黄铜HSn70-1A、HA177-2A的抗冲刷能力比较研究

王志武;原素芳

武汉大学动力与机械学院材料工程系

EROSION RESISTANCE OF HA177-2A IN COMPARISON WITH HSn70-1A

;

武汉大学动力与机械学院材料工程系

全文: PDF(122 KB)

摘要: 利用自制的冲刷腐蚀装置，对HSn70-1A、HA177-2A黄铜管进行冲刷试验，对实验数据进行曲线拟合.结果表明：HSn70-1A、HA177-2A的冲刷腐蚀率与Cl-浓度及含砂量均成抛物线关系.HSn70-1A黄铜较HA177-2A黄铜对Cl-更敏感，更耐砂冲刷腐蚀；而HA177-2A黄铜较HSn70-1A黄铜更耐Cl-冲刷腐蚀.在低砂含量时，HA177-2A的抗冲刷腐蚀能力较HSn70-1A高；在高砂含量时，HA177-2A的抗冲刷腐蚀能力较HSn70-1A低.

关键词 ：黄铜, 冲刷腐蚀, 氯浓度, 含砂量

Abstract：With the self-made erosion test device,the erosion test of HSn70-1A brass and HA177-2A brass was carried out,and the right experiment data were matched into curves.The results showed clearly that the ［Cl-］and sand content influence the erosion.With the ［Cl-］or sand content increasing independently,the material erosion rate increased in a parabolic relationship.HSn70-1A brass was more sensitive to Cl- than HA177-2A brass,but it was more resistant to the erosion of sand in comparison with HA177-2A brass.However,when the sand content was low,the erosion resistance of HA177-2A brass was higher than HSn70-1A brass while in high sand content conditions,the result was just reversed.

Key words： brass erosion ［Cl-］ sand content

收稿日期: 2003-11-04

ZTFLH:

TG172.85

通讯作者: 王志武 E-mail: ysf8023@sohu.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	王志武
	原素芳
44.8K

引用本文:

王志武; 原素芳 . 黄铜HSn70-1A、HA177-2A的抗冲刷能力比较研究[J]. 中国腐蚀与防护学报, 2005, 25(3): 179-182 .
. EROSION RESISTANCE OF HA177-2A IN COMPARISON WITH HSn70-1A. J Chin Soc Corr Pro, 2005, 25(3): 179-182 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2005/V25/I3/179

[1]TheGenerateandTransmitElectricityBusinessOfficeofNational ElectricPowerCo.ElectricPowerIndustryTechnologyIntendance Manual[M].Beijing:ChineseElectricityPress,2003,885(国家电力公司发输电运营部编.电力工业技术监督标准汇编[M].北京:中国电力出版社,2003,885)
[2]DouZY.ErosionandCorrosion-ResistantofElectricPowerIn dustry[M].Beijing:ChemicalIndustryPress,1995,209(窦照英.电力工业的腐蚀与防护[M].北京:化学工业出版社,1995,209)
[3]WangXQ.ErosionandProtectionofThermodynamicEquipment[M].Beijing:WaterandElectricPowerPublishingCompany,1998,232-252(王杏卿.热力设备的腐蚀与防护[M].北京:水利电力出版社,1998,232-252)
[4]WangZW.Theinvestigationofthemainfirepowerplantcon densers′erosionconditionwhichbelongstoTianjinelectricpower company[J].TianjinElectricPowerTechnology,1998,(2):13-17(王志武.天津局属主要火电厂凝器铜管腐蚀情况的调查研究[J].天津电力技术,1998,(2):13-17)
[5]QianSB.Theinvestigationofthemainfirepowerplantcondensers′erosioncondition[J].GuangxiElectricPowerTechnology,1993,(4):1-6(钱生保.局属火电厂凝气器铜管腐蚀情况的调查研究[J].广西电力技术,1993,(4):1-6)
[6]YuLL.AppliedNonferrousMetalsManual[M].Beijing:Mechani calIndustryPress,2002,167(虞莲莲.实用有色金属材料手册[M].北京:机械工业出版社,2002,167)
[7]WangXT.MetalMaterials[M].Beijing:MechanicalIndustry Press,1987,273(王笑天.金属材料学[M].北京:机械工业出版社,1987,273)
[8]XiaLY,HuangGQ,ZhangSP.MarineCorrosionandCorrosion-ResistantofMetalMaterials[M].Beijing:MetallurgyIndustry Press,2003,103(夏兰廷,黄桂桥,张三平.金属材料的海洋腐蚀与防护[M].北京:冶金工业出版社,2003,103)
[9]LiJG,ZhaoGY.ErosionandCorrosion-ResistantControlManu al[M].Beijing:NationalDefenseIndustryPress,1988,16(李金桂,赵闺彦.腐蚀和防护控制手册[M].北京:国防工业出版社,1988,16)

