泡沫SiC/Cu双连续相复合材料在NaCl溶液中的腐蚀行为

中国腐蚀与防护学报

2011, Vol. 31

Issue (2): 111-115

研究报告

本期目录 | 过刊浏览

泡沫SiC/Cu双连续相复合材料在NaCl溶液中的腐蚀行为

李凤歧，田冲，曹小明，张劲松

中国科学院金属研究所沈阳 110016

CORROSION BEHAVIOR OF FOAMED SiC/Cu CO-CONTINUOUS COMPOSITE IN NaCl AQUEOUS SOLUTION

LI Fengqi, TIAN Chong, CAO Xiaoming, ZHANG Jinsong

Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016

全文: PDF(1506 KB)

摘要: 用腐蚀失重法和电化学阻抗谱研究了泡沫SiC/Cu双连续相复合材料和对应的基体材料纯Cu在3.5% NaCl水溶液中的腐蚀行为。结果表明，在3.5% NaCl水溶液中，泡沫SiC/Cu双连续相复合材料比纯基体Cu具有更大的腐蚀敏感性，主要原因是该复合材料的特殊结构及残余应力的存在致使泡沫筋微孔中的 Cu严重腐蚀。

关键词 ： SiC/Cu双连续相复合材料, 腐蚀失重, 阻抗谱, 残余应力

Abstract：The corrosion behavior of the foamed SiC/Cu co-continuous composite and the corresponding matrix Cu in 3.5% NaCl aqueous solution was investigated by electrochemical impedance spectroscopy and immersion test. The results showed that the composite was corroded more seriously than the matrix Cu in the solution because of the severe corrosion of Cu in the micropores of the foamed SiC struts which could be mainly attributed to the special structure of the composite and the presence of residual stress.

Key words： SiC/Cu co-continuous composite corrosion mass loss electrochemical impedance spectroscopy residual stress

收稿日期: 2010-02-08

ZTFLH:

TG172.3

通讯作者: 张劲松 E-mail: jshzhang@imr.ac.cn

Corresponding author: ZHANG Jinsong E-mail: jshzhang@imr.ac.cn

作者简介: 李凤歧，男，1964年生，博士生，研究方向为复合材料

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	李凤歧
44.8K

引用本文:

李凤歧，田冲，曹小明，张劲松. 泡沫SiC/Cu双连续相复合材料在NaCl溶液中的腐蚀行为[J]. 中国腐蚀与防护学报, 2011, 31(2): 111-115.
LI Feng-Qi. CORROSION BEHAVIOR OF FOAMED SiC/Cu CO-CONTINUOUS COMPOSITE IN NaCl AQUEOUS SOLUTION. J Chin Soc Corr Pro, 2011, 31(2): 111-115.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2011/V31/I2/111

[1] Xie S J, Cao X M. Dry friction and wear properties of Cu matrix composite reinforced with three-dimensional network SiC [J]. Tribology, 2003, 23(2): 86-88

    (谢素菁, 曹小明. 三维网络SiC增强铜基复合材料的干摩擦磨损性能 [J]. 摩擦学学报, 2003, 23(2): 86-88)

[2] Ahmad Z. Mechanism of localized corrosion of aluminum-silicon carbide composites in a chloride containing environment [J]. J. Mater. Sci., 2000, 35: 2573--2577

[3] Arsenault R J, Fisher R M. Microstructure of fiber and particulate SiC in 6061Al composites [J]. Scr.Metall, 1983, 17: 67-71

[4] Candan S. Effect of SiC particle size on corrosion behavior of pressure infiltrated Al matrix composites in a NaCl solution [J]. Mater. Lett., 2004, 58: 3601-3605

[5] Saraswathi Y L, Das S, Mondal D P. Influence of microstructure and experimental parameters on the erosion-corrosion behavior of Al alloy composites [J].Mater. Sci. Eng., 2006, A 425: 244--254

[6] Shen B, Hu W, Liu L, Zhou W, Zhang D. Metal-matrix interpenetrating phase composites produced by squeeze casting [J]. Trans. Nonferrous Met. Soc.China, 2002, 12(1): 26-29

[7] Xu M D, Liu Y. Standard Manual for Metal Corrosion and Protection [S]. Beijing: China Environmental Science Press, 1996

    (徐明德, 刘颖. 金属腐蚀与防护标准手册 [S]. 北京: 中国环境科学出版社, 1996)

[8] Young W C, Budynas R G. Roark's Formulas for Strain and Stress [M]. Beijing: Science Press, 2005

    (W. 杨，R. 布迪纳斯. 罗氏应力应变公式手册 [M]. 北京: 科学出版社, 2005)

[9] An J R, Tian L G. Metallic Materials Data Handbook [M].Beijing: Chemical Industry Press, 2008

    (安继儒, 田龙刚. 金属材料手册 [M]. 北京: 化学工业出版社, 2008)

[10] Liu D X. The Corrosions and Protection of Materials [M]. Xi'an: Northwestern Polytechnical University Press, 2008

     (刘道新. 材料的腐蚀与防护 [M]. 西安: 西北工业大学出版社, 2008)

[1]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[2]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[3]	李雨,关蕾,王冠,张波,柯伟. 机械应力对不锈钢点蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(3): 215-226.
[4]	王霞,任帅飞,张代雄,蒋欢,古月. 豆粕提取物在盐酸中对Q235钢的缓蚀性能[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.
[5]	达波,余红发,麻海燕,吴彰钰. 等效电路拟合珊瑚混凝土中钢筋锈蚀行为的电化学阻抗谱研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 260-266.
[6]	达波,余红发,麻海燕,吴彰钰. 阻锈剂的掺入方式对全珊瑚海水混凝土中钢筋锈蚀的影响[J]. 中国腐蚀与防护学报, 2019, 39(2): 152-159.
[7]	邓培昌, 刘泉兵, 李子运, 王贵, 胡杰珍, 王勰. X70管线钢在热带海水-海泥跃变区的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 415-423.
[8]	邓三喜, 闫小宇, 柴柯, 吴进怡, 史洪微. 假单胞菌对聚硅氧烷树脂清漆涂层分解及防腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(4): 326-332.
[9]	曹海娇, 魏英华, 赵洪涛, 吕晨曦, 毛耀宗, 李京. Q345钢预热时间对熔结环氧粉末涂层防护性能的影响II：涂层体系失效行为分析[J]. 中国腐蚀与防护学报, 2018, 38(3): 255-264.
[10]	张杰, 胡秀华, 郑传波, 段继周, 侯保荣. 海洋微藻环境中钙质层对Q235碳钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(1): 18-25.
[11]	梅朦, 郑红艾, 陈惠达, 张鸣, 张大全. 硫酸盐还原菌对Cu在循环冷却水中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2017, 37(6): 533-539.
[12]	孟凡帝, 刘莉, 李瑛, 王福会. 用于原位检测在深海并压力交变环境中有机涂层电化学阻抗的预埋微电极研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 561-566.
[13]	王军, 冯超, 彭碧草, 谢亿, 张明华, 吴堂清. S450EW焊接接头在NaHSO₃溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 575-582.
[14]	王佳, 贾梦洋, 杨朝晖, 韩冰. 腐蚀电化学阻抗谱等效电路解析完备性研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 479-486.
[15]	陈振宁,陈日辉,潘金杰,滕艳娜,雍兴跃. L921A钢在3.5%NaCl溶液中的有机/无机复配缓蚀剂研究[J]. 中国腐蚀与防护学报, 2017, 37(5): 473-478.

Viewed

Full text

Abstract

Cited

Shared

Discussed