中国腐蚀与防护学报  2014, Vol. 34 Issue (2): 165-170    DOI: 10.11902/1005.4537.2013.104
  研究报告 本期目录 | 过刊浏览 |
N6和Monel400镍合金在中国南海深海环境下的腐蚀行为研究
孙飞龙, 卢琳, 李晓刚, 肖葵, 吴俊升, 汪崧
北京科技大学腐蚀与防护中心 北京 100083
Corrosion Behavior of N6 and Monel400 Nickel Alloy in Deep Sea Environment of South China Sea
SUN Feilong, LU Lin, LI Xiaogang, XIAO Kui, WU Junsheng, WANG Song
Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083, China
全文: PDF(5009 KB)   HTML
摘要: 

通过实海暴露实验,研究了N6纯Ni和Monel400镍合金在中国南海海域800和1200 m深海环境下的长周期 (3 a) 腐蚀行为。采用SEM,EDS和XRD技术,分别进行了腐蚀形貌观察,腐蚀产物成分和相组成分析。结果表明:在深海环境下,Monel400镍合金的耐局部腐蚀能力要优于N6纯Ni。N6纯Ni在绿色腐蚀产物膜 (由NiCl26H2O组成,还覆盖有少量的CaCO3和MgCO3等无机盐类) 下发生了很严重的隧道腐蚀,甚至出现了局部穿孔现象。Monel400镍合金表面生成了宽浅型的点蚀坑,点蚀坑上覆盖有由 (CuNi)2Cl(OH)3组成的腐蚀产物。N6纯Ni和Monel400镍合金的最大点蚀坑深度均随水深的增加而降低。

关键词 镍合金点腐蚀隧道腐蚀深海实海    
Abstract:The corrosion behavior of N6 nickel and Monel400 nickel alloy in 800 and 1200 m deep sea environment of South China Sea was studied by field test. The morphology and composition of corrosion product were examined by means of SEM, EDS and XRD techniques. The results indicated that the resistance to localized corrosion of Monel400 nickel alloy was better than that of N6 nickel. The green corrosion product of N6 nickel was composed of NiCl26H2O with a small amount of CaCO3 and MgCO3, under which severe tunnel corrosion occurred, while localized corrosion induced perforation even took place on N6 nickel samples. However, shallow and large size corrosion pits formed on Monel400 nickel alloy, which were covered by green corrosion product consisted of (CuNi)2Cl(OH)3. Comparing with the data of literatures, the maximum pit depth of N6 and Monel400 nickel alloy decreased as the depth of test side increased.
Key wordsnickel alloy    pitting corrosion    tunnel corrosion    deep sea    field test
收稿日期: 2013-06-06     
ZTFLH:  TG172.5  
基金资助:国家自然科学基金项目(51171025) 资助
通讯作者: lixiaogang@ustb.edu.cn   
作者简介: 孙飞龙,女,1985年生,博士生,研究方向为材料的自然环境腐蚀与防护

引用本文:

孙飞龙, 卢琳, 李晓刚, 肖葵, 吴俊升, 汪崧. N6和Monel400镍合金在中国南海深海环境下的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2014, 34(2): 165-170.
SUN Feilong, LU Lin, LI Xiaogang, XIAO Kui, WU Junsheng, WANG Song. Corrosion Behavior of N6 and Monel400 Nickel Alloy in Deep Sea Environment of South China Sea. Journal of Chinese Society for Corrosion and protection, 2014, 34(2): 165-170.

链接本文:

https://www.jcscp.org/CN/10.11902/1005.4537.2013.104      或      https://www.jcscp.org/CN/Y2014/V34/I2/165

