用热喷涂技术防止湿硫化氢应力腐蚀

张亦良;王慕;孙耀峰

北京工业大学机电学院

STUDY ON THERMAL SPRAYING TECHNIQUE USED FOR RESISTANCE TO WET H2S SULPHIDE STRESS CRACKING

Yiliang Zhang;Mu Wang;Yaofeng Sun

北京工业大学机电学院

全文: PDF(137 KB)

摘要: 采用热喷涂技术，设计了Al系、Fe-Cr系粉芯丝材涂层共5种，并对其进行了结合强度、氢扩散能力、电化学性能及应力腐蚀性能等系列试验，考核其抗湿硫化氢应力腐蚀能力.通过对各涂层试验结果的对比分析，从中筛选出了防护效果最佳的配方，并对涂层抗湿硫化氢应力腐蚀的机理进行了讨论.

关键词 ：湿硫化氢应力腐蚀, 热喷涂层, 粉芯丝材

Abstract：Considering the urgent need for methods of resistan ce to wet H2S stress corrosion cracking (SSC) during petrochemical production ,this paper,with a view to isolate substrate from the corrosives,introduced arc spraying metallic coatings as a method resistant to SSC.Five coating products i ncluding both coatings of Al series and coatings of Fe-Cr series,which are made from self-developed cored wires,were designed.A series of tests where variables such as bond adhesion tests,hydrogen permeation tests,electrochemical tests and stress corrosion tests were carried out in order to check the performance of SSC .The test results of all kinds of coatings were compared with each other,a kind of most protective coating termed ZH4 containing Al+Al2O3+RE was obtained.I n addition,the protective mechanism of coatings resistance to SSC was discussed. 

Key words： wet H2S stress corrosion cracking thermal spraying c oating cored wire

收稿日期: 2001-11-20

ZTFLH:

TG174

通讯作者: 张亦良 E-mail: zhangyil@bjut.edu.cn

Corresponding author: Yiliang Zhang E-mail: zhangyil@bjut.edu.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	张亦良
	王慕
	孙耀峰
44.8K

引用本文:

张亦良; 王慕; 孙耀峰 . 用热喷涂技术防止湿硫化氢应力腐蚀[J]. 中国腐蚀与防护学报, 2003, 23(4): 243-247 .
Yiliang Zhang, Mu Wang, Yaofeng Sun. STUDY ON THERMAL SPRAYING TECHNIQUE USED FOR RESISTANCE TO WET H2S SULPHIDE STRESS CRACKING. J Chin Soc Corr Pro, 2003, 23(4): 243-247 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2003/V23/I4/243

[1]ZhangYiliang,YaoXimeng.Onsulphidestresscrackingofsteelusedinpressurevessels[J].PressureVesselTechnology,1998,15(1):30-35.(张亦良.姚希梦.压力容器用钢的硫化氢应力腐蚀[J].压力容器,1998,15(1):30-35)
[2]IwonaSmuga-Otto.Developingamethodologyforperformancee valuationofmetallicthermalspraycoatingsforoilandgasindustryservice[J].MaterialsPerformance,1998,37(7):34-40
[3]TsaiSY ,ShihHC .Theuseofthermal-spraycoatingsforpre ventingwetH2ScrackinginHSLAsteelplates[J].CorrosionPre vention&Control,April1997,42-48
[4]BaronJJ ,HayMG ,etal.ResultsoffieldapplicationandlaboratorytestingofthermalsprayUNSN10276coatingforsouraminevessels[A].Corrosion/98[C].Houston:NACE ,1998,512
[5]GaoLimin,LiGuoxing.TheapplicationofthermalsprayZn-Alcoatingforcorrosionprotectioninoiltank[J].StoreandTrans portationofOil&Gas,1997,16(11):21-22(高莉敏,李国兴.热喷涂锌铝覆盖层在油罐防腐中的应用[J].油气储运,1997,16(11):21-22)
[6]Themeasurementofbondadhesionstrengthforthermalspraycoat ing[S].GB8642-88(热喷涂层结合强度的测定[S].GB8642-88)
[7]Theconstantloadtensiletestmethodofmetalsforresistancetosul phidestresscorrosioncracking[S].GB4157-84(金属抗硫化氢应力腐蚀开裂恒负荷拉伸试验方法[S].GB4157-84)

[1]	黄鹏, 高荣杰, 刘文斌, 尹续保. 盐溶液刻蚀-氟化处理制备X65管线钢镀镍超双疏表面及其耐蚀性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 96-100.
[2]	戴婷, 顾艳红, 高辉, 刘凯龙, 谢小辉, 焦向东. 水下摩擦螺柱焊接头在饱和CO₂中的电化学性能[J]. 中国腐蚀与防护学报, 2021, 41(1): 87-95.
[3]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[4]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[5]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[6]	王亚婷, 王棵旭, 高鹏翔, 刘冉, 赵地顺, 翟建华, 屈冠伟. 淀粉接枝共聚物对Zn的缓蚀性能[J]. 中国腐蚀与防护学报, 2021, 41(1): 131-138.
[7]	魏征, 马保吉, 李龙, 刘潇枫, 李慧. 镁合金表面超声滚压预处理对微弧氧化膜耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[8]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[9]	陈文韦奉黄德兴. 苏铁蕨提取物对碳钢在盐酸中的缓蚀行为研究[J]. 中国腐蚀与防护学报, 0, (): 0-0.
[10]	吴林涛周泽华张欣杨光恒张凯城王光宇. 等离子喷涂FeCrMoCBY铁基非晶涂层长期耐蚀性研究[J]. 中国腐蚀与防护学报, 0, (): 0-0.
[11]	姜伯晨曹将栋曹雪玉王建涛张少朋. Gd2(Zr1-xCex)2O7热障涂层陶瓷层材料的CMAS热腐蚀行为研究[J]. 中国腐蚀与防护学报, 0, (): 0-0.
[12]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[13]	孙海静, 覃明, 李琳. 深海低溶解氧环境下Al-Zn-In-Mg-Ti牺牲阳极性能研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 508-516.
[14]	张浩, 杜楠, 周文杰, 王帅星, 赵晴. 模拟海水溶液中Fe³⁺对不锈钢点蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[15]	卢爽, 任正博, 谢锦印, 刘琳. 2-氨基苯并噻唑与苯并三氮唑复配体系对Cu的缓蚀性能[J]. 中国腐蚀与防护学报, 2020, 40(6): 577-584.

Viewed

Full text

Abstract

Cited

Shared

Discussed