蒸汽发生器的腐蚀失效分析

程芳婷

江苏联合职业技术学院连云港中医药分院江苏省连云港中医药高等职业技术学校

Corrosion of Steam Generators In TIANWAN Nuclear Power Plant

江苏联合职业技术学院连云港中医药分院江苏省连云港中医药高等职业技术学校

全文: PDF(292 KB)

摘要: 田湾核电站蒸汽发生器在冷态和热态调试结束后发生的穿晶型应力腐蚀裂纹及点蚀，其腐蚀原因可能为运输及安装期间保养措施不当。提出对蒸汽发生器进行干保护、由设计的KOH-N2H4碱性水冲洗方案调整为NH3-N2H4碱性水、降低水中溶解氧和Cl-含量、提高溶液pH、对设备进行定期清洗、化水系统加装反渗透装置等方案，以保证蒸汽发生器的稳定运行。

关键词 ：蒸汽发生器, 应力腐蚀, 点腐蚀

Abstract：Stress corrosion cracking and pit corrosion of steam generators In Tianwan Nuclear Power Plant is described,The cause of corosion is preservation method which is not correct during transportation and installation, measurement and suggestions for safe operation of steam generator is proposed. Steam generators should be protected dryly during outage, it is necessary to adjust scour project by using KOH-N2H4 alkali liquor instead of NH3-N2H4 alkali liquor,to reduce the content of deliquescent -oxygen and Cl- in water, to increase the pH value of the liquor, to purge of equipment regularly and to install reverse infiltration equipment in chemistry water treatment system.

Key words： Steam Generators Stress corrosion cracking Pit corrosion

收稿日期: 2006-03-02

ZTFLH:

TG172.9

通讯作者: 程芳婷 E-mail: shuxinkuan@163.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	程芳婷
44.8K

引用本文:

程芳婷 . 蒸汽发生器的腐蚀失效分析[J]. 中国腐蚀与防护学报, 2006, 26(6): 376-379 .

链接本文:

https://www.jcscp.org/CN/Y2006/V26/I6/376

[1]Wang R G,Wei Y,Zhang Q L,et al.Study on SCC behavior ofaustenitic stainless steelsin H2Ssaturated aqueous solutions contain-ing Cl-[J].J.Chin.Soc.Corros.Prot.,2000,20(1):47-53(王荣光,魏云,张清廉等.奥氏体不锈钢SUS316及SUS316L在含Cl-的饱和H2S水溶液中的应力腐蚀行为研究[J].中国腐蚀与防护学报,2000,20(1):47-53)
[2]Edeleanu C.Tansgranular stress corrosion in chromium-nickelstainless steels[J].J.Iron Steel Inst.,1953,173:140
[3]Hines J C,Hear T P.Stress corrosion of austenitic stainless steelsinsteamand hot water systems[J].J.Iron Steel Inst.,1956,186:406
[4]Staehle R W,Beck F H,Fontana M G.Mechanismof stress corro-sion of austenitic stainless steels in chloride waters[J].Corrosion,1959,15:373
[5]Liu J J,Yong X Y,Lin Y Z,et al.Cavitation erosion behaviors andmechanismof 1Cr18Ni9Ti stainless steel in chloride solution[J].J.Chin.Soc.Corros.Prot.,2005,25(3):157-162(刘景军,雍兴跃,林玉珍等.不锈钢在氯化物介质中的空泡腐蚀行为及机理[J].中国腐蚀与防护学报,2005,25(3):157-162)
[6]Yan MC,Weng YJ.Effects of environmental solutions on electro-chemical behaviors related to SCC of pipe line steels[J].J.Chin.Soc.Corros.Prot.,2005,25(1):34-38(闫茂成,翁永基.环境溶液对管道钢应力腐蚀过程电化学行为的影响[J].中国腐蚀与防护学报,2005,25(1):34-38)
[7]Wang HT,Zhao J M,Zuo Y,et al.The effects of some anions onmetastable pitting of 316L stainless steel[J].J.Chin.Soc.Corros.Prot.,2002,22(4):202-206(王海涛,赵景茂,左禹等.几种阴离子对316L不锈钢亚稳态孔蚀行为的影响[J].中国腐蚀与防护学报,2002,22(4):202-206)
[8]Li P Y,Qian D Z,Wang MJ.Treatment of Boiler Water[M].Hubei:Hubei Scientific Technology Press,1999(李培元,钱达中,王蒙聚.锅炉水处理[M].湖北:湖北科学技术出版社,1999)
[9]Wang X Q.Corrosion and Protection of Caloric Equipment[M].Beijing:Irrigation Works and Electric Power Press,1993(王杏卿.热力设备的腐蚀及防护[M].北京:水利电力出版社,1993)
[10]Luo S Z,Zheng Y G,Yao Z M,et al.Cavitation corrosion behaviorof 1Cr18 Mn14Nstainless steel in HCl solution[J].J.Chin.Soc.Corros.Prot.,2004,24(6):350-355(骆素珍,郑玉贵,姚治铭等.1Cr18 Mn14N不锈钢在HCl溶液中的空蚀行为[J].中国腐蚀与防护学报,2004,24(6):350-355),