[1] Schumacher M. Sea Water Corrosion Handbook [M]. New Jersey: Park Ridge, 1979
[2] Venkatesan R, Venkataswamy M A, Bhaskaran T A, et al. Corrosion of ferrous alloys in deep sea environment [J]. Br. Corros. J., 2002, 37: 257-266
[3] Venkatesan R. Studies on corrosion of some structural materials in deep sea environment [D]. Bangalore: Indian Institute of Science, 2000
[4] Beccaria A M, Poggi G, Castello G. Effect of some surface treatments on kinetics of aluminum corrosion in NaCl solutions at various hydrostatic pressure [J]. Br. Corros. J., 1986, 21: 19-27
[5] Beccaria A M, Fiordiponti P, Mattogno G. The effect of hydrostatic pressure on the corrosion of nickel in slightly alkaline solutions containing Cl- ions [J]. Corros. Sci., 1989, 29(4): 403-416
[6] Beccaria A M, Poggi G, Arfelli M, et al. The effect of salt concentration on nickel corrosion behaviour in slightly alkaline solutions at different hydroatatic pressures [J]. Corros. Sci., 1993, 34(6): 989-1005
[7] Beccaria A M, Poggi G, Gingaud D, et al. Effect of hydroatatic pressure on passivating power of corrosion layers formed on 6061 T6 aluminium alloy in sea water [J]. Br. Corros. J., 1994, 29(1): 65-69
[8] Beccaria A M, Poggi G, Castello G. Influence of passive film composition and sea water pressure on resistance to localized corrosion of some stainless steels in sea water [J]. Br. Corros. J., 1995, 30(4): 283-287
[9] Zhang T, Yang Y G, Shao Y W, et al. A stochastic analysis of the effect of hydrostatic pressure on the pit corrosion of Fe-20Cr alloy [J]. Electrochim. Acta, 2009, 54: 3915-3922
[10] Yang Y G, Zhang T, Shao Y W, et al. Effect of hydrostatic pressure on the corrosion behaviour of Ni-Cr-Mo-V high strength steel [J]. Corros. Sci., 2010, 52: 2697-2706
[11] Liu B, Cong Y, Zhang T, et al. Influence of deep-sea environment on corrosion behavior of pure nickel: influence of hydroatatic pressures on performance of passive film on pure nickel [J]. Corros. Sci. Prot. Technol., 2009, 21(1): 5-10
(刘斌, 丛园, 张涛等. 深海环境下静水压力对纯镍腐蚀行为的影响 [J]. 腐蚀科学与防护技术, 2009, 21(1): 5-10)
[12] Liu B, Cong Y, Zhang T, et al. Influence of deep-sea environment on corrosion behavior of pure nickel III-influence of hydroatatic pressures on pitting mechanism of pure nickel [J]. Corros. Sci. Prot. Technol., 2011, 23(3): 239-244
(刘斌, 丛园, 张涛等. 深海环境下对纯镍腐蚀行为的影响III-静水压力对纯镍点蚀机制的影响 [J]. 腐蚀科学与防护技术, 2011, 23(3): 239-244)
[13] Liu J, Li X B, Wang J. Effect of hydrostatic pressure on the corroaion behaviors of two low alloy steels [J]. Acta Metall. Sin., 2011, 47(6): 697-705
(刘杰, 李相波, 王佳. 模拟深海压力对2种低合金钢腐蚀行为的影响 [J]. 金属学报, 2011, 47(6): 697-705)
[14] Li J H, Lin D C. Metallographic Atlas of Metals [M]. Beijing: China Machine Press, 2006
(李炯辉, 林德成. 金属材料金相图谱 [M]. 北京: 机械工业出版社, 2006)
[1] 孙海静, 覃明, 李琳. 深海低溶解氧环境下Al-Zn-In-Mg-Ti牺牲阳极性能研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 508-516.
[2] 周宇, 张海兵, 杜敏, 马力. 模拟深海环境中阴极极化对1000 MPa级高强钢氢脆敏感性的影响[J]. 中国腐蚀与防护学报, 2020, 40(5): 409-415.
[3] 刘志峰,朱志平,石纯,黄赵鑫. 载流法制备硫酸露点腐蚀模拟气体的试验研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 1-9.
[4] 彭文山,侯健,丁康康,郭为民,邱日,许立坤. 深海环境中304不锈钢腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 145-151.
[5] 孙艳, 吴佳佳, 张盾, 陈士强. 不同海域、不同腐蚀区带Q235碳钢实海挂片腐蚀产物层内微生物调查[J]. 中国腐蚀与防护学报, 2018, 38(4): 333-342.
[6] 偶国富, 赵露露, 王凯, 王宽心, 金浩哲. 10#碳钢在HCl-H2O环境中的露点腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(1): 33-38.
[7] 高洪扬,王巍,许立坤,马力,叶章基,李相波. 改性环氧防腐涂层在模拟深海高压环境的失效行为[J]. 中国腐蚀与防护学报, 2017, 37(3): 247-263.
[8] 王子豪,黄运华,李佳,杨浪,谢冬寒. Nb对X80钢焊接热影响区在模拟海水中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2016, 36(6): 604-610.
[9] 曹攀, 周婷婷, 白秀琴, 袁成清. 深海环境中的材料腐蚀与防护研究进展[J]. 中国腐蚀与防护学报, 2015, 35(1): 12-20.
[10] 赵晓宏, 郭泉忠, 杜克勤, 郭兴华, 王勇. 不同涂层处理的汽车紧固件用ST12冷轧钢与SS400热轧钢的电偶腐蚀行为研究[J]. 中国腐蚀与防护学报, 2015, 35(1): 86-90.
[11] 常钦鹏, 陈友媛, 宋芳, 彭涛. B30铜镍合金和316L不锈钢在热泵系统中的耐腐蚀性能[J]. 中国腐蚀与防护学报, 2014, 34(6): 544-549.
[12] 李成杰,杜敏. 深海钢铁材料的阴极保护技术研究及发展[J]. 中国腐蚀与防护学报, 2013, 33(1): 10-16.
[13] 张勤杰,姚文红,贺本林,葛洪仑,孙苗,刘威,曲俊,王玮. 阳极氧化法制备TiO2膜在模拟深海热液区的耐腐蚀性能[J]. 中国腐蚀与防护学报, 2013, 33(1): 23-28.
[14] 鹿文珊,徐天凤,陈宇,张昭,张鉴清. 碱性电镀锌镍合金的研究[J]. 中国腐蚀与防护学报, 2012, 32(6): 443-448.
[15] 唐俊文,邵亚薇,张涛,孟国哲,王福会. 循环压力对环氧涂层在模拟深海环境中失效行为的影响[J]. 中国腐蚀与防护学报, 2011, 31(4): 275-281.