K4104合金渗Al-Si涂层抗高温氧化性能研究

杨世伟;刘海涛;朱玲斌;娄瑾

哈尔滨工程大学

Study on high temperature oxidation resistance of Al-Si coating on K4104 Superalloy

;Haitao Liu;;

哈尔滨工程大学

全文: PDF(394 KB)

摘要: 采用无机盐料浆法，在K4104镍基高温合金表面制备Al－Si涂层。通过改变粘结剂中CrO3的含量得到两种不同成分的Al－Si涂层。依据HB5258－2000标准，对制备了Al－Si涂层的K4104镍基高温合金进行了高温氧化性能试验。绘制了氧化动力学曲线, 用带能谱分析的扫描电镜观察了涂层的表面氧化形貌和截面组织形貌。结果表明，K4104镍基高温合金表面的Al－Si涂层在高温氧化过程中已转变成完整致密的α－Al2O3氧化层和β－NiAl相化合物层，且与基体合金的粘附性良好，说明Al－Si涂层具有优良的抗高温氧化性能。

关键词 ： K4104镍基高温合金, Al－Si涂层, 高温氧化

Abstract：The Al－Si coating on the surface of K4104 superalloy were prepared by using slurry process. Two different coating were formed by changing the CrO3 content of agglomerant. According to HB5258－2000, the high temperature performance of these coating have been investigated by high temperature oxidation test.The oxidation kinetics curve was drawn. The surface morphology of the Al－Si coating were studied by using SEM. The results indicate that the Al－Si coating on the surface of K4104 superalloy have transformed to compact oxidized film α－Al2O3 and β－NiAl compound scale in the process of high temperature oxidation and all of them have good adhesivity. The Al－Si coatings have excellent high temperature oxidation resistance.

Key words： K4104 superalloy Al－Si coating high temperature oxidation

收稿日期: 2005-06-27

ZTFLH:

TG172.8

通讯作者: 刘海涛

Corresponding author: Haitao Liu

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	杨世伟
	刘海涛
	朱玲斌
	娄瑾
44.8K

引用本文:

杨世伟; 刘海涛; 朱玲斌; 娄瑾 . K4104合金渗Al-Si涂层抗高温氧化性能研究[J]. 中国腐蚀与防护学报, 2006, 26(6): 371-375 .
Haitao Liu. Study on high temperature oxidation resistance of Al-Si coating on K4104 Superalloy. J Chin Soc Corr Pro, 2006, 26(6): 371-375 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2006/V26/I6/371

[1]Lou H Y.Interdiffusion between high temperature coating and su-peralloy substrate[J].J.Chin.Soc.Corros.Prot.,1997,17(suppl.):464-469(楼翰一.高温合金涂层与基体界面上的互扩散[J].中国腐蚀与防护学报,1997,17(增刊):464-469)
[2]Liu P S.Status of study on high-temperature oxidation law for alu-minide coatings[J].Rare Metal Materials and Engineering,2003,32(9):681-685(刘培生.铝化物高温防护涂层的现状[J].稀有金属材料与工程,2003,32(9):681-685)
[3]Doychak J,Smialek J L,Mitchell T E.Transient oxidation of single-crystalβ-NiAl[J].Metall.Trans.A,1989,20A:499-518
[4]Schumann E.Effect of Y-ion implantation on the oxidation ofβ-NiAl[J].Oxidation of Metals,1995,43:157-172
[5]Yang Z L.High temperature performance of the Al-Si coating[J].J.Chin.Soc.Corros.Prot.,1981,1(4):28-37(杨忠林.铝-硅涂层防护性能的研究[J].中国腐蚀与防护学报,1981,1(4):28-37)
[6]Yang S W.Study on high temperature oxidation of Al-Si coating onsuperalloy[J].Trans.Mater.Heat Treatment,2004,25(1):66-68(杨世伟.高温合金Al-Si涂层抗高温氧化性能的研究[J].材料热处理学报,2004,25(1):66-68)
[7]Zhu R Z,He Y D,Qi H B.The High Temperature Corrosion andMaterials of High Temperature Corrosion Resistance[M].Shanghai:Shanghai Science&Technology Press,1993:344-348(朱日彰,何业东,齐慧滨.高温腐蚀及耐高温腐蚀材料[M].上海:上海科学技术出版社,1993:344-348)
[8]Yang Z L,Yu X F.Effect of Si distribution on hot corrosion behaviorof Al-Si coating[J].J.Aeronautical Materials,1994,14(2):38-40(杨忠林,余霞飞.硅的分布对铝-硅涂层抗热腐蚀性能的研究[J].航空材料学报,1994,14(2):38-40)