[1]	白苗苗, 白子恒, 蒋立, 张东玖, 姚琼, 魏丹, 董超芳, 肖葵. H62黄铜/TC4钛合金焊接件腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 159-166.
[2]	胡宗武, 刘建国, 邢蕊, 尹法波. 单相流条件下90°水平弯管冲刷腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 115-122.
[3]	王勤英,裴芮,西宇辰. 镍基激光熔覆层冲刷腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 458-462.
[4]	姜爱国,张建文,辛亚男,丛晓明,董轼. 加氢裂化空冷器管束多相流冲刷腐蚀数值模拟[J]. 中国腐蚀与防护学报, 2019, 39(2): 192-200.
[5]	魏木孟,杨博均,刘洋洋,王孝平,姚敬华,高灵清. Cu-Ni合金管海水冲刷腐蚀研究现状及展望[J]. 中国腐蚀与防护学报, 2016, 36(6): 513-521.
[6]	彭文山,曹学文. 固体颗粒对液/固两相流弯管冲蚀作用分析[J]. 中国腐蚀与防护学报, 2015, 35(6): 556-562.
[7]	宋芳,陈友媛,常钦鹏,彭涛. 植酸自组装膜对HAl77-2黄铜缓蚀性能的影响[J]. 中国腐蚀与防护学报, 2015, 35(4): 317-325.
[8]	刘贵群, 郑玉贵, 姜胜利, 荆军航, 董伟娟, 曾宏, 司品宪. 模拟炼油环境中Q235钢和Cr5Mo钢表面硫化物膜稳定性及动态冲刷腐蚀行为研究[J]. 中国腐蚀与防护学报, 2015, 35(2): 122-128.
[9]	周婷婷, 袁成清, 曹攀, 王雪君, 董从林. 柴油机喷油嘴内流体冲刷腐蚀的数值模拟分析[J]. 中国腐蚀与防护学报, 2014, 34(6): 574-580.
[10]	李强, 唐晓, 李焰. 冲刷腐蚀研究方法进展[J]. 中国腐蚀与防护学报, 2014, 34(5): 399-409.
[11]	朱娟, 张乔斌, 陈宇, 张昭, 张鉴清, 曹楚南. 冲刷腐蚀的研究现状[J]. 中国腐蚀与防护学报, 2014, 34(3): 199-210.
[12]	乔岩欣,刘飞华,任爱,姜胜利,郑玉贵. 高氮钢和321不锈钢的冲刷腐蚀行为[J]. 中国腐蚀与防护学报, 2012, 32(2): 141-145.
[13]	吴军,李晓刚,董超芳,张三平,周建龙. 紫铜T2和黄铜H62在热带海洋大气环境中早期腐蚀行为[J]. 中国腐蚀与防护学报, 2012, 32(1): 70-74.
[14]	李守彪, 许立坤,沈承金,李相波. 等离子喷涂耐冲蚀陶瓷涂层的性能研究[J]. 中国腐蚀与防护学报, 2011, 31(3): 196-201.
[15]	金威贤雒娅楠宋诗哲. 金属材料实海冲刷腐蚀检测[J]. 中国腐蚀与防护学报, 2008, 28(6期): 337-340.

Viewed

Full text

Abstract

Cited

Shared

Discussed