[1]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[2]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[3]	艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.
[4]	李清, 张德平, 李晓荣, 王薇, 孙宝壮, 艾池. TP110TS和P110钢在CO₂注入井环空环境中应力腐蚀行为比较[J]. 中国腐蚀与防护学报, 2020, 40(4): 302-308.
[5]	李清, 张德平, 王薇, 吴伟, 卢琳, 艾池. L80油管钢实际腐蚀状况评估及室内电化学和应力腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 317-324.
[6]	朱丽霞, 贾海东, 罗金恒, 李丽锋, 金剑, 武刚, 胥聪敏. 外加电位对X80管线钢在轮南土壤模拟溶液中应力腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 325-331.
[7]	张震, 吴欣强, 谭季波. 电化学噪声原位监测应力腐蚀开裂的研究现状与进展[J]. 中国腐蚀与防护学报, 2020, 40(3): 223-229.
[8]	刘志峰,朱志平,石纯,黄赵鑫. 载流法制备硫酸露点腐蚀模拟气体的试验研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 1-9.
[9]	陈旭,马炯,李鑫,吴明,宋博. 温度与SRB协同作用下X70钢在海泥模拟溶液中应力腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 477-483.
[10]	王保杰,栾吉瑜,王士栋,许道奎. 镁合金应力腐蚀开裂行为研究进展[J]. 中国腐蚀与防护学报, 2019, 39(2): 89-95.
[11]	张克乾,胡石林,唐占梅,张平柱. 冷加工核电结构材料在高温高压水中应力腐蚀裂纹扩展行为的研究进展[J]. 中国腐蚀与防护学报, 2018, 38(6): 517-522.
[12]	朱若林, 张利涛, 王俭秋, 张志明, 韩恩厚. 核级316LN不锈钢弯管在高温高压水中的应力腐蚀裂纹扩展行为[J]. 中国腐蚀与防护学报, 2018, 38(1): 54-61.
[13]	偶国富, 赵露露, 王凯, 王宽心, 金浩哲. 10^#碳钢在HCl-H₂O环境中的露点腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(1): 33-38.
[14]	周霄骋, 崔巧棋, 贾静焕, 刘智勇, 杜翠薇. Cl^-浓度对316L不锈钢在碱性NaCl/Na₂S溶液中SCC行为的影响[J]. 中国腐蚀与防护学报, 2017, 37(6): 526-532.
[15]	张乃强,岳国强,吕法彬,曹琦,李梦源,徐鸿. Inconel625合金在高温水蒸气环境中应力腐蚀开裂裂纹扩展速率研究[J]. 中国腐蚀与防护学报, 2017, 37(1): 9-15.

Viewed

Full text

Abstract

Cited

Shared

Discussed