CHLORIDE PERMEABILITY TEST ON CONCRETE

Linhua Jiang

河海大学材料科学与工程系

Download:

PDF(154KB)
Export: BibTeX | EndNote (RIS)

Abstract Three methods for measuring the chloride ion permeability were used,a nd the corresponding results were compared.The methods used were chloride perme ability test (AASHTO T227 and ASTM C1202),steady-state migration test and condu ctivity test.The concrete used in this paper included the control Portland ceme nt concrete,lightweight concrete and the concrete containing fly ash,slag,sil ica fume,metakaolin and rice husk ash.Test results indicate that the resistanc e of concrete to chloride ion penetration increases with the decrease of water-c ement ratio.Fly ash and slag can increase the resistance of concrete to chlorid e ion penetration,and silica fume,metakaolin,rice husk ash and some content s lag can increase significantly the resistance of concrete to chloride ion penetr ation.There is not a good linear relationship between the charge passed and ini tial current in the whole charge range.Three tests lead to a similar conclusion regarding the relative qualities of concretes.ASTM C1202 still can be used in many cases,and the conductivity test method appears to be better suited to the chloride permeability test.

Key words: concrete chloride ion diffusivity

Received: 29 June 2001

ZTFLH:

TG174

Corresponding Authors: Linhua Jiang

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	Linhua Jiang

Cite this article:

Linhua Jiang. CHLORIDE PERMEABILITY TEST ON CONCRETE. J Chin Soc Corr Pro, 2002, 22(6): 343-348 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2002/V22/I6/343

[1]ShiC ,etal.Effectofsupplementarycementingmaterialsonthespe cificconductivityofporesolutionanditsimplicationsontherapidchloridepermeabilitytest(AASHTOT277andASTMC1202)re sults[J].ACIMaterialsJournal,1998,95(4):389-394
[2]ZhangT ,GjrvOE .Anelectrochemicalmethodforacceleratedtestingofchloridediffusivityinconcrete[J].CementandConcreteResearch,1994,24(8):1534-1548
[3]StreicherPE ,AlexanderMG .Achlorideconductiontestforcon crete[J].CementandConcreteResearch,1995,25(6):1284-1294
[4]FeldmanRF ,etal.Investigationoftherapidchloridepermeabilitytest[J].ACIMaterialsJournal,1994,91(2):246-255
[5]FeldmanRF ,etal.Rapidchloridepermeabilitytestonblendedce mentandotherconcretes:correlationsbetweencharge,initialcur rentandconductivity[J].ConstructionandBuildingMaterials,1999,13:149-154
[6]ZhaoTJ,etal.Analternatingtestmethodforconcretepermeability[J].CementandConcreteResearch,1998,28(1):7-12

[1]	TANG Rongmao, ZHU Yichen, LIU Guangming, LIU Yongqiang, LIU Xin, PEI Feng. Gray Correlative Degree Analysis of Q235 Steel/conductive Concrete Corrosion in Three Typical Soil Environments[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[2]	WEN Yang, XIONG Lin, CHEN Wei, XUE Gang, SONG Wenxue. Chloride Penetration Resistance of Polyvinyl Alcohol Fiber Concrete under Dry and Wet Cycle in Chloride Salt Solutions[J]. 中国腐蚀与防护学报, 2020, 40(4): 381-388.
[3]	Bo DA,Hongfa YU,Haiyan MA,Zhangyu WU. Equivalent Electrical Circuits Fitting of Electrochemical Impedance Spectroscopy for Rebar Steel Corrosion of Coral Aggregate Concrete[J]. 中国腐蚀与防护学报, 2019, 39(3): 260-266.
[4]	Bo DA,Hongfa YU,Haiyan MA,Zhangyu WU. Influence of Inhibitors on Reinforced Bar Corrosion of Coral Aggregate Seawater Concrete[J]. 中国腐蚀与防护学报, 2019, 39(2): 152-159.
[5]	Yunxiang CHEN, Lijuan FENG, Jianbin CAI, Xuan WANG, Yicheng HONG, Deyuan LIN, Jianhuang ZHUANG, Huaiyu YANG. Inhibition Effect of a New Composite Organic Inhibitor on Corrosion of Steel Rebar in Simulated Concrete Solution or Inside Mortar Specimen[J]. 中国腐蚀与防护学报, 2018, 38(4): 343-350.
[6]	Xuekai TIAN, Hailong WANG, Xudong CHENG, Xiaoyan SUN. Effect of Crack Characteristics on Chloride Transport in Concrete: An Overview[J]. 中国腐蚀与防护学报, 2018, 38(4): 309-316.
[7]	Weihang MIAO,Wenbin HU,Zhiming GAO,Xiangang KONG,Ru ZHAO,Junwu TANG. Corrosion Behavior of 304SS in Simulated Pore Solution of Concrete for Use in Marine Environment[J]. 中国腐蚀与防护学报, 2016, 36(6): 543-548.
[8]	Jianchun ZHANG,Jingyang JIANG,Yang LI,Jinjie SHI,Longfei ZUO,Danqian WANG,Han MA. Passive Films Formed on Seawater Corrosion Resistant Rebar 00Cr10MoV in Simulated Concrete Pore Solutions[J]. 中国腐蚀与防护学报, 2016, 36(5): 441-449.
[9]	Jianghong MAO,Weiliang JIN,Hua ZHANG,Chen XU,Jin XIA. Technology for Enhancing Durability of Structures of Sea-sand Concrete and Its Application[J]. 中国腐蚀与防护学报, 2015, 35(6): 563-570.
[10]	Xingguo FENG,Xiangyu LU,Yu ZUO,Da CHEN. Effect of Strain on Passivation of Stainless Steel in a Simulated Concrete Pore Solution[J]. 中国腐蚀与防护学报, 2015, 35(4): 372-378.
[11]	Xudong CHENG,Lianfang SUN,Zhifeng CAO,Xingji ZHU. Cracking Process Analysis of Concrete Cover Caused by Non-uniform Corrosion[J]. 中国腐蚀与防护学报, 2015, 35(3): 257-264.
[12]	CHENG Xudong, SUN Lianfang, CAO Zhifeng, ZHU Xingji, ZHAO Lixin. Numerical Simulation of Chloride Ion Induced Corrosion of Reinforced Concrete Structures in Marine Environment[J]. 中国腐蚀与防护学报, 2015, 35(2): 144-150.
[13]	YUE Zhuwen,LI Jingpei,YANG Bo,SHAO Wei,LV Tao. Solve Chloride Ions Diffusion Problem by Separation Variable Method for Reinforced Concrete Slab in Marine Environment[J]. 中国腐蚀与防护学报, 2014, 34(1): 95-100.
[14]	DU Yali,ZHANG Junxi,JIANG Jun,YUAN Xujie,WANG Lingzhi,MA Xingchi. Corrosion Behavior of Reinforced Steel in Simulated Pore Solution with Gradual Augment of Cl^-[J]. 中国腐蚀与防护学报, 2013, 33(4): 331-338.
[15]	XU Chen,YUE Zengguo,JIN Weiliang. Research on Reinforcement Corrosion in Concrete by Using Electrochemical Frequency Modulation Technology[J]. 中国腐蚀与防护学报, 2013, 33(2): 136-140.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed