喷射电沉积镍阴极极化行为研究

韩东生;荆天辅;乔桂英;周继锋;李季辉

亚稳材料制备技术与科学重点实验室

JET ELECTRODEPOSIT CATHODIC POLARIZATION ACTION

Dongsheng Han;Tianfu Jing;Guiying Qiao;Jifeng Zhou;Jihui Li

亚稳材料制备技术与科学重点实验室

全文: PDF(148 KB)

摘要: 通过阴极极化曲线的测定研究了硫酸盐电解液喷射速度μ(流速）对电流密度jc和阴极过电位ηc的影响。结果表明，电流密度为140A/dm2时，喷射速度由0.83m/s增大到5.00m/s,阴极过电位从1.48V增到8.52V.与槽镀搅拌作用相比,电解液流速增大,有利于氢还原析出,导致过电位显著增大,随电流密度增大,阴极上析氢步骤逐渐取代水合镍离子电化学还原步骤成为整个过程的控制步骤,过电位可达12.03V

关键词 ：喷射电沉积, 镍, 过电位, 控制步骤

Abstract：The relationship between jet flow rate,current density and cathodic overpotential was studied by measuring cathodic polarization curve in simple sulfate system.The results show that when jet flow rate increases from 0.83m/s to 5.00 m/s, overpotential increases from 1.48V to 8.52V (current density is 140 A/dm2). Compared with stir of traditional plating, cathodic overpotential increased obviously with jet flow rate increasing because of hydrogen deoxidization.Comtrol steps change from Ni2+. mH2O electrochemistry deoxidization to hydrogen deoxidization on cathodic surface with increase of current density. Overpotential can reach 12.03

Key words： jet electrodeposit nickel overpotential control steps

收稿日期: 2004-01-05

ZTFLH:

TG174.4

通讯作者: 韩东生 E-mail: hands130@sohu.com

Corresponding author: Dongsheng Han E-mail: hands130@sohu.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	韩东生
	荆天辅
	乔桂英
	周继锋
	李季辉
44.8K

引用本文:

韩东生; 荆天辅; 乔桂英; 周继锋; 李季辉 . 喷射电沉积镍阴极极化行为研究[J]. 中国腐蚀与防护学报, 2005, 25(1): 30-33 .
Dongsheng Han, Tianfu Jing, Guiying Qiao, Jifeng Zhou, Jihui Li. JET ELECTRODEPOSIT CATHODIC POLARIZATION ACTION. J Chin Soc Corr Pro, 2005, 25(1): 30-33 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2005/V25/I1/30

[1]ChengGH ,WangGX .ElectrochemicalMethodandApplication[M ].Beijing:ChemicalIndustryPress,2003:351-356(陈国华,王光信.电化学方法应用[M ].北京:化学工业出版社,2003:351-356)
[2]ImreBakonyi,EnikoToth-Kadar.Preparationandcharacterizationofd.c.-platednanocrystallinenickelelectrodeposits[J].Surf.Coat.Technol.,1996,(78):124-136
[3]EnikoToth-Kadar,ImreBakonyi.Microstructureandelectricaltransportpropertiesofpulsed-platednanocrystallinenickelelec trodeposits[J].Surf.Coat.Technol.,1996,(88):57-65
[4]XiongY ,JingTF ,ZhangCJ.Astudyofjetelectrodepositingnanometercrystallinenickel[J].PlatingandFinishing,2000,22(5):1-4(熊毅,荆天辅,张纯江.喷射电沉积纳米晶镍的研究[J].电镀与精饰,2000,22(5):1-4)
[5]ZhaQX ,etal.IntroductionofElectrodeDynamicsProcess(theThirdEdition)[M].Beijing:SciencePress,2002:204-211(查全性等.电极过程动力学导论(第三版)[M ].北京:科学出版社,2002:204-211)
[6]LiD .PrincipleofElectrochemistry[M ].Beijing:BeijingAviationandSpaceflightCollegePress,1989:420-441(李荻.电化学原理[M ].北京:北京航空航天大学出版社,1989:420-441)
[7]CarterTJ,CornishLA .HydrogeninMetals[J].EngineeringFail ureAnalysis,2001,(8):113-121
[8]AntropovLI .AcademicElectrochemistry[M].Beijing:HigherEd ucationPress,1984:85-90(安特罗波夫(苏).理论电化学[M ].北京:高等教育出版社,1984:85-90)
[9]ShanghaiLightIndustryAcad.Electrochemistry[M ].Shanghai:ShanghaiTechnologyPress,1978,6:88-91(上海轻工业专科学校.电化学[M ].上海:上海科学技术出版社,1978,6:88-91)

[1]	黄鹏, 高荣杰, 刘文斌, 尹续保. 盐溶液刻蚀-氟化处理制备X65管线钢镀镍超双疏表面及其耐蚀性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 96-100.
[2]	杨寅初,傅秀清,刘琳,马文科,沈莫奇. 喷射电沉积Ni-P-BN(h)-Al₂O₃复合镀层的耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 57-62.
[3]	王勤英,裴芮,西宇辰. 镍基激光熔覆层冲刷腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 458-462.
[4]	谢冬柏,周游宇,鲁金涛,王文,朱圣龙,王福会. Al/Si对镍基合金在超临界水中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(1): 68-76.
[5]	程多云,赵晋斌,刘波,姜城,付小倩,程学群. 高镍钢和传统耐候钢在马尔代夫严酷海洋大气环境中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(1): 29-35.
[6]	虞礼嘉,梁文萍,林浩,缪强,黄彪子,崔世宇. 激光重熔YSZ热障涂层950 ℃的热腐蚀行为[J]. 中国腐蚀与防护学报, 2019, 39(1): 77-82.
[7]	蒋斌, 曾利兰, 梁涛, 潘浩波, 乔岩欣, 张竞, 赵颖. 316L不锈钢表面超疏水微纳镍镀层定向电沉积工艺优化研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 438-446.
[8]	谢冬柏, 周游宇, 鲁金涛, 王文, 朱圣龙, 王福会. Cr对镍基合金在超临界水中氧化行为的影响研究[J]. 中国腐蚀与防护学报, 2018, 38(4): 358-364.
[9]	张心华,周仲康,徐群杰,陈晓春,闫爱军,廖强强,葛红花. 富镍导电涂层在模拟海水中的耐蚀性能研究[J]. 中国腐蚀与防护学报, 2017, 37(2): 189-194.
[10]	张乃强,岳国强,吕法彬,曹琦,李梦源,徐鸿. Inconel625合金在高温水蒸气环境中应力腐蚀开裂裂纹扩展速率研究[J]. 中国腐蚀与防护学报, 2017, 37(1): 9-15.
[11]	丁诗炳,项腾飞,李澄,郑顺丽,王绮,杜梦萍. 两步法制备超疏水耐蚀镍镀层[J]. 中国腐蚀与防护学报, 2016, 36(5): 450-456.
[12]	刘阳,华小珍,黄晋华,崔霞,周贤良,俞应炜. SiC表面化学镀镍对SiC_p/Al复合材料界面及耐蚀性影响[J]. 中国腐蚀与防护学报, 2016, 36(2): 130-136.
[13]	赵晓宏, 郭泉忠, 杜克勤, 郭兴华, 王勇. 不同涂层处理的汽车紧固件用ST12冷轧钢与SS400热轧钢的电偶腐蚀行为研究[J]. 中国腐蚀与防护学报, 2015, 35(1): 86-90.
[14]	常钦鹏, 陈友媛, 宋芳, 彭涛. B30铜镍合金和316L不锈钢在热泵系统中的耐腐蚀性能[J]. 中国腐蚀与防护学报, 2014, 34(6): 544-549.
[15]	孙飞龙, 卢琳, 李晓刚, 肖葵, 吴俊升, 汪崧. N6和Monel400镍合金在中国南海深海环境下的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2014, 34(2): 165-170.

Viewed

Full text

Abstract

Cited

Shared

Discussed