固溶温度对15-5PH不锈钢耐点蚀性能的影响 |
周贤良1,2,聂轮2,华小珍2,刘智勇2,崔霞2,彭新元2 |
1. 南昌航空大学 教育部无损检测重点实验室 南昌 330063
2. 南昌航空大学材料科学与工程学院 南昌 330063 |
|
EFFECTS OF SOLID SOLUTION TEMPERATURE ON PITTING CORROSION BEHAVIOR OF 15-5PH PRECIPITATION HARDENED STAINLESS STEEL |
ZHOU Xianliang1,2, NIE Lun2, HUA Xiaozhen2, LIU Zhiyong2, CUI Xia2, PENG Xinyuan2
|
1. Key Laboratory of Nondestructive Test, Ministry of Education, Nanchang Hangkong University, Nanchang 330063
2. School of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063 |
引用本文:
周贤良,聂轮,华小珍,刘智勇,崔霞,彭新元. 固溶温度对15-5PH不锈钢耐点蚀性能的影响[J]. 中国腐蚀与防护学报, 2012, 32(4): 333-337.
ZHOU Xian-Liang.
EFFECTS OF SOLID SOLUTION TEMPERATURE ON PITTING CORROSION BEHAVIOR OF 15-5PH PRECIPITATION HARDENED STAINLESS STEEL. J Chin Soc Corr Pro, 2012, 32(4): 333-337.
链接本文:
https://www.jcscp.org/CN/
或
https://www.jcscp.org/CN/Y2012/V32/I4/333
|
[1] Liu Z B,Liang J X,Yang Z Y,et al. Effect of carbon content on microstructure and mechanical properties of type 15-5PH precipitation hardened stainless steel[J].J. Aeronaut. Mater., 2011,31(1): 7-12 (刘振宝, 梁剑雄, 杨志勇等. 碳含量对15-5PH沉淀硬化不锈钢板材的组织与性能的影响[J]. 航空材料学报, 2011, 31(1): 7-12)[2] Yang S W, Guo Y H, Zhang T Y, et al. Effect of solution treatment on corrosion resistance property and microstructure of 0Cr17Ni4Cu4Nb steel[J]. Develop. Appl. Mater., 2010, 25(6): 1-5 (杨世伟, 郭亚欢, 张天宇等. 固溶处理对0Cr17Ni4Cu4Nb钢耐腐蚀性能及组织的影响[J]. 材料开发与应用, 2010, 25(6): 1-5)[3] Hbibi Bajguirani H R. The effect of aging upon the microstructure and mechanical properties of type 15-5PH stainless steel[J]. Mater. Sci. Eng., 2002, A338: 142-159[4] Abdelshehid M, Mahmodieh K, Mori K, et al. On the correlation between fracture toughness and precipitation hardening heat treatments in 15-5PH stainless steel[J]. Eng. Failure Anal., 2007, 14: 626-631[5] Kamila Amato de Campos, Celso Yoshino, Luis Rogerio de Olivera Hein. Fractal behavior throughout stretch zone of 15-5PH steel under elastic-plastic loading conditions[J]. Mater. Sci. Eng., 2009, A525: 37-41[6] Tavares S S M, Silva F J, Scandian C, et al. Microstructure and intergranular corrosion resistance of UNS S17400 (17-4PH) stainless steel[J]. Corros. Sci., 2010, 52(11): 3835-3839[7] Huang G Q, Jin W X, Hou W T. A study on relationship between corrosion resistance and corrosion potential of stainless in seawater[J]. J. Chin. Soc. Corros. Prot., 2000, 20(1): 35-39 (黄桂桥, 金威贤, 候文泰. 不锈钢在海水中的腐蚀性与腐蚀电位的关系[J]. 中国腐蚀与防护学报, 2000, 20(1): 35-39)[8] Song S Z. Corrosion Electrochemical Research Methods[M]. Beijing: Chemical Industry Press, 1988: 187-188 (宋诗哲. 腐蚀电化学研究方法[M]. 北京: 化学工业出版社, 1988: 187-188)[9] Raja K S, Rao K P. Pitting behavior of type 17-4PH stainless steel weldments[J]. Corros. Sci., 1995, 51(8): 586-592 |
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|