机械合金化Cu-Cr合金在0.1MPa纯氧气中的氧化

付广艳;牛焱;王崇琳

中科院腐蚀与防护研究所

OXIDATION OF MECHANICALLY ALLOYED Cu-Cr ALLOYS IN 0.1 MPa O2

Guangyan Fu;Yan Niu;;

中科院腐蚀与防护研究所

全文: PDF(244 KB)

摘要: 采用机械合金化法制备了两相颗粒极细的Cu-20Cr与Cu-40Cr合金，研究其在700-800℃0.1MPa纯氧气中的氧化。MACu-40Cr合金24h氧化后均形成了连续的Cr2O3层，这主要由于两相颗粒的细化，加快了Cr颗粒的溶解，缩短了Cr的扩散距离，从而有效地促进CrO3层的形成。

关键词 ：机械合金化, Cu-Cr合金, 氧化

Abstract：The oxidation behavior of Cu-Cr alloys with Cr concentrations 20%(mass) (MACu-20Cr) and 40% (MACu-40Cr) was studied in 0.1 MPa O2 at 700-800℃.The Cu-Cr alloys were prepared by mechanical alloying, presenting a much smaller particle size of phases. Both MA Cu-20Cr of MACu-40Cr formed a continuos Cr2O3 layer.The result is connected with the fact that the smaller Cr-rich particles dissolve more rapidly ,have short diffusion distance between Cr-rich phase particles,and can provide a faster supply of Cr to the external Cr2O3 scales with respect to larger particles.

Key words： mechanical alloying Cu-Cr alloy oxidation

收稿日期: 1999-08-23

ZTFLH:

TG172.82

通讯作者: 付广艳

Corresponding author: Guangyan Fu

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	付广艳
	牛焱
	王崇琳
44.8K

引用本文:

付广艳; 牛焱; 王崇琳 . 机械合金化Cu-Cr合金在0.1MPa纯氧气中的氧化[J]. 中国腐蚀与防护学报, 2000, 20(5): 269-274 .
Guangyan Fu, Yan Niu. OXIDATION OF MECHANICALLY ALLOYED Cu-Cr ALLOYS IN 0.1 MPa O2. J Chin Soc Corr Pro, 2000, 20(5): 269-274 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2000/V20/I5/269

[1] Kofstad P.High Temperature Corrosion[M].London: Elsevier Applied Science,1988.389 - 408, 335 - 340.
[2]付广艳,牛焱,吴维　.二元双相Cu-50Cr合金在700-900℃空气中的氧化[J].金属学报,1998,34(2):159-163.
[3] Niu Yan, Gesmundo F,Fu Guangyan,Douglass D L. The Sulfidation of three two-phase Cu-Cr alloys in H2-H2S mixtures at 400~600℃[J]. Oxidation of Metals,1998,50:327-335
[4]付广艳,牛焱,吴维　.粉末冶金Cu-Cr合金在0.1MPa纯氧气中的氧化[J].中国有色金属学报.接收待发表
[5] Chakrabarti D J,Laughlin D E. Copper-Chromium phase diagram[J].Bulletin of alloy phase diagram,1984, 5:59-67.
[6] Gesmundo F, Nanni P.Oxidation behavior of two-phase alloy Fe-44 w/o Cu[J].J.Electrochemical Society ,1980,81773-1782
[7] Niu Yan,Fu Guangyan,Wu Weitao,Gesmundo F.The oxidation of a Fe-Ce alloy under low oxygen pressures at 600-800℃[J].HighTemperature Materials and Processes,1999,18:159-172
[8] Fu Guangyan,Niu Yan,Wu Weitao.The oxidation of a Co-15wt% Ce alloy under low oxygen pressures at 600~800℃[J].CorrosionScience,1998,40:1215-1228
[9] Gesmundo F,Niu Y,Viani F,et al.The transition from the formation of mixed scales to the selective oxidation of the most component inthe corrosion of single and two-phase binary alloys[J].oxidation of Metals,1993,40:373 - 393
[10] Gesmundo F,Viani F, Niu Yan.The possible scaling modes in the high-temperature oxidation of two-phase binary alloys[J]. Oxidation of metals,1994,42:409-429.
[11] Perez P, Gonzalez-Carresco J L, Adeva P. Influence of powder particle size on the oxidation behavior of a PM Ni3 AI alloy[J]. Oxidationof Metals, 1998,49:485-507

[1]	魏征, 马保吉, 李龙, 刘潇枫, 李慧. 镁合金表面超声滚压预处理对微弧氧化膜耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[2]	刘晓, 王海, 朱忠亮, 李瑞涛, 陈震宇, 方旭东, 徐芳泓, 张乃强. 电站用奥氏体耐热钢HR3C与Sanicro25在超临界水中的氧化特性[J]. 中国腐蚀与防护学报, 2020, 40(6): 529-538.
[3]	谢冬柏, 洪昊, 王文, 彭晓, 多树旺. 模拟燃烧环境介质和温度对不锈钢表面氧化物形态的影响研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 358-366.
[4]	曹京宜, 方志刚, 陈晋辉, 陈志雄, 殷文昌, 杨延格, 张伟. 5083铝合金表面单致密微弧氧化膜的制备及其性能研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[5]	王廷勇, 董如意, 许实, 王辉. 石墨烯改性Ti/IrTaSnSb-G金属氧化物阳极在低温和低盐NaCl溶液中的电化学性能[J]. 中国腐蚀与防护学报, 2020, 40(3): 289-294.
[6]	方旭东, 刘晓, 徐芳泓, 李瑞涛, 朱忠亮, 张乃强. 超超临界电站国产奥氏体钢C-HRA-5在超临界水中的氧化特性[J]. 中国腐蚀与防护学报, 2020, 40(3): 266-272.
[7]	王英君, 刘洪雷, 王国军, 董凯辉, 宋影伟, 倪丁瑞. 新型高强稀土Al-Zn-Mg-Cu-Sc铝合金的阳极氧化及其抗腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 131-138.
[8]	秦越强, 左勇, 申淼. FLiNaK-CrF₃/CrF₂氧化还原缓冲熔盐体系对316L不锈钢耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(2): 182-190.
[9]	郑艳欣, 刘颖, 宋青松, 郑峰, 贾玉川, 韩培德. 含铁铜基陶瓷复合材料高温氧化行为与耐磨性研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 191-198.
[10]	范益,陈林恒,蔡佳兴,代芹芹,马宏驰,程学群. 热轧AH36船板钢在室内仓储条件下的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 10-16.
[11]	徐勋虎,何翠群,向军淮,王玲,张洪华,郑晓冬. Co-20Re-25Cr-1Si合金在0.1 MPa纯O₂中的高温氧化行为[J]. 中国腐蚀与防护学报, 2020, 40(1): 75-80.
[12]	姜冬雪,付颖,张峻巍,张伟,辛丽,朱圣龙,王福会. 钛合金表面Al₂O₃陶瓷膜制备及性能研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 469-476.
[13]	王毅,张盾. 铋系可见光催化海洋防污材料研究进展[J]. 中国腐蚀与防护学报, 2019, 39(5): 375-386.
[14]	魏欣欣,张波,马秀良. FeCr₁₅Ni₁₅单晶600 ℃下热生长氧化膜的TEM观察[J]. 中国腐蚀与防护学报, 2019, 39(5): 417-422.
[15]	肖金涛,陈妍,邢明秀,鞠鹏飞,孟引根,王芳. 工艺参数对2195铝锂合金阳极氧化膜的耐蚀性影响[J]. 中国腐蚀与防护学报, 2019, 39(5): 431-438.

Viewed

Full text

Abstract

Cited

Shared

Discussed