RECENT ADVANCES AND PROSPECT OF GALVANIC CORROSION IN MARINE ENVIRONMENT

J Chin Soc Corr Pro

2010, Vol. 30

Issue (5): 416-420 DOI:

Review

Current Issue | Archive | Adv Search

RECENT ADVANCES AND PROSPECT OF GALVANIC CORROSION IN MARINE ENVIRONMENT

WANG Chunli^1,2, WU Jianhua^1,2, LI Qingfen³

1. College of Materials Science and Chemical Engineering, Harbin Engineering University, Harbin 150001
2. State Key Laboratory for Marine Corrosion and Protection, Luoyang Ship Materials Research Institute, Qingdao 266071
3. College of Mechanical and Electrical Engineering, Harbin Engineering University, Harbin 150001

Download:

PDF(499KB)
Export: BibTeX | EndNote (RIS)

Abstract This paper reviewed the status of the recent researches on galvanic corrosion in marine environment in the fields of bimetal coupling system and multimetal coupling system. Corrosion prediction model of galvanic corrosion is briefly introduced, and progress in research on factor of galvanic corrosion such as galvanic potential, cathode/anode area ratio and temperature is discussed in more detail. Problems existed were summarized and the future development trend was outlined in the researches field.

Key words: marine environment galvanic corrosion bimetal coupling system multimetal coupling system influence factor model

Received: 28 April 2009

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	YU Chun-Li
	WU Jian-Hua

Cite this article:

WANG Chunli, WU Jianhua, LI Qingfen. RECENT ADVANCES AND PROSPECT OF GALVANIC CORROSION IN MARINE ENVIRONMENT. J Chin Soc Corr Pro, 2010, 30(5): 416-420.

