含钪Al-Mg合金的抗应力腐蚀和剥落腐蚀性能研究

中国腐蚀与防护学报

2005, Vol. 25

Issue (4): 218-221

研究报告

本期目录 | 过刊浏览

含钪Al-Mg合金的抗应力腐蚀和剥落腐蚀性能研究

王月;王政红;付自来;张海峰

STRESS CORROSION CRACKING AND EXFOLIATION CORROSION RESISTANCE OF Al-Mg ALLOY WITH ADDITION OF SCANDIUM

Yue Wang;Zhenghong Wang;Zilai Wu;Haifeng Zhang

全文: PDF(233 KB)

摘要: 采用GJB1742-1993中有关铝镁系合金的应力腐蚀和剥落腐蚀试验方法，研究了高镁Al-Mg合金中添加微量元素Sc后的抗应力腐蚀和剥落腐蚀性能，利用金相显微镜和透射电子显微镜观察了合金的显微组织.结果表明，该合金具有良好的抗应力腐蚀和剥落腐蚀性能，合金变形组织中均匀弥散分布着β（Mg5Al8、Mg2Al3）沉淀相，在晶界上未出现连续β相形成的网络，因此合金耐腐蚀性能优良.

关键词 ：钪, 铝合金, 应力腐蚀, 剥落腐蚀

Abstract：The stress corrosion cracking and exfoliation corrosion resistance of Al-Mg alloy with high level of Mg and trace Sc addition were studied by means of such methods as stress corrosion cracking and exfoliation corrosion test of Al-Mg alloys in GJB1742-1993.Their microstructures were observed by using optical microscope and transmission electron microscope (TEM).The results showed that Al-Mg alloy with trace Sc addition has good stress corrosion cracking and exfoliation corrosion resistance,and a homogeneous,dispersed distribution of β-phase (Mg5Al8,Mg2Al3) in microstructures.The discontinuous precipitation of β-phase in grain boundaries therefore highly improved corrosion resistance of the alloy.

Key words： scandium aluminum alloy stress corrosion cracking exfoliation corrosion

收稿日期: 2004-03-26

ZTFLH:

TG146.2

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	王月
	王政红
	付自来
	张海峰
44.8K

引用本文:

王月; 王政红; 付自来; 张海峰 . 含钪Al-Mg合金的抗应力腐蚀和剥落腐蚀性能研究[J]. 中国腐蚀与防护学报, 2005, 25(4): 218-221 .
Yue Wang, Zhenghong Wang, Zilai Wu, Haifeng Zhang. STRESS CORROSION CRACKING AND EXFOLIATION CORROSION RESISTANCE OF Al-Mg ALLOY WITH ADDITION OF SCANDIUM. J Chin Soc Corr Pro, 2005, 25(4): 218-221 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2005/V25/I4/218

[1]GaoYZ,YinZM,PanQL.InfluenceofminorZronmechanicalpropertiesandmicrostructuresofAl-Mg-Scalloy[J].Chinese JournalofRareMetals,1998,22(3):212～215(高拥政,尹志民,潘青林.微量锆对Al-Mg-Sc合金力学性能与显微组织的影响[J].稀有金属,1998,22(3):212～215)
[2]BazinYuA,etal.Possiblereasonforthemodificationandhardening ofaluminumbyscandium[J].Sov.Non-FerrousMet.Res.,1984,12:44
[3]BushuevYG,ShulginaVE.Aluminumandscandiumalloys:re searchandtestinginspacetechnology[J].Russ.Metall.,2001,4:425～431
[4]DritsME,etal.Theeffectofhomogenizingheatingontheproper tiesofalloysintheAl-ScandAl-Mg-Scsystems[J].Russ.Metall.,1984,4:229～323
[5]AhmadA,Ul-HamidA,Abdul-AleemBJ.Thecorrosionbehavior ofscandiumalloyedAl5052inneutralsodiumchloridesolution[J].Corros.Sci.,2001,43:1227-1243
[6]AhmadZ.Thepropertiesandapplicationofscandium-reinforceda luminum[J].JOM,2003,55(2):35-39
[7]BraunR,LenczowskiB,TempusG.Effectofthermalexposureon thecorrosionpropertiesofanAl-Mg-Scalloysheet[J].Mater.Sci.Forum.,2000,331-337:1647-1652
[8]ZhangYH,YinZ.etal.RecrystallizationofAl-Mg-Sc-Zralloys[J].RareMetalMater.Eng.,2002,31(4):167～170

[1]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[2]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[3]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[4]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[5]	艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.
[6]	李清, 张德平, 李晓荣, 王薇, 孙宝壮, 艾池. TP110TS和P110钢在CO₂注入井环空环境中应力腐蚀行为比较[J]. 中国腐蚀与防护学报, 2020, 40(4): 302-308.
[7]	李清, 张德平, 王薇, 吴伟, 卢琳, 艾池. L80油管钢实际腐蚀状况评估及室内电化学和应力腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 317-324.
[8]	朱丽霞, 贾海东, 罗金恒, 李丽锋, 金剑, 武刚, 胥聪敏. 外加电位对X80管线钢在轮南土壤模拟溶液中应力腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 325-331.
[9]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[10]	曹京宜, 方志刚, 陈晋辉, 陈志雄, 殷文昌, 杨延格, 张伟. 5083铝合金表面单致密微弧氧化膜的制备及其性能研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[11]	张震, 吴欣强, 谭季波. 电化学噪声原位监测应力腐蚀开裂的研究现状与进展[J]. 中国腐蚀与防护学报, 2020, 40(3): 223-229.
[12]	王英君, 刘洪雷, 王国军, 董凯辉, 宋影伟, 倪丁瑞. 新型高强稀土Al-Zn-Mg-Cu-Sc铝合金的阳极氧化及其抗腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 131-138.
[13]	陈旭,马炯,李鑫,吴明,宋博. 温度与SRB协同作用下X70钢在海泥模拟溶液中应力腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 477-483.
[14]	任建平,宋仁国. 双级时效对7050铝合金力学性能及氢脆敏感性的影响[J]. 中国腐蚀与防护学报, 2019, 39(4): 359-366.
[15]	王保杰,栾吉瑜,王士栋,许道奎. 镁合金应力腐蚀开裂行为研究进展[J]. 中国腐蚀与防护学报, 2019, 39(2): 89-95.

Viewed

Full text

Abstract

Cited

Shared

Discussed