凝露状态下SO2对A3钢腐蚀机理的影响

韩薇;贾薇;汪俊

中国科学院金属研究所;金属腐蚀与防护国家重点实验室

EFFECT OF SO2 ON CORROSION MECHANISMOF A3 STEEL AT DEWING ENVIRONMENT

Wei Han;Wei Jia;Jun Wang

中国科学院金属研究所;金属腐蚀与防护国家重点实验室

全文: PDF(150 KB)

摘要: 采用红外光谱、电化学交流阻抗和扫描电镜等方法研究了大气中对金属腐蚀性最强的污染物SO2在凝露状态下对A3钢的腐蚀作用规律.结果表明，A3钢在加SO2试验环境中腐蚀失重随试验时间延长呈正指数变化规律；试样表面呈龟裂状腐蚀形貌，红外光谱的分析结果显示出腐蚀产物为FeSO4·7H2O、Fe2(SO4)3·9H2O 和γ-FeOOH，还含有δ-FeOOH及少量的Fe(OH)2和Fe3O4.A3钢在未加SO2试验环境中腐蚀失重随时间呈直线变化规律；腐蚀产物主要为Fe2O3和γ-FeOOH；试样表面未形成连续的腐蚀产物膜.

关键词 ： A3钢, 大气腐蚀, SO2

Abstract：The effect of SO2 which is the most aggressive su bstance towards metals in wet atmosphere on the corrosion A3 steel was studied b y means of AC impedance,IRAS and SEM.The results indicate that,corrosion weight loss increased with time evidently in test environment with SO2,especially at last period time.The surface of the test specimens is in a chap feature.The IR a b sorption spectra shows that,corrosion product layer is rich of FeSO4·7H2O,F e2(SO4)3·9H2O and γ-FeOOH,there are a little of δ-FeOOH and,a nd a trace of Fe(OH)2 and Fe3O4.The corrosion weight loss with time of A3 steel accords with the law of line in test environment without SO2,the corrosi on products on specimens are Fe2O3 and γ-FeOOH，which did not cover com pletely on speciments.

Key words： A3 steel atmospheric corrosion sulphur dioxide

收稿日期: 2001-09-17

ZTFLH:

TG172.3

通讯作者: 韩薇

Corresponding author: Wei Han

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	韩薇
	贾薇
	汪俊
44.8K

引用本文:

韩薇; 贾薇; 汪俊 . 凝露状态下SO2对A3钢腐蚀机理的影响[J]. 中国腐蚀与防护学报, 2002, 22(6): 355-358 .
Wei Han, Wei Jia, Jun Wang. EFFECT OF SO2 ON CORROSION MECHANISMOF A3 STEEL AT DEWING ENVIRONMENT. J Chin Soc Corr Pro, 2002, 22(6): 355-358 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2002/V22/I6/355

[1]BrawnPW .“FactorsAffectingtheCorrosionofMetalsinAtmo sphere”AtmosphericCorrosion[M].Canada:JohnWileyandSons,1982,31-49
[2]DuncanJR .Analysesofsomesuggestedmechanismsforatmo sphericcorrosionofironinpresenceofSO2[J].Werkst.Korros,1974,25:420
[3]AllamIM ,ArlowJS ,SaricimenH .InitialstagesofatmosphericcorrosionofsteelintheArabiangulf[J].CorrosionScience,1991,32:417
[4]NyquistRichardA ,KagelRonaldO .InfraredSpectraofInorganicCompounds[M].London:AcademicPress,UK ,1971
[5]RamanA ,KubanB ,RazvanA .Theapplicationofinfraredspec troscopytothestudyofatmosphericrustsystems-Ⅰ.standardspectraandillustrativeapplicationstoidentifyrustphasesinnaturalatmosphericcorrosion products[J].CorrosionScience,1991,32:1295
[6]CoxA ,LyonSB .Anelectrochemicalstudyoftheatmosphericcor rosionofiron-Ⅱcathodicandanodicprocessesonuncorrodedandpre-corrodediron[J].CorrosionScience,1994,36(7):1177-1192
[7]WangJH ,WeiFI ,ShihHC .Modelingofatmosphericcorrosionbehaviorofweatheringsteelinsulfurdioxide-pollutedatmo spheres[J].Corrosion,1996,52(12):900-909
[8]WangZhenyao,ZhengYiping,YuGuocai,LiWenqing.Atmospher iccorrosionofsteelsinpollutedenvironment[J].Corr.Sci.Prote.Technol.,1999,11:306
[9]JohanssonLG ,VannerbergNG .Theatmosphericcorrosionofun protectedcarbonsteel-acomparisonbetweenfieldandlaboratory[J].Werkst.Korros.1981,32:265
[10]CoxA ,LyonSB .Anelectrochemicalstudyoftheatmosphericcor rosionofmildsteel-Ⅲtheeffectofsulphurdioxide[J].CorrosionScience,1994,36(7):1193-1199

[1]	范益,陈林恒,蔡佳兴,代芹芹,马宏驰,程学群. 热轧AH36船板钢在室内仓储条件下的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 10-16.
[2]	潘成成,马超,夏大海. EBSD技术研究金属材料晶体取向对大气腐蚀萌生的影响机理[J]. 中国腐蚀与防护学报, 2019, 39(6): 495-503.
[3]	赵晋斌,赵起越,陈林恒,黄运华,程学群,李晓刚. 不同表面处理方式对300M钢在青岛海洋大气环境下腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 504-510.
[4]	邓俊豪,胡杰珍,邓培昌,王贵,吴敬权,王坤. 氧化皮对SPHC热轧钢板在热带海洋大气环境中初期腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(4): 331-337.
[5]	孙永伟,钟玉平,王灵水,范芳雄,陈亚涛. 低合金高强度钢的耐模拟工业大气腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 274-280.
[6]	王力, 郭春云, 肖葵, 吐尔逊·斯拉依丁, 董超芳, 李晓刚. Q235和Q450钢在吐鲁番干热大气环境中长周期暴晒时的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 431-437.
[7]	王军, 冯超, 彭碧草, 谢亿, 张明华, 吴堂清. S450EW焊接接头在NaHSO₃溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 575-582.
[8]	张新新,高志明,胡文彬,伍志鹏,韩连恒,卢丽花,修妍,夏大海. Q235钢在薄液膜下腐蚀行为与图像信息的相关性研究[J]. 中国腐蚀与防护学报, 2017, 37(5): 444-450.
[9]	张鑫,戴念维,杨燕,张俊喜. 模拟工业环境下直流电场对金属Zn腐蚀机理的影响[J]. 中国腐蚀与防护学报, 2017, 37(5): 451-459.
[10]	孟晓波,蒋武斌,廖永力,李锐海,郑志军,高岩. 输电杆塔材料在模拟工业环境中的大气腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(5): 460-466.
[11]	孙霜青,郑弃非,李春玲,王秀民,胡松青. 腐蚀产物对纯Al 8A06长期大气腐蚀行为影响的研究[J]. 中国腐蚀与防护学报, 2017, 37(2): 110-116.
[12]	白子恒,黄运华,李晓刚,杨浪,董超芳,颜利丹,肖葵. 硫硼酸阳极氧化处理的7050铝合金在工业海洋大气中的腐蚀行为[J]. 中国腐蚀与防护学报, 2016, 36(6): 580-586.
[13]	李东亮,付贵勤,朱苗勇. 湿热工业海洋大气中Si对桥梁钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2016, 36(5): 433-440.
[14]	刘艳洁,王振尧,柯伟. 纯Al在3种典型沿海,工业和乡村大气中的腐蚀行为[J]. 中国腐蚀与防护学报, 2016, 36(1): 47-51.
[15]	陈启萌,张俊喜,原徐杰,戴念维. 外加交流电场对薄液膜中氧扩散的影响[J]. 中国腐蚀与防护学报, 2015, 35(6): 549-555.

Viewed

Full text

Abstract

Cited

Shared

Discussed