7020铝合金列车车钩梁开裂原因与机理

中国腐蚀与防护学报

2008, Vol. 28

Issue (4): 240-245

研究报告

本期目录 | 过刊浏览

7020铝合金列车车钩梁开裂原因与机理

王荣;鄢国强;李光福;陈冰川

上海材料研究所检测中心

Failure analysis and the mechanism of 7020 aluminum alloy train coupler girder

上海材料研究所检测中心

全文: PDF(1448 KB)

摘要: 用直读光谱仪、万能材料试验机、光学显微镜、扫描电子显微镜等分析手段，分析高速列车7020铝合金车钩梁多处开裂现象及其原因。结果表明，开裂的7020铝合金车钩梁材料质量正常，服役后的车钩梁基体表面存在腐蚀坑，腐蚀坑中存在Cl-离子，主裂纹位于焊接热影响区和母材交界处，裂纹沿晶扩展。实验室采用和车钩梁相似的环境和受力状况进行模拟试验，高强度合金双悬臂梁试样的应力腐蚀开裂（SCC）裂纹形貌特征和车钩梁裂纹吻合良好，表明车钩梁开裂原因为SCC，并讨论了铝合金的SCC机理。

关键词 ： 7020铝合金, 车钩梁, 焊接

Abstract：By means of optical emission spectrometer, universal material testing machine, optical microscope, scanning electronic microscope and finite element calculation were used to analyze the multi-cracking reason of 7020 aluminum alloy train coupler girder, and study results indicated that stress corrosion cracking (SCC) caused by wet and sweltering hot weather .According to finite element calculation results it could be known there was no stress at the “Z” direction, and welding residual tension stress is the main cracking reason. Modeling test results of DCB samples showed that the cracking mode of train coupler girder and DCB sample is same. Cracking mechanism of 7020 aluminum alloy was researched and discussed.

Key words：

收稿日期: 2008-02-19

ZTFLH:

TG146.32

通讯作者: 王荣 E-mail: hgf_1966@yahoo.com.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	王荣
	鄢国强
	李光福
	陈冰川
44.8K

引用本文:

王荣; 鄢国强; 李光福; 陈冰川 . 7020铝合金列车车钩梁开裂原因与机理[J]. 中国腐蚀与防护学报, 2008, 28(4): 240-245 .

链接本文:

https://www.jcscp.org/CN/Y2008/V28/I4/240

[1]Yao S P,Xu P.High speed maglev transportation made in China[J].J.Traffic Transp.Eng.,2004,4(2):40-44(姚曙光,许平.高速磁浮列车车体国产化[J].交通运输工程学报,2004,4(2):40-44)
[2]Gür C H,Yld Z I.Nondestructive investigation on the effect of pre-cipitation hardening on impact toughness of 7020 Al-Zn-Mg alloy[J].Mater.Sci.Eng.,2004,A382:95-400
[3]Song R G,Dietzel W.Stress corrosion cracking and hydrogen em-brittlement of an Al-Zn-Mg-(Cu)alloy[J].Acta Mater.,2004,52(16):4727-4743
[4]Liu J,Kulak M.A new parading in the design of aluminum alloy for aerospace applications[J].Mater.Sci.Forum,2000,331-337:127-140
[5]Heinz A,Haszler A,Keidel C.Recent development in aluminium alloy for aerospace applications[J].Mater.Sci.Eng.,2000,A280(1):102-107
[6]Zhang X Y,Sun Z H,Liu M H,et al.Effect of environment onstress corrosion cracking of high strength Al alloy[J].J.Chin.Soc,Corros.Prot.,2007,27(6):354-362(张小云,孙志华,刘明辉等.环境对高强度铝合金应力腐蚀行为的影响[J].中国腐蚀与防护学报,2007,27(6):354-362)
[7]Sun Z H,Liu M H,Zhang X Y,et al.Effect of aging parameterson stress corrosion cracking susceptibility of Al-Zn-Mg-Cu alloy[J].J.Chin.Soc.Corros.Prot.,2006,26(4):232(孙志华,刘明辉,张晓云等.时效制度对Al-Zn-Mg-Cu铝合金应力腐蚀敏感性的影响[J].中国腐蚀与防护学报,2006,26(4):232)
[8]Burleigh T D.Mechanism of stress corrosion cracking for aluminumalloy(2)1980～1989 document summary[J].Corrosion,1991,47(2):89-98
[9]Liu J H,Li D,Zhang P F.Effect of hydrogen on stress corrosion cracking of LC4 high strength Al alloy[J].J.Chin.Sic.Corros.Prot.,2002,22(5):308-310(刘继华,李荻,张佩芬.氢对LC4高强铝合金应力腐蚀断裂的影响[J].中国腐蚀与防护学报,2002,22(5):308-310)
[10]Parkins R N,Translated by Yang W.Stress Corrosion Cracking,in Uhlig′s Corrosion Handbook(Second Edition)[M].Beijing:Chemical Industry Press,2005:525
[11]Chu W Y,Qiao L J,Chen Q Z,et al.Fracture and Environment Fracture[M].Beijing:Science Press,2001:120(褚武扬,乔利杰,陈奇志等.断裂与环境断裂[M].北京:科学出版社,2001:120)
[12]Hollingsworth E H,Hunsticker H Y.Corrosion of aluminum and aluminum alloys[J].Corrosion,1987,43(9):583-609
[13]Liu Y.Progress ofresearch on stress corrosion crackingofaluminum alloys[J].J.Beijing Union Univ.(Nat.Sci.),2006,20(1):34(刘洋.铝合金应力腐蚀研究进展[J].北京联合大学学报(自然科学版),2006,20(1):34)

[1]	伊红伟, 胡慧慧, 陈长风, 贾小兰, 胡丽华. CO₂环境下油酸咪唑啉对X65钢异种金属焊缝电偶腐蚀的抑制作用研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 96-104.
[2]	白苗苗, 白子恒, 蒋立, 张东玖, 姚琼, 魏丹, 董超芳, 肖葵. H62黄铜/TC4钛合金焊接件腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 159-166.
[3]	黄宸,黄峰,张宇,刘海霞,刘静. 高强耐候钢焊接接头电偶腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 527-535.
[4]	孙晓光,韩晓辉,张星爽,张志毅,李刚卿,董超芳. 超低碳奥氏体不锈钢焊接接头耐腐蚀性及环保型化学钝化工艺研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 345-352.
[5]	李兆登,崔振东,侯相钰,高丽丽,王维珍,尹建华. 核级316LN不锈钢焊接接头在高温高压水中的腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 106-113.
[6]	王希靖, 王博士, 杨超, 杨艳, 沈斌. 纯Ni母材及焊缝在熔融Na₂SO₄-K₂SO₄中热腐蚀研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 495-501.
[7]	王凯, 易耀勇, 卢清华, 易江龙, 江泽新, 马金军, 张宇. 基于窄间隙焊接的热模拟峰值温度对Q690高强钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(5): 447-454.
[8]	孔祥峰, 张婧, 姜源庆, 褚东志, 李春虎, 高楠, 吕婧, 邹妍. 基于失重法的水下焊接接头腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(3): 226-232.
[9]	郭强, 陈长风, 李世瀚, 于浩波, 李鹤林. 冷焊修复层在H₂S环境下的开裂行为研究[J]. 中国腐蚀与防护学报, 2018, 38(2): 167-173.
[10]	王军, 冯超, 彭碧草, 谢亿, 张明华, 吴堂清. S450EW焊接接头在NaHSO₃溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 575-582.
[11]	戴芸,刘胜胆,邓运来,张新明. 7020铝合金在3.5%NaCl溶液中的点蚀行为[J]. 中国腐蚀与防护学报, 2017, 37(3): 279-286.
[12]	白强,邹妍,孔祥峰,高杨,刘岩,董胜. 奥氏体焊条水下湿法焊接CCSE40钢在海水中的腐蚀电化学行为研究[J]. 中国腐蚀与防护学报, 2016, 36(5): 427-432.
[13]	朱若林,张志明,王俭秋,韩恩厚. 核电异种金属焊接接头的应力腐蚀裂纹扩展行为研究进展[J]. 中国腐蚀与防护学报, 2015, 35(3): 189-198.
[14]	刘智勇, 万红霞, 李禅, 杜翠薇, 李晓刚, 刘翔. X65钢焊接接头在模拟浅表海水和深海环境中的腐蚀行为对比[J]. 中国腐蚀与防护学报, 2014, 34(4): 321-326.
[15]	邢云颖, 刘智勇, 杜翠薇, 李晓刚, 刘然克, 朱敏. H₂S浓度和pH值对X65海管钢焊接接头腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2014, 34(3): 231-236.

Viewed

Full text

Abstract

Cited

Shared

Discussed