al. Corrosion resistance and protection mechanism of hot-dip Zn-Al-Mg alloy coated steel sheet under accelerated corrosion environment [J]. Tetsu-to-Hagane, 2000, 86: 534
|
|
小松厚志, 泉谷秀房, 辻村太佳夫 等. 溶融Zn-Al-Mg系合金めっき鋼板の促進腐食環境下における耐食性と防食機構 [J]. 鉄と鋼, 2000, 86: 534
|
2 |
Nishimura K, Shindo H, Okada T, et al. Development and properties of Zn-Mg galvanized steel sheet “DYMAZINC” [J]. Mat. Japan, 2001, 40: 292
|
|
西村一実, 新頭英俊, 岡田哲也 等. 高耐食性Zn-Mg合金めっき鋼板「ダイマジンク」の開発と製品特性 [J]. まてりあ, 2001, 40: 292
|
3 |
Morimoto Y, Honda K, Nishimura K, et al. Excellent corrosion-resistant Zn-Al-Mg-Si alloy hot-dip galvanized steel sheet “SUPER DYMA” [J]. Nippon Steel Tech. Rep., 2003, (87): 24
|
4 |
Sohn I R, Kim T C, Ju G I, et al. Anti-corrosion performance and applications of PosMAC® steel [J]. Corros. Sci. Technol., 2021, 20: 7
|
5 |
Schouller-Guineta P, Allelyb C, Volovitchc P. Zn-Al-Mg: An innovative metallic coating that offers protection in the harshest environments [A]. Proceedings of the 8th International Conference on Zinc and Zinc Alloy Coated Steel Sheet [C]. Milano: the Associazione Italiana Di Metallurgia, 2011
|
6 |
Jiang G R, Zheng X B, Zhao X F, et al. Application of the hot-dip galvanized Zn-Al-Mg alloyed coating steel sheet on automobile body [J]. Automob. Technol. Mater., 2021, (4): 12
|
|
蒋光锐, 郑学斌, 赵晓非 等. 汽车车身用热浸镀锌铝镁镀层钢板 [J]. 汽车工艺与材料, 2021, (4): 12
|
7 |
Xie Y X, Jin X Y, Wang L. Development and application of hot-dip galvanized zinc-aluminum-magnesium coating [J]. J. Iron Steel Res., 2017, 29: 167
|
|
谢英秀, 金鑫焱, 王 利. 热浸镀锌铝镁镀层开发及应用进展 [J]. 钢铁研究学报, 2017, 29: 167
|
8 |
Jiang G R, Wang H Q, Li M, et al. Corrosion properties of steel sheet with zinc-base alloyed coatings [J]. J. Chin. Soc. Corros. Prot., 2017, 37: 354
|
|
蒋光锐, 王海全, 黎 敏 等. 锌基合金镀层钢板的耐蚀性研究 [J]. 中国腐蚀与防护学报, 2017, 37: 354
doi: 10.11902/1005.4537.2016.101
|
9 |
Volovitch P, Vu T N, Allély C, et al. Understanding corrosion via corrosion product characterization: II. Role of alloying elements in improving the corrosion resistance of Zn-Al-Mg coatings on steel [J]. Corros. Sci., 2011, 53: 2437
doi: 10.1016/j.corsci.2011.03.016
|
10 |
LeBozec N, Thierry D, Rohwerder M, et al. Advanced Zinc-Based Hot Dip Coatings for the Automotive Application (AUTOCOAT) [M]. LU: Publications Office, 2013
|
11 |
Schul J, Schüßler A, Parma G, et al. New potentials for Zn-Mg-Al hot-dip galvanized coatings in automotive applications [A]. Proceedings of the 11th International Conference on Zinc and Zinc Alloy Coated Steel Sheet [C]. Tokyo: The Iron and Steel Institute of Japan, 2017: 733
|
12 |
Gu H. Study of coatings compatibility with zinc-magnesium steel [J]. Paint Coat. Ind., 2019, 49(4): 65
|
|
顾 宏. 锌镁涂层新型热镀锌钢板与涂料的匹配研究 [J]. 涂料工业, 2019, 49(4): 65
|
13 |
Chen L, Xing Y, Yu Y, et al. Corrosion behaviors of different steel sheets in salt spray tests [J]. Electroplat. Finish., 2020, 39: 1528
|
|
陈 磊, 邢 阳, 俞 雁 等. 不同钢板在盐雾试验中的腐蚀行为 [J]. 电镀与涂饰, 2020, 39: 1528
|
14 |
Schinkinger B, Zügner S. Zinc magnesium 70 - Implementation of a new metallic coating within the BMW group [A]. Proceedings of the 4th International Conference on Steels in Cars and Trucks [C]. Braunschweig: Steel Institute VDEh, 2014: 524
|
15 |
Sigvant M, Pilthammar J, Hol J, et al. Friction in sheet metal forming simulations: Modelling of new sheet metal coatings and lubricants [J]. IOP Conf. Ser.: Mater. Sci. Eng., 2018, 418: 012093
|
16 |
Tian F. Stamping analysis based on Zn-Al-Mg and Zn-Fe coatings [J]. Forg. Metalform., 2020, (16): 38
|
|
田 飞. 基于锌铝镁和锌铁镀层的冲压成形分析 [J]. 锻造与冲压, 2020, (16): 38
|
17 |
Hu Y Z, Zhang Y, Li Z H. Application research on body outer cover panel with zinc-magnesium coated steel sheet [J]. Die Mould Ind., 2020, 46(4): 64
|
|
胡彦昭, 张 宇, 李振华. 锌镁涂层钢板车身外覆盖件的应用研究 [J]. 模具工业, 2020, 46(4): 64
|
18 |
Yang Z, Ma F X, Sun H, et al. Evaluation on anticorrosion and paintability of Zn-Al-Mg alloy coated steel sheet [J]. Electroplat. Finish., 2021, 40: 1393
