A Comparative Study on Sulfate Reducing Bacteria Influenced Corrosion of Copper Alloys

J Chin Soc Corr Pro

2007, Vol. 27

Issue (6): 342-347 DOI:

Research Report

Current Issue | Archive | Adv Search

A Comparative Study on Sulfate Reducing Bacteria Influenced Corrosion of Copper Alloys

;;;;

北京交通大学市政环境工程系

Download:

PDF(379KB)
Export: BibTeX | EndNote (RIS)

Abstract The growth characterization for sulfate reducing bacteria (SRB) under anaerobic condition was studied. Measurements of corrosion potential and the polarization resistance were used to investigate the electrochemical behavior of HSn-70-1AB and BFe30-1-1copper alloys in medium containing sulfate reducing bacteria. The results shows that the biological corrosion of copper alloys is closely related to growth characterization of SRB. The corrosion potential and the polarization resistance of electrode for copper alloys drastically moved toward negative direction as the SRB was in the logarithm growth stage. While both of them would slowly drop down as SRB entered into stable growth stage. Scanning electron Microscopy and X-ray diffraction were respectively used to analyze the morphology and chemical composition of the biofilm. The results showed that biofilm characterization formed on the copper alloys were totally different.

Key words: copper alloys sulfate reducing bacteria biofilm corrosion potential polarization resistance

Received: 24 April 2006

ZTFLH:

TB304、Q93-335

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors

Cite this article:

. A Comparative Study on Sulfate Reducing Bacteria Influenced Corrosion of Copper Alloys. J Chin Soc Corr Pro, 2007, 27(6): 342-347 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2007/V27/I6/342

[1]Bremmer P J,Geesey G G,Drake B.Atomic force microscopy ex-amination of the topography of a hydrated bacterial biofilm on acopper surface[J].Curr.Microbiol.,1992,24:223-230
[2]Steele A,Goddard D T,Beech I B.Atomic force microscopy studyof the biodeterioration of stainless steel in the presence of bacteri-al biofilms[J].Inter.Biodeterior.Biodegrad.,1994,34(1):35-46
[3]Lee W,Characklis W G.Corrosion of mild steel under anaerobicbiofilm[J].Corrosion,1993,49(3):186-199
[4]Liu J,Xu L M,Zheng J S.A study on corrosion behavior underthe biofilm of sulfate-reducing bacteria on Cu-Zn alloy[J].J.Chin.Soc.Corros.and Prot.,2001,21(6):345-351(刘靖,许立铭,郑家.硫酸盐还原菌生物膜下Cu-Zn合金的腐蚀研究[J].中国腐蚀与防护学报,2001,21(6):345-351)
[5]Wang Q F,Song S Z.Progress in marine biologically influencedcorrosion study[J].J.Chin.Soc.Corros.and Prot.,2002,22(3):184-188(王庆飞,宋诗哲.金属材料海洋环境生物污损腐蚀研究进展[J].中国腐蚀与防护学报,2002,22(3):184-188)
[6]Strickland L N,Fortnum R T,Du Bose B W.A case history of mi-crobiologically influenced corrosion in the lost hills oilfield[A].Proceedings of the NACE Annual Conference,Corrosion/1996[C].California,1996
[7]Rainha V L,Fonseca I T E.Kinetic studies on the SRB influencedcorrosion of steel:a first approach[J].Corros.Sci.,1997,39(4):807-813
[8]Iveson W P.Direct evidence for the cathodic depolarization theoryof bacterial corrosion[J].Science,1996,151:986-988
[9]Liu H F,Xu L M,Zheng J S.Influence of SRB biofilm on corrosionof carbon steel[J].J.Chin.Soc.Corros.Prot.,2000,20(1):41-46(刘宏芳,许立铭,郑家.SRB生物膜与碳钢腐蚀的关系[J].中国腐蚀与防护学报,2000,20(1):41-46)
[10]Little B,Wagner P,Mansfeld F.Microbiologically influenced cor-rosion of metals and alloys[J].Int.Mater.Rev.,1991,36:253-272
[11]Wagner P,Little B.Impact of alloying on microbiologically influ-enced corrosion.a review[J].Mater.Performance,1993,32(9):65-68
[12]Gentil V.Corrosion(3rd edition)[M].Brazil:LTC-Livros Tecni-cos e Cientificos Ed.SA.,1996
[13]Donlan R M.Correlation between sulfate reducing bacterial colo-nization and metabolic activity on selected metals in a recirculat-ing cooling water system[J].Corrosion,1992,183:1-16
[14]Postgate J R.The Sulfate Reducing Bacteria[M].Cambridge:Cambridge University Press,1984
[15]Liu G Z,Wu J H.Study on sulfate reducing bacteria influencedcorrosion of 90/10 Cu/Ni alloy by dual-cell[A].National Scientif-ic Seminar on Proceeding and Application in Corrosion Electro-chemistry[C].Kunming,2000(刘光洲,吴建华.双区电解法研究B10合金的硫酸盐还原菌腐蚀[A].全国腐蚀电化学进展与应用学术研讨会论文集[C].昆明,2000)
[16]Rainha V L,Fonseca I T E.Kinetic studies on the SRB influ-enced corrosion of steel:A first approach[J].Corros.Sci.,1997,39(4):807-813
[17]Keresate Zs,Telegdi J,Beczner J,et al.The influence of bio-cides on the microbiologically influenced corrosion of mild steeland brass[J].Electrochim.Acta,1998,43(1-2):77-85
[18]Marcus P.Surface science approach of corrosion phenomena[J].Electrochim.Acta,1998,43(1-2):109-118
[19]Rahmouni K,Keddam M,Srhiri A,Takenouti H.Corrosion ofcopper in 3%Na Cl solution polluted by sulphides ions[J].Cor-ros.Sci.,2005,47:3249-3266