[1]	郑艳欣, 刘颖, 宋青松, 郑峰, 贾玉川, 韩培德. 含铁铜基陶瓷复合材料高温氧化行为与耐磨性研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 191-198.
[2]	徐勋虎,何翠群,向军淮,王玲,张洪华,郑晓冬. Co-20Re-25Cr-1Si合金在0.1 MPa纯O₂中的高温氧化行为[J]. 中国腐蚀与防护学报, 2020, 40(1): 75-80.
[3]	夏俊捷,牛红志,刘敏,曹华珍,郑国渠,伍廉奎. 基于卤素效应的阳极氧化技术提高Ti48Al5Nb合金抗高温氧化性能[J]. 中国腐蚀与防护学报, 2019, 39(2): 96-105.
[4]	谢冬柏,周游宇,鲁金涛,王文,朱圣龙,王福会. Al/Si对镍基合金在超临界水中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(1): 68-76.
[5]	王玲,向军淮,张洪华,覃宋林. 3种不同Cr含量Co-20Re-Cr合金在1000和1100 ℃的高温氧化行为[J]. 中国腐蚀与防护学报, 2019, 39(1): 83-88.
[6]	谢冬柏, 周游宇, 鲁金涛, 王文, 朱圣龙, 王福会. Cr对镍基合金在超临界水中氧化行为的影响研究[J]. 中国腐蚀与防护学报, 2018, 38(4): 358-364.
[7]	李越, 王剑, 张勇, 白晋钢, 胡亚迪, 乔永锋, 张彩丽, 韩培德. 2205双相不锈钢密闭容器中高温初始氧化过程分析[J]. 中国腐蚀与防护学报, 2018, 38(3): 296-302.
[8]	孙超, 杨潇, 文玉华. 表面溅射高含铝奥氏体不锈钢合金涂层对316不锈钢抗高温氧化性能的影响[J]. 中国腐蚀与防护学报, 2017, 37(6): 590-596.
[9]	赵展,李景阳,董建新,姚志浩,张麦仓. 925镍铁基耐蚀合金均匀化及高温氧化行为[J]. 中国腐蚀与防护学报, 2017, 37(1): 1-8.
[10]	王喜忠,吴建颢,彭徽,郭洪波,宫声凯. 电子束物理气相沉积La₂Ce₂O₇热障涂层的高温燃气热腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(1): 36-40.
[11]	谢冬柏,单国. 燃油火场环境中助燃剂的快速检验方法研究[J]. 中国腐蚀与防护学报, 2017, 37(1): 74-80.
[12]	杨甜甜,徐敬军,钱余海,李美栓. 石墨基体上ZrC/MoSi₂微叠层涂层的制备及抗超高温氧化性能[J]. 中国腐蚀与防护学报, 2016, 36(5): 476-482.
[13]	黄嘉鹏,杨斌,汪航. 稀土 (Y,La,Ce) 复合添加对Ni-10Cr-5Al合金在1000 ℃下高温氧化行为的影响[J]. 中国腐蚀与防护学报, 2016, 36(5): 489-496.
[14]	袁军涛, 王文, 朱圣龙, 王福会. Super 304H钢在700~900 ℃纯水蒸汽中的氧化行为[J]. 中国腐蚀与防护学报, 2014, 34(3): 218-224.
[15]	袁军涛, 吴细毛, 王文, 朱圣龙, 王福会. 晶粒尺寸对耐热钢在高温水蒸汽中的氧化行为的影响[J]. 中国腐蚀与防护学报, 2013, 33(4): 257-264.

Viewed

Full text

Abstract

Cited

Shared

Discussed