|
|
杨 忠, 马风雪, 孙 浩 等. 锌铝镁钢板的防腐及涂装性评价 [J]. 电镀与涂饰, 2021, 40: 1393
|
19 |
Zeng F B, Qin Y R, Tian C W, et al. Performance test analysis of Zn-Al-Mg automobile sheet material [A]. SAECCE2021 [C]. Shanghai: China Machine Press, 2021: 2539
|
|
曾凡波, 秦永瑞, 田成伟 等. Zn-Al-Mg汽车板材料的性能试验分析 [A]. 2021中国汽车工程学会年会论文集 [C]. 上海: 机械工业出版社, 2021: 2539
|
20 |
Pan J M. 1000 Questions about Painting Technology [M]. Beijing: Machinery Industry Press, 2013: 315
|
|
潘继民. 涂装技术1000问 [M]. 北京: 机械工业出版社, 2013: 315
|
21 |
De Bruycker E, Zermout Z, De Cooman B C. Zn-Al-Mg coatings: Thermodynamic analysis and microstructure related properties [J]. Mater. Sci. Forum, 2007, 539-543: 1276
doi: 10.4028/www.scientific.net/MSF.539-543
|
22 |
Nogueira T M C, Cruz M A S, Rios P R. Influence of an annealing heat treatment on the microstructure, ductility, and corrosion resistance of a chromated 55wt.% Al-Zn coated steel sheet [J]. J. Mater. Eng. Perform., 2001, 10: 314
doi: 10.1361/105994901770345024
|
23 |
Wang Y F, Ma D G, Li J Y, et al. Effect of heating system on structure and corrosion resistance of zinc-aluminium-magnesium coating [J]. Hebei Metall., 2021, (8): 28
|
|
王言峰, 马德刚, 李建英 等. 加热制度对锌铝镁镀层结构及耐蚀性的影响 [J]. 河北冶金, 2021, (8): 28
|
24 |
Ghatei-Kalashami A, Khan M S, Lee M Y, et al. High-temperature phase evolution of the ZnAlMg coating and its effect on mitigating liquid-metal-embrittlement cracking [J]. Acta Mater., 2022, 229: 117836
doi: 10.1016/j.actamat.2022.117836
|
25 |
Riener C K, Raab A E, Luckeneder G, et al. Zinc-magnesium-aluminium (ZM)-HDG-coated steel sheet for structural parts to outer panels [R]. Detroit: SAE International, 2017
|
26 |
Meng Y, Jiang G R, Ju X H, et al. TEM study on the microstructure of the Zn-Al-Mg alloy [J]. Mater. Charact., 2017, 129: 336
doi: 10.1016/j.matchar.2017.05.011
|
27 |
Gaskell D R, Laughlin D E. Introduction to the Thermodynamics of Materials [M]. 6th ed. Boca Raton: CRC Press, 2018: 467
|
28 |
Gesmundo F, Gleeson B. Oxidation of multicomponent two-phase alloys [J]. Oxid. Met., 1995, 44: 211
doi: 10.1007/BF01046728
|
29 |
Gesmundo F, Viani F, Niu Y. The internal oxidation of two-phase binary alloys under low oxidant pressures [J]. Oxid. Met., 1996, 45: 51
doi: 10.1007/BF01046820
|
30 |
Chang J K, Lin C S. Microstructural evolution of 11Al-3Mg-Zn ternary alloy-coated steels during austenitization heat treatment [J]. Metall. Mater. Trans., 2017, 48A: 3734
|
31 |
Ahmadi M, Salgın B, Kooi B J, et al. The effect of grain refinement on the deformation and cracking resistance in Zn-Al-Mg coatings [J]. Mater. Sci. Eng., 2022, 840A: 142995
|
32 |
Paladino A E, Coble R L. Effect of grain boundaries on diffusion-controlled processes in aluminum oxide [J]. J. Am. Ceram. Soc., 1963, 46: 133
doi: 10.1111/jace.1963.46.issue-3
|
33 |
Svensson H, Knutsson P, Stiller K. Formation and healing of voids at the metal-oxide interface in NiAl alloys [J]. Oxid. Met., 2009, 71: 143
doi: 10.1007/s11085-008-9132-z
|
34 |
Wood G C, Stott F H. Oxidation of alloys [J]. Mater. Sci. Technol., 1987, 3: 519
doi: 10.1080/02670836.1987.11782263
|
35 |
LeBozec N, Thierry D, Persson D, et al. Influence of microstructure of zinc-aluminium-magnesium alloy coated steel on the corrosion behavior in outdoor marine atmosphere [J]. Surf. Coat. Technol., 2019, 374: 897
doi: 10.1016/j.surfcoat.2019.06.052
|
36 |
Prosek T, Persson D, Stoulil J, et al. Composition of corrosion products formed on Zn-Mg, Zn-Al and Zn-Al-Mg coatings in model atmospheric conditions [J]. Corros. Sci., 2014, 86: 231
doi: 10.1016/j.corsci.2014.05.016
|
37 |
El-Sayed A R, Mohran H S, Abd El-Lateef H M. Corrosion study of zinc, nickel, and zinc-nickel alloys in alkaline solutions by tafel plot and impedance techniques [J]. Metall. Mater. Trans., 2012, 43A: 619
|
No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|