| EFFECTS OF MECHANOCHEMISTRY TO THE PITTING BEHAVIOUR OF LY12CZ ALUMINUM ALLOY |
| ;;;; |
|
Cite this article:
. EFFECTS OF MECHANOCHEMISTRY TO THE PITTING BEHAVIOUR OF LY12CZ ALUMINUM ALLOY. J Chin Soc Corr Pro, 2007, 27(4): 228-232 .
|
|
|
Abstract Electrochemical measurement techniques are applied to investigate the effect of applied stress on free corrosion potential，breakdown potential and protection potential of LY12CZ in 3% NaCl.Meanwhile pit propaga－tion rate(PPR)-potential curve technique and potential scanning techniques and micro measurement technique are applied to study the influence of applied stress on the real pit propagation rate of LY12CZ under preselected po－tential.The results show that when stressed， free corrosion potential，breakdown potential and protection potential of LY12CZ all move negatively，the movement extent depend on the stress.the pitting current density also increase with the increment of stress.The results show that mechanochemical effect can greatly enhance the pitting sensi－tivity of LY12CZ aluminum alloy.
|
|
Received: 28 February 2006
|
|
|
[1]GutmanЭМ.Mechanochemistry and Corrosion Prevection of Met-als[M].Peking:Science Publication,1989(Э.М.古特曼.金属力学化学与腐蚀防护[M].北京:科学出版社,1989)
[2]Bonora P L,Andrei M,Eliezer A.Corrosion hehavior ofstressed mag-nesiumalloys[J].Corros.Sci.,2002,44:729-749
[3]Wang Z F,Li J.Effects of strain amplitude and strain rate to cor-rosion acceleration of deformation[J].Acta Metall.Sin.,1994,30:213-217(王政富,李劲.应变幅与应变速率在形变加速腐蚀过程中的作用[J].金属学报,1994,30:213-217)
[4]Wang J Q.Research on the interaction of deformation and electro-chemistry in corrosion fatigue[D].Shenyang:Ph.D dissertation of the Institute of Metal Research,Chinese Science Academy,1995(王俭秋.腐蚀疲劳过程中形变与电化学交互作用研究[D].沈阳:中国科学院金属腐蚀与防护研究所博士学位论文,1995)
[5]Wang J R,Zhu L Q,Rao S X.Strain electrode of A3steel under elastic deformation[J].J.Chin.Soc.Corros.Prot.,2005,25(4):226-231(王景茹,朱立群,饶思贤.A3钢在弹性形变范围内的应变电极行为[J].中国腐蚀与防护学报,2005,25(4):226-231)
[6]Gutman E M,Solovioff G,Eliezer D.The mechanochemical behav-ior of type316L stainless steel[J].Corros.Sci.,1996,38(7):1141-1145
[7]He J P,Fan W X,Yuan Q M.Study on corrosion properties of a-luminum alloys at low strain rate[J].J.Chin.Soc.Corros.Prot.,2003,23(1):17-20(何建平,樊蔚勋,袁庆铭,慢应变速率下铝合金的腐蚀行为[J].中国腐蚀与防护学报,2003,23(1):17-20)
[8]Iwanaga Hiroyuki,Oki Takeo.Effect of applied stress on anodic polarization behavior and pitting corrosion of stainless steel[J].J.Soc.Mater.Sci.,Japan/Zairyo1981,30(331):394-400
[9]France JR W D.Effect of stress and plastic deformation on the corrosion of steel[J].The Fourth International Congress on Metal-lic Corrosion,The Netherland,1970,26(5):189-199
[10]Saito Koichi,Kuniya Jiro.Mechanochemical model to predict stress corrosion crack growth of stainless steel in high temperature water[J].Corros.Sci.,2001,43:1751-1766
[11]Kuwano Saburou,Oki Takeo.Effect of applied stress on SCC susceptibility and polarization behavior of sus316type stainless steel[J].Japan/Zairyo,1982,31(347):828-833
[12]Magnin T.Advances in Corrosion-Deformation Interactions[M].Switzerland:Trans Tech Publications Ltd.,1996
[13]Research Techniques ofCorrosion on Metals[M].Changsha:Teach-ingMaterial of Hunan University,1997,121-122(金属腐蚀研究方法[M].长沙:湖南大学教材,1997,121-122) |
| No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|