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2010/V30/I5/416

[1] Wei B M. Theory and Application of Metal Corrosion [M]. Beijing: Chemical Industry Press, 1984: 142-143 (魏宝明. 金属腐蚀理论及应用 [M]. 北京: 化学工业出版社, 1984: 142-143) [2] Zhu X R, Wang X R. Corrosion and Protection of Metals in Marine Environment [M]. Beijing: National Defence Industry Publishing House, 1999: 57-58 (朱相荣, 王相润. 金属材料的海洋腐蚀与防护 [M]. 北京: 国防工业出版社, 1999: 57-58) [3] Cao C N. Principles of Electrochemistry of Corrosion [M]. Beijing: Chemical Industry Press, 2004: 40-41 (曹楚南. 腐蚀电化学原理 [M]. 北京: 化学工业出版社, 2004: 40-41) [4] Zhu X R, Huang G Q. Research of contact corrosion of metallic materials in seawater [J]. Mar. Sci., 1994, 6: 55-59 (朱相荣, 黄桂桥. 金属材料在海水中的接触腐蚀研究 [J]. 海洋科学, 1994, 6: 55-59) [5] Schumacher M. Seawater Corrosion Handbook [M]. USA: Noyes Data Corporation, NJ, 1979: 2-16 [6] Zhao M Q, Lei A L. Corrosion and Its Protection of Metal [M]. Beijing: National Defense Industry Press, 2002: 98-102 (赵麦群, 雷阿丽. 金属的腐蚀与防护 [M]. 北京: 国防工业出版社, 2002: 98-102) [7] Zahran R R, Sedahmed G H. Galvanic corrosion of zinc in turbulently moving containing drag reducing polymers [J]. Mater.Lett., 1997: 29-33 [8] Zhang Y C, Wu Y S, Zhang J. Galvanic corrosion of rusty cast iron and 304 stainless steel [J]. Corros.Sci. Prot. Technol., 2001: 13(2): 66-70 (张艳成, 吴荫顺, 张健. 带锈铸铁与304不锈钢的电偶腐蚀 [J]. 腐蚀科学与防护技术, 2001: 13(2): 66-70) [9] Mansfeld F. Area relationships in galvanic corrosion [J].Corrosion, 1971, 27(10): 436-442 [10] Huang G Q, Yu C J, Li L S. Study on galvanic corrosion of steel couples in seawater [J]. J. Chin. Soc.Corros. Prot., 2001, 21(1): 46-53 (黄桂桥, 郁春娟, 李兰生. 海水中钢的电偶腐蚀研究 [J]. 中国腐蚀与防护学报, 2001, 21(1): 46-53) [11] Du M, Guo Q K, Zhou C J. Galvanic corrosion of carbon steel/titanium and carbon steel/titanium/naval brass in seawater [J]. J. Chin. Soc. Corros. Prot., 2006, 26(5): 263-266 (杜敏, 郭庆锟, 周传静. 碳钢/Ti和碳钢/Ti/海军黄铜在海水中电偶腐蚀的研究 [J]. 中国腐蚀与防护学报, 2006, 26(5): 263-266) [12] Li S Y, Chen W. Galvanic coupling behavior on carbon steel/red copper in NaCl media [J].Corros. Sci. Prot. Technol., 2000, 12(5): 300-302 (李淑英, 陈玮. 碳钢/紫铜在NaCl介质中的电偶行为 [J]. 腐蚀科学与防护技术, 2000, 12(5): 300-302) [13] Blasco-Tamarit E, Igual-Munoz A, Garcia J Anton. Effect of temperature on the galvanic corrosion of a high alloyed austenitic stainless steel in its welded and non-welded condition in LiBr solutions [J]. Corros. Sci., 2007, 49: 4472-4490 [14] Blasco-Tamarit E, Igual-Munoz A, Garcia J Anton. Comparison between open circuit and imposed potential measurements to evaluate the effect of temperature on galvanic corrosion of the pair alloy 31-welded alloy 31 in LiBr solutions [J]. Corros. Sci., 2008, 50: 3590-3598 [15] Varela F E, Kurata Y, Sanada N. The influence of temperature on the galvanic corrosion of a cast iron-stainless steel couple (prediction by boundary element method) [J]. Corros. Sci., 1997, 39(4): 775-788 [16] Shalaby L A. Galvanic coupling of Ti with Cu and Al alloys in chloride media [J]. Corros. Sci., 1971, 11(10): 767-778 [17] Liu D. Research on galvanic corrosion and protective measures of shipbuilding material [D]. Harbin：Harbin Engineering University, 2002 (刘冬. 二氧化碳环境中缓蚀剂抑制电偶腐蚀机理研究 [D]. 哈尔滨: 哈尔滨工程大学, 2002) [18] Zhu X R, Dai M A, Cheng Z J, et al. Corrosion behaviour of metallic materials in high velocity seawater [J]. J. Chin. Soc.Corros. Prot., 1992, 12(2): 173-179 (朱相荣, 戴明安, 陈振进等, 高流速海水中金属材料的腐蚀行为 [J]. 中国腐蚀与防护学报. 1992, 12(2): 173-179) [19] Dai M A, Zhang Y, Yin Z A, et al. Dynamics characters of galvanic corrosion in high velocity seawater [J]. Corros. Sci. Prot. Technol., 1992, 4(3): 209-211 (戴明安, 张英, 殷正安等. 流动海水中电偶腐蚀动力学规律 [J]. 腐蚀科学与防护技术. 1992, 4(3): 209-211) [20] Zhang Y, Dai M A. Galvanic corrosion of ship-building steel couple with low potential-difference in seawater [J]. J. Chin.Soc. Corros. Prot., 1993, 13(1): 86-90 (张英, 戴明安. 海水中舰船钢低电位差电偶的腐蚀 [J]. 中国腐蚀与防护学报, 1993, 13(1): 86-90) [21] Arya C, Vassie P R W. Influence of cathode-to-anode area ratio and separation distance on galvanic corrosion currents of steel in concrete containing chlorides [J]. Cem. Concr.Res., 1995, 25(5): 989-998 [22] Song G L，Johannesson B，Hapugoda S，et al. Galvanic corrosion of magnesium alloy AZ91D in contact with an aluminum alloy，steel and zinc [J]. Corros.Sci., 2004, 46: 955-977 [23] Zhao H L. Galvanic corrosion research of production tubing production casing and Packer materials in Packer fluid [D]. Chengdu: Sichuan University, 2007 (赵华莱. 油套管及封隔器用钢在封隔液环境下的电偶腐蚀行为研究 [D]. 成都: 四川大学, 2007) [24] Fu J W, Chan S K. Finite element modeling of galvanic corrosion during chemical cleaning of Westinghouse series 51 steam generator [J]. Math Modell, 1987, 8: 289-294 [25] Tahara A, Kodama T. Potential distribution measurement in galvanic corrosion of Zn/Fe couple by means of Kelvin probe [J]. Corros. Sci., 2000, 42: 655-673 [26] Crump T. A Brief History of Science-As Seen through the Development of Scientific Instruments [M]. Robinson, London, 2002 [27] Aoki S, Kishimoto K. Prediction of galvanic corrosion rates by the boundary element method [J]. Math. Comput. Modell., 1991, 15(3): 11-22 [28] Varela F E. The influence of temperature on the galvanic corrosion of a cast iron-stainless steel couple(prediction by boundary element method) [J]. Corros. Sci., 1997, 39: 775-788 [29] Li Y M. Application of boundary element method to coupling galvanic corrosion [D]. Wuhan: Huazhong University of Science and Technology, 2004 　　 (李亚民. 边界元数值方法在双金属电偶腐蚀中的应用 [D]. 武汉: 华中科技大学, 2004) [30] Zhang C, Xu C B. A localized A. C. impedance scanning technique and study of metallic galvanic corrosion [J]. J.Chin. Soc. Corros. Prot., 1989, 9(2): 137-143 (张春, 许川壁. 局部交流阻抗扫描技术对金属电偶腐蚀的研究 [J]. 中国腐蚀与防护学报. 1989, 9(2): 137-143) [31] Akid R, Mils D J. A comparison between conventional macroscopic and novel microscopic scanning electrochemical methods to evaluate galvanic corrosion [J]. Corros.Sci., 2001, 43: 1203-1216 [32] El-moneim A A, Gebert A.Electrochemical characterization of galvanically coupled single phases and nanocrystalline NdFeB-based magnets in NaCl solutions [J].J. Appl. Electrochem., 2003, 33: 795-805

[1]	LIU Yang, WU Jinyi, YAN Xiaoyu, CHAI Ke. *Effect of Bacillus flexus* on Degradation of Polyurethane Varnish Coating in Marine Environment**[J]. 中国腐蚀与防护学报, 2021, 41(1): 36-42.
[2]	DING Qingmiao, QIN Yongxiang, CUI Yanyu. Galvanic Corrosion of Aircraft Components in Atmospheric Environment[J]. 中国腐蚀与防护学报, 2020, 40(5): 455-462.
[3]	YI Hongwei, HU Huihui, CHEN Changfeng, JIA Xiaolan, HU Lihua. Corrosion Behavior and Corrosion Inhibition of Dissimilar Metal Welds for X65 Steel in CO₂-containing Environment[J]. 中国腐蚀与防护学报, 2020, 40(2): 96-104.
[4]	BAI Miaomiao, BAI Ziheng, JIANG Li, ZHANG Dongjiu, YAO Qiong, WEI Dan, DONG Chaofang, XIAO Kui. Corrosion Behavior of H62 Brass Alloy/TC4 Titanium Alloy Welded Specimens[J]. 中国腐蚀与防护学报, 2020, 40(2): 159-166.
[5]	FENG Yali,BAI Ziheng,CHEN Lihong,WEI Dan,ZHANG Dongjiu,YAO Qiong,WU Junsheng,DONG Chaofang,XIAO Kui. Correlation of Indoor Accelerated Corrosion with Outdoor Exposure for Corten-A Weathering Steel in Polluted Marine Atmospheric Environments[J]. 中国腐蚀与防护学报, 2019, 39(6): 519-526.
[6]	HUANG Chen,HUANG Feng,ZHANG Yu,LIU Haixia,LIU Jing. Galvanic Corrosion Behavior for Weld Joint of High Strength Weathering Steel[J]. 中国腐蚀与防护学报, 2019, 39(6): 527-535.
[7]	Peichang DENG, Quanbing LIU, Ziyun LI, Gui WANG, Jiezhen HU, Xie WANG. Corrosion Behavior of X70 Pipeline Steel in the Tropical Juncture Area of Seawater-Sea Mud[J]. 中国腐蚀与防护学报, 2018, 38(5): 415-423.
[8]	Zhenhua WANG, Yang BAI, Xiao MA, Shaohua XING. Numerical Simulation of Galvanic Corrosion for Couple of Ti-alloy with Cu-alloy in Seawaters[J]. 中国腐蚀与防护学报, 2018, 38(4): 403-408.
[9]	Yukun WANG, Jing LIU, Qian HU, Feng HUANG. Effect of S^2- on Corrosion Behavior of A710 Steel in NaCl Solution[J]. 中国腐蚀与防护学报, 2018, 38(3): 233-240.
[10]	Wanjun PENG, Jiheng DING, Hao CHEN, Haibin YU. Corrosion Inhibition of Bio-based Inhibitor Furfuryl Glycidyl Ether[J]. 中国腐蚀与防护学报, 2018, 38(3): 303-308.
[11]	Sai YE, Moradi Masoumeh, Zhenlun SONG, Fangqin HU, Zhaohui SHUN, Jianping LONG. Inhibition Effect of Pseudoalteromonas Piscicida on Corrosion of Q235 Carbon Steel in Simulated Flowing Seawater[J]. 中国腐蚀与防护学报, 2018, 38(2): 174-182.
[12]	Guofu OU, Lulu ZHAO, Kai WANG, Kuanxin WANG, Haozhe JIN. Dew-Point Corrosion Behavior of 10^# Carbon Steel inHCl-H₂O Environment[J]. 中国腐蚀与防护学报, 2018, 38(1): 33-38.
[13]	Jia WANG, Mengyang JIA, Zhaohui YANG, Bing HAN. On Completeness of EIS Equivalent Circuit Analysis for Electrochemical Corrosion Process[J]. 中国腐蚀与防护学报, 2017, 37(6): 479-486.
[14]	Yanjie LIU,Zhenyao WANG,Binbin WANG,Yan CAO,Yang HUO,Wei KE. Mechanism of Galvanic Corrosion of Coupled 2024 Al-alloy and 316L Stainless Steel Beneath a Thin Electrolyte Film Studied by Real-time Monitoring Technologies[J]. 中国腐蚀与防护学报, 2017, 37(3): 261-266.
[15]	Xin ZHAO,Yulong HU,Fu DONG,Xiaodong ZHANG,Zhiqiao WANG. Effect of Moistened Electrical Insulation on Galvanic Corrosion Behavior of Dissimilar Metals[J]. 中国腐蚀与防护学报, 2017, 37(2): 175-182.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed