磁控溅射IN738涂层耐盐水腐蚀性能研究

李瑛;耿树江;王福会

中国科学院金属研究所;金属腐蚀与防护国家重点实验室

CORROSION RESISTANCE OF NANOCRYSTALLIZEDIN738 COATING IN SALT SOLUTION

Ying Li;Shujiang Geng;Fuhui Wang

中国科学院金属研究所;金属腐蚀与防护国家重点实验室

全文: PDF(367 KB)

摘要: 利用电化学方法、扫描电镜和扫描隧道显微镜等技术，研究了纳米晶IN738涂层耐盐水腐蚀性能，探讨了溅射纳米涂层的腐蚀机制，发现表面纳米化导致钝性金属材料钝化膜的溶解速度增加,而表面微观孔隙的存在使材料的耐点蚀能力下降，但是纳米IN738涂层总体耐蚀性能很高.

关键词 ：磁控溅射, IN738涂层, 盐水, 耐蚀性能

Abstract：The corrosion resistance of nanocrystallized IN738 coating fabricated by magnetron sputtering technique has been evaluated by elect rochemical methods and surface analysis technique such as SEM、STM.The dissoluti on rate of IN738 coating was higher than that of IN738 alloy and the pitting res istance was deteriorated for the defects engendered during sputtering process.Ho wever,the corrosion resistance of nanocrystallized IN738 coating was high enough for the application requirement.

Key words： magnetron sputtering IN738 coating corrosion resistanc

收稿日期: 2001-06-22

ZTFLH:

TG174.71

通讯作者: 李瑛

Corresponding author: Ying Li

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	李瑛
	耿树江
	王福会
44.8K

引用本文:

李瑛; 耿树江; 王福会 . 磁控溅射IN738涂层耐盐水腐蚀性能研究[J]. 中国腐蚀与防护学报, 2002, 22(6): 349-354 .
Ying Li, Shujiang Geng, Fuhui Wang. CORROSION RESISTANCE OF NANOCRYSTALLIZEDIN738 COATING IN SALT SOLUTION. J Chin Soc Corr Pro, 2002, 22(6): 349-354 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2002/V22/I6/349

[1]LouH ,WangF ,XiaB ,ZhangL .High-temperatureoxidationre sistanceofsputteredmicro-grainsuperalloyK38G [J].Oxid.Met.,1992,38:299
[2]LouH ,WangF ,ZhuS ,XiaB ,ZhangL .OxideformationofK38Gsuperalloyanditssputteringmicrograinedcoating[J].Surf.Coat.Tech.,1994,38:105
[3]WangF .TheeffectofnanocrystallizationontheselectiveoxidationandadhesionofAl2O3 scales[J].Oxid.Met.,1997,48:21
[4]LouH ,TangY ,SunX ,GuanH .OxidationbehaviorofsputteredmicrocrystallinecoatingofsuperalloyK17Fathightemperature[J].Mater.Sci.Eng.1996,A207:121
[5]ZhangJ ,LouHY .OxidationbehaviorofthesputteredmicrocrystallinecoatingofLDZ125superalloyathigh-temperature[J].ActaMetallurgicaSinica,1998,34:627(张捷,楼翰一.溅射LDZ125微晶涂层抗高温氧化行为[J].金属学报,1998,34:627)
[6]ZhangJ,LouHY .Cyclicoxidationbehaviorofthesputteredmicro crystallinecoatingofLDZ125superalloyat1000℃[J].Corros.Sci.Prote.Technol.,1998,10:82(张捷,楼翰一.LDZ125微晶涂层抗循环氧化性能[J].腐蚀科学与防护技术,1998,10:82)
[7]GenSJ,WangFH ,ZhuSL .Isothermaloxidationbehaviorofsput teredIN738nanocrystallinecoating[J].J.ChineseSocietyforCor rosionandProtection,2001,21(3):137(耿树江,王福会,朱圣龙.溅射纳米晶IN738合金的恒温氧化行为[J].中国腐蚀与防护学报,2001,21(4):137)
[8]LiY ,WangFH ,LiuG .Grain-sizeeffectontheelectrochemicalcorrosionofsurfacenanocrystallizedlowcarbonsteel[J].J.ChineseSocietyforCorrosionandProtection,2001,21(4):215(李瑛,王福会,刘刚.表面纳米化低碳钢电化学行为尺寸效应[J].中国腐蚀与防护学报,2001,21(4):215)
[9]LiXL ,LiY ,WangFH .StudyonthecorrosionpropertyofsurfacenanocrystallizedFe20CralloybyUSSPtechnique[J].J.ChineseSocietyforCorrosionandProtection,2002,22(6):326-329(李雪莉,李瑛,王福会.USSP表面纳米化Fe-20Cr合金腐蚀性能研究[J].中国腐蚀与防护学报,2002,22(6):326-329)

[1]	骆鸿,高书君,肖葵,董超芳,李晓刚. 磁控溅射工艺对CrN薄膜及其腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(5): 423-430.
[2]	孙超, 杨潇, 文玉华. 表面溅射高含铝奥氏体不锈钢合金涂层对316不锈钢抗高温氧化性能的影响[J]. 中国腐蚀与防护学报, 2017, 37(6): 590-596.
[3]	杨甜甜,徐敬军,钱余海,李美栓. 石墨基体上ZrC/MoSi₂微叠层涂层的制备及抗超高温氧化性能[J]. 中国腐蚀与防护学报, 2016, 36(5): 476-482.
[4]	晏敏胜, 何进, 冒守栋, 杨丽景, 聂霞, 宋振纶, 詹肇麟. NiCrAlY薄膜对Sm₂Co₁₇磁体高温抗氧化性的影响[J]. 中国腐蚀与防护学报, 2015, 35(2): 183-188.
[5]	蒋穹,缪强,姚正军,魏小昕. 水性Al-Zn-Si合金涂层微观组织及腐蚀性能研究[J]. 中国腐蚀与防护学报, 2012, 32(4): 311-316.
[6]	余建飞;江莉;甘复兴. 3-氨基-5-巯基-1,2,4-三唑在除盐水中对Cu的缓蚀作用[J]. 中国腐蚀与防护学报, 2010, 30(1): 21-24.
[7]	吕海波; 李瑛; 王福会 . 纳米化对Cu-20Zr合金腐蚀行为的改善[J]. 中国腐蚀与防护学报, 2006, 26(3): 171-175 .
[8]	吕海波; 李瑛; 王福会 . Cu-20Zr合金在盐酸溶液中的脱合金腐蚀历程[J]. 中国腐蚀与防护学报, 2006, 26(2): 75-79 .
[9]	孟国哲; 李瑛; 王福会 . Fe-20Cr纳米涂层的电化学行为[J]. 中国腐蚀与防护学报, 2006, 26(1): 11-18 .
[10]	耿树江; 朱圣龙; 王福会 . 在600℃～700℃固态NaCl和水蒸气综合作用下K38G及其纳米晶涂层的腐蚀行为[J]. 中国腐蚀与防护学报, 2003, 23(4): 193-197 .
[11]	李雪莉; 李瑛; 王福会 . Fe20Cr溅射纳米涂层腐蚀电化学性能研究[J]. 中国腐蚀与防护学报, 2003, 23(2): 84-88 .
[12]	卢锦堂;陈锦虹;许乔瑜;曾广亮;李国雄;张泽健. Si和RE对热浸铝镀层耐盐水腐蚀性能的影响[J]. 中国腐蚀与防护学报, 1997, 17(1): 63-67.

Viewed

Full text

Abstract

Cited

Shared

Discussed