STUDY ON THERMAL SPRAYING TECHNIQUE USED FOR RESISTANCE TO WET H2S SULPHIDE STRESS CRACKING

Yiliang Zhang;Mu Wang;Yaofeng Sun

北京工业大学机电学院

Download:

PDF(137KB)
Export: BibTeX | EndNote (RIS)

Abstract Considering the urgent need for methods of resistan ce to wet H2S stress corrosion cracking (SSC) during petrochemical production ,this paper,with a view to isolate substrate from the corrosives,introduced arc spraying metallic coatings as a method resistant to SSC.Five coating products i ncluding both coatings of Al series and coatings of Fe-Cr series,which are made from self-developed cored wires,were designed.A series of tests where variables such as bond adhesion tests,hydrogen permeation tests,electrochemical tests and stress corrosion tests were carried out in order to check the performance of SSC .The test results of all kinds of coatings were compared with each other,a kind of most protective coating termed ZH4 containing Al+Al2O3+RE was obtained.I n addition,the protective mechanism of coatings resistance to SSC was discussed. 

Key words: wet H2S stress corrosion cracking thermal spraying c oating cored wire

Received: 20 November 2001

ZTFLH:

TG174

Corresponding Authors: Yiliang Zhang E-mail: zhangyil@bjut.edu.cn

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	Yiliang Zhang
	Mu Wang
	Yaofeng Sun

Cite this article:

Yiliang Zhang; Mu Wang; Yaofeng Sun. STUDY ON THERMAL SPRAYING TECHNIQUE USED FOR RESISTANCE TO WET H2S SULPHIDE STRESS CRACKING. J Chin Soc Corr Pro, 2003, 23(4): 243-247 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2003/V23/I4/243

[1]ZhangYiliang,YaoXimeng.Onsulphidestresscrackingofsteelusedinpressurevessels[J].PressureVesselTechnology,1998,15(1):30-35.(张亦良.姚希梦.压力容器用钢的硫化氢应力腐蚀[J].压力容器,1998,15(1):30-35)
[2]IwonaSmuga-Otto.Developingamethodologyforperformancee valuationofmetallicthermalspraycoatingsforoilandgasindustryservice[J].MaterialsPerformance,1998,37(7):34-40
[3]TsaiSY ,ShihHC .Theuseofthermal-spraycoatingsforpre ventingwetH2ScrackinginHSLAsteelplates[J].CorrosionPre vention&Control,April1997,42-48
[4]BaronJJ ,HayMG ,etal.ResultsoffieldapplicationandlaboratorytestingofthermalsprayUNSN10276coatingforsouraminevessels[A].Corrosion/98[C].Houston:NACE ,1998,512
[5]GaoLimin,LiGuoxing.TheapplicationofthermalsprayZn-Alcoatingforcorrosionprotectioninoiltank[J].StoreandTrans portationofOil&Gas,1997,16(11):21-22(高莉敏,李国兴.热喷涂锌铝覆盖层在油罐防腐中的应用[J].油气储运,1997,16(11):21-22)
[6]Themeasurementofbondadhesionstrengthforthermalspraycoat ing[S].GB8642-88(热喷涂层结合强度的测定[S].GB8642-88)
[7]Theconstantloadtensiletestmethodofmetalsforresistancetosul phidestresscorrosioncracking[S].GB4157-84(金属抗硫化氢应力腐蚀开裂恒负荷拉伸试验方法[S].GB4157-84)

[1]	HUANG Peng, GAO Rongjie, LIU Wenbin, YIN Xubao. Fabrication of Superamphiphobic Surface for Nickel-plate on Pipeline Steel by Salt Solution Etching and Its Anti-corrosion Properties[J]. 中国腐蚀与防护学报, 2021, 41(1): 96-100.
[2]	DAI Ting, GU Yanhong, GAO Hui, LIU Kailong, XIE Xiaohui, JIAO Xiangdong. Electrochemical Performance of Underwater Friction Stud Welding Joint in CO₂ Saturated NaCl Solution[J]. 中国腐蚀与防护学报, 2021, 41(1): 87-95.
[3]	ZUO Yong, CAO Mingpeng, SHEN Miao, YANG Xinmei. Effect of Mg on Corrosion of 316H Stainless Steel in Molten Salts MgCl₂-NaCl-KCl[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[4]	SHI Kunyu, WU Weijin, ZHANG Yi, WAN Yi, YU Chuanhao. Electrochemical Properties of Nb Coating on TC4 Substrate in Simulated Body Solution[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[5]	ZHENG Li, WANG Meiting, YU Baoyi. Research Progress of Cold Spraying Coating Technology for Mg-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[6]	WANG Yating, WANG Kexu, GAO Pengxiang, LIU Ran, ZHAO Dishun, ZHAI Jianhua, QU Guanwei. Inhibition for Zn Corrosion by Starch Grafted Copolymer[J]. 中国腐蚀与防护学报, 2021, 41(1): 131-138.
[7]	WEI Zheng, MA Baoji, LI Long, LIU Xiaofeng, LI Hui. Effect of Ultrasonic Rolling Pretreatment on Corrosion Resistance of Micro-arc Oxidation Coating of Mg-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[8]	YU Hongfei, SHAO Bo, ZHANG Yue, YANG Yange. Preparation and Properties of Zr-based Conversion Coating on 2A12 Al-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[9]	. Investigation of Inhibition Effect of Brainea insignis Extractive against Carbon Steel Corrosion in HCl Solution[J]. 中国腐蚀与防护学报, 0, (): 0-0.
[10]	. Study of long-term corrosion resistance of plasma sprayed FeCrMoCBY Fe-based amorphous coating[J]. 中国腐蚀与防护学报, 0, (): 0-0.
[11]	. Hot corrosion behavior of Gd2(Zr1-xCex)2O7 thermal barrier coating ceramics exposed to CMAS[J]. 中国腐蚀与防护学报, 0, (): 0-0.
[12]	YUE Liangliang, MA Baoji. Effect of Ultrasonic Surface Rolling Process on Corrosion Behavior of AZ31B Mg-alloy[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[13]	SUN Haijing, QIN Ming, LI Lin. Performance of Al-Zn-In-Mg-Ti Sacrificial Anode in Simulated Low Dissolved Oxygen Deep Water Environment[J]. 中国腐蚀与防护学报, 2020, 40(6): 508-516.
[14]	ZHANG Hao, DU Nan, ZHOU Wenjie, WANG Shuaixing, ZHAO Qing. Effect of Fe³⁺ on Pitting Corrosion of Stainless Steel in Simulated Seawater[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[15]	LU Shuang, REN Zhengbo, XIE Jinyin, LIU Lin. Investigation of Corrosion Inhitibion Behavior of 2-aminobenzothiazole and Benzotriazole on Copper Surface[J]. 中国腐蚀与防护学报, 2020, 40(6): 577-584.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed