304不锈钢在热带海洋大气下暴露试验和加速腐蚀试验研究

中国腐蚀与防护学报

技术报告

本期目录 | 过刊浏览

304不锈钢在热带海洋大气下暴露试验和加速腐蚀试验研究

骆鸿¹,李晓刚¹,董超芳¹,²,肖葵³

1. 北京科技大学腐蚀与防护中心
2.
3. 北京科技大学

The research of 304 stainless steel in the tropical marine atmosphere exposure and the accelerated corrosion test

xiaogang li ²,³,

全文: PDF(1069 KB)

摘要:

根据304不锈钢材料在西沙地区典型的热带海洋大气腐蚀的特点，在当量计算的基础上，发展了一种模拟西沙室外大气环境的室内加速腐蚀方法，且从腐蚀动力学特征、腐蚀机理、腐蚀产物等几个方面探讨了304不锈钢材料在我国典型热带海洋地区大气暴露试验结果和室内加速腐蚀试验结果的相关性。研究结果表明，紫外/周期浸润复合加速腐蚀试验一定程度上能较好的模拟304不锈钢材料在西沙海洋大气环境中的腐蚀行为，通过这个加速腐蚀试验可以针对304不锈钢材料在该地区的大气腐蚀行为进行一定程度的预测。

关键词 ：不锈钢, 大气暴露, 加速腐蚀, 相关性

Abstract：

According to the typical tropical marine atmospheric corrosion features in Xisha area and on the base of the equivalent calculation, a laboratory-accelerated corrosion method was conducted, and the dynamic characteristics, mechanism of corrosion, corrosion products and indoor/outdoor correlation of the 304 stainless steel during the outdoor and indoor accelerated corrosion was also studied. The results show that, to some extent, the uv/cycle wet-dry synergistic accelerated corrosion test can simulate tropical marine atmospheric corrosion behavior of 304 stainless steel, and the corrosion behaviour of stainless steel in the tropical marine atmospheric environments can be predicted by the synergistic accelerated corrosion test.

收稿日期: 2012-06-28

ZTFLH:

TG174.2

基金资助:

先进超高强度不锈钢钝化膜稳定性机器主控机制研究;大气环境中材料薄液膜腐蚀的电化学基础理论研究

通讯作者: 骆鸿

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	骆鸿李晓刚董超芳肖葵
44.8K

引用本文:

骆鸿李晓刚董超芳肖葵. 304不锈钢在热带海洋大气下暴露试验和加速腐蚀试验研究[J]. 中国腐蚀与防护学报, .
xiaogang li. The research of 304 stainless steel in the tropical marine atmosphere exposure and the accelerated corrosion test. Journal of Chinese Society for Corrosion and protection, 0, 0(0): 0-0.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y0/V0/I0/0

[1]H.E. Button,D.W. Simm. .The influence of particulate matter on the corrosion behaviour of type 316 stainless steel[J].Anti-Corrosion methods,1985,32((6)):8-10

[2]K. E. Johnson.Role of inclusion in the atmospheric pitting of stainless steels[J].British Corrosion Journal,1980,15(3):123-127

[3]K.E.Johnson.Airborne contaminants and the pitting of stainless steels in the atmosphere[J].Corrosion Science,1982,22(3):175-191

[4]陈鸿川,于国才,王振尧.常用材料大气暴露与室内加速试验相关性研究[J].腐蚀科学与防护技术,1991,3(3):34-

[5]蔡健平,刘明,罗振华,等.航空铝合金大气腐蚀加速试验研究[J].中国腐蚀与防护学报,2005,25(5):262-265

[6] ASTM G46.Standard Guide for Examination and Evaluation of Pitting Corrosion[J].American,Society for Testing and Materials,Philadelphia,1994,:-

[7]穆志韬,柳文林,于战樵.飞机服役环境当量加速腐蚀折算方法研究[J].海军航空工程学院学报,2007,22 (3):301-304

[8] 刘元海，任三元.典型海洋大气环境当量加速试验环境谱研究[J].装备环境工程,2011,8(1):48-51

[9] K.Asami,K. Hashimoto. Importance of initial surface film in the degradation of stainless steels by atmospheric exposure[J].Corrosion Science,2003,45:2263-2283

[10]N.Azzerri.Ageing of passive surfaces of stainless steels in an urban-industry atmosphere[J].Corrosion Science,1982,22(9):867-876

[11] L.J. Oblonsky,T.M. Devine.Corrosion of Carbon Steels in CO2-Saturated Brine. A Surface Enhanced Raman Spectroscopic Study[J].Journal of the Electrochemical Society,1997,144:1252-1260

[12]Ph.Colomban,S.Cherifi,G.Despert,.Raman identification of corrosion products on automotive galvanized steel sheets[J].Journal of Raman Spectroscopy,2008,39:881-886

[1]	陈昊, 樊志彬, 陈志坚, 周学杰, 郑鹏华, 吴军. Cl^-与HSO₃^-对建筑用439不锈钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2022, 42(3): 493-500.
[2]	徐迪, 杨小佳, 李清, 程学群, 李晓刚. 材料大气环境腐蚀试验方法与评价技术进展[J]. 中国腐蚀与防护学报, 2022, 42(3): 447-457.
[3]	陈志坚, 周学杰, 陈昊. 高速列车铆接件中6A01铝合金腐蚀行为研究[J]. 中国腐蚀与防护学报, 2022, 42(3): 507-512.
[4]	张泽群, 陈质彬, 董其娟, 邬聪, 李宗欣, 王禾祖, 吴飞, 张博威, 吴俊升. 低合金钢、不锈钢和铝镁合金在模拟深海环境中的电偶腐蚀行为研究[J]. 中国腐蚀与防护学报, 2022, 42(3): 417-424.
[5]	伊璞, 侯利锋, 杜华云, 刘笑达, 贾建文, 李阳, 张威, 徐芳泓, 卫英慧. 新型奥氏体不锈钢高温NaCl腐蚀行为研究[J]. 中国腐蚀与防护学报, 2022, 42(2): 288-294.
[6]	丁奕, 王力伟, 刘德运, 王昕. 低合金钢与双相不锈钢异种金属焊接接头组织和性能的研究[J]. 中国腐蚀与防护学报, 2022, 42(2): 295-300.
[7]	苏娜, 叶梦颖, 李建民, 高荣杰. ZIF-8/TiO₂纳米复合材料的制备及光生阴极保护性能[J]. 中国腐蚀与防护学报, 2022, 42(2): 267-273.
[8]	王淇萱, 吕文生, 杨鹏, 诸利一, 廖文景, 朱远乐. 尾矿库埋入式传感器不锈钢外壳腐蚀研究[J]. 中国腐蚀与防护学报, 2022, 42(2): 331-337.
[9]	尹阳阳, 刘建峰, 缪克基, 王婷, 宁锴, 潘卫国, 袁斌霞, 尹诗斌. SO₄^2-对不锈钢在含Cl^-溶液中腐蚀影响的研究进展[J]. 中国腐蚀与防护学报, 2022, 42(1): 34-38.
[10]	程琪栋, 王燕华. 表面划痕对304不锈钢液滴腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2022, 42(1): 99-105.
[11]	张文丽, 张振龙, 吴兆亮, 韩思柯, 崔中雨. 温度对316L不锈钢在油田污水中点蚀行为的影响研究[J]. 中国腐蚀与防护学报, 2022, 42(1): 143-148.
[12]	雷哲缘, 汪毅聪, 胡骞, 黄峰, 刘静. 组织配分对2002双相不锈钢点蚀萌生及扩展的影响[J]. 中国腐蚀与防护学报, 2021, 41(6): 837-842.
[13]	安易强, 王昕, 崔中雨. 硝酸钝化对304不锈钢在模拟混凝土孔隙液中点蚀的临界Cl^-浓度的影响[J]. 中国腐蚀与防护学报, 2021, 41(6): 804-810.
[14]	郑世恩, 潘应君, 张恒, 柯德庆, 杨岭, 朱星宇. 304不锈钢表面硼化物熔覆层的耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(6): 843-848.
[15]	孙宝壮, 周霄骋, 李晓荣, 孙玮潞, 刘子瑞, 王玉花, 胡洋, 刘智勇. 不同组织的316L不锈钢在NH₄Cl环境下应力腐蚀行为与机理[J]. 中国腐蚀与防护学报, 2021, 41(6): 811-818.

Viewed

Full text

Abstract

Cited

Shared

Discussed