[1]	ZHANG Tianyi,LIU Wei,FAN Yueming,LI Shimin,DONG Baojun,BANTHUKUL Wongpat,CHOWWANONTHAPUNYA Thee. Effect of Synergistic Action of Cu/Ni on Corrosion Resistance of Low Alloy Steel in a Simulated Tropical Marine Atmosphere[J]. 中国腐蚀与防护学报, 2019, 39(6): 511-518.
[2]	DING Guoqing,LI Xiangyang,ZHANG Bo,YANG Zhaohui,HUANG Guiqiao,YANG Haiyang,LIU Kaiji. Variation of Free Corrosion Potential of Several Metallic Materials in Natural Seawater[J]. 中国腐蚀与防护学报, 2019, 39(6): 543-549.
[3]	CHEN Jiachen,WANG Zhongwei,QIAO Lijie,YAN Yu. Interaction between Friction-wear and Corrosion in Special Environment[J]. 中国腐蚀与防护学报, 2019, 39(5): 404-410.
[4]	Bo DA,Hongfa YU,Haiyan MA,Zhangyu WU. Influence of Inhibitors on Reinforced Bar Corrosion of Coral Aggregate Seawater Concrete[J]. 中国腐蚀与防护学报, 2019, 39(2): 152-159.
[5]	Meng MEI, Hongai ZHENG, Huida CHEN, Ming ZHANG, Daquan ZHANG. Effect of Sulfate Reducing Bacteria on Corrosion Behavior of Cu in Circulation Cooling Water System[J]. 中国腐蚀与防护学报, 2017, 37(6): 533-539.
[6]	Hongwei LIU,Hongfang LIU. Research Progress of Corrosion of Steels Induced by Iron Oxidizing Bacteria[J]. 中国腐蚀与防护学报, 2017, 37(3): 195-206.
[7]	Yu TENG,Xu CHEN,Chuan HE,Yichuang WANG,Bing WANG. Effect of Microstructure on Corrosion Behavior of X70 Steel in 3.5%NaCl Solution with SRB[J]. 中国腐蚀与防护学报, 2017, 37(2): 168-174.
[8]	Yalin LV,Bijuan ZHENG,Hongwei LIU,Fuping XIONG,Hongfang LIU,Yulong HU. Effect of Static Magnetic Field on Adhesion of Sulfate Reducing Bacteria Biofilms on 304 Stainless Steel[J]. 中国腐蚀与防护学报, 2016, 36(6): 652-658.
[9]	Jinheng LUO,Congmin XU,Dongping YANG. Stress Corrosion Cracking of X100 Pipeline Steel in Acid Soil Medium with SRB[J]. 中国腐蚀与防护学报, 2016, 36(4): 321-327.
[10]	Boqiang SONG,Xu CHEN,Guiyang MA,Rui LIU. Effect of SRB on Corrosion Behavior of X70 Pipeline Steel in Near-neutral pH Solution[J]. 中国腐蚀与防护学报, 2016, 36(3): 212-218.
[11]	ZHANG Fan, LIU Hongwei, CHEN Bi, LIU Hongfang. Corrosion Inhibition of Imidazoline for Carbon Steel in CO₂-saturated Artificial Sewages with Sulfate Reduction Bacteria[J]. 中国腐蚀与防护学报, 2015, 35(2): 156-162.
[12]	WANG Yongxia, XIANG Hongliang, YANG Caiping, LIU Dong. Corrosion Resistance of Copper-bearing Duplex Stainless Steel in Culture Medium without and with Bacteria[J]. 中国腐蚀与防护学报, 2014, 34(6): 558-565.
[13]	ZHOU Nianguang, ZHA Fanglin, FENG Bing, HE Tiexiang. Application of Electrochemical Frequency Modulation for Study of Q235 Steel Corrosion in NaCl Solution[J]. 中国腐蚀与防护学报, 2014, 34(5): 445-450.
[14]	NIE Yuanyuan, DUAN Jizhou, DU Min, HOU Baorong. Influence of NaN₃ on Cathodic Oxygen Reduction Induced by Microbe-assisted Catalysis on Surface of 316LSS in Seawater[J]. 中国腐蚀与防护学报, 2014, 34(4): 359-365.
[15]	HAI Zhengyin, WANG Hui, CAO Linyuan, HU Yong. Effect of Pt Deposit on Corrosion Behavior of 316LN in Simulated Primary Loop Water Environment of Pressurized Water Reactor[J]. 中国腐蚀与防护学报, 2014, 34(3): 253-256.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed