APPLICATION OF ATOMIC FORCE MICROSCOPY IN STUDY OF SULFATE-REDUCING BACTERIA TO A3 STEEL

J Chin Soc Corr Pro

2007, Vol. 27

Issue (2): 70- DOI:

Research Report

Current Issue | Archive | Adv Search

APPLICATION OF ATOMIC FORCE MICROSCOPY IN STUDY OF SULFATE-REDUCING BACTERIA TO A3 STEEL

;;;;

腐蚀与防护国防科技重点实验室

Cite this article:

. APPLICATION OF ATOMIC FORCE MICROSCOPY IN STUDY OF SULFATE-REDUCING BACTERIA TO A3 STEEL. J Chin Soc Corr Pro, 2007, 27(2): 70-.

Download:

PDF(1967KB)
Export: BibTeX | EndNote (RIS)

Abstract The morphology of sulfate- reducing bacteria (SRB),microbial biofilms，corrosion product film and corroded A3 steel have been observed by atomic force microscopy (AFM).The results of high-resolution topographical images gave the information of the size of the cell， the thickness of biofilms and corrosion product film and the pitting corrosion depth. It can be concluded that compact sulphide films were formed on the surface of A3 steel and then microbiologically attached and formed biofilms during the process of microbiologically influenced corrosion.The corrosion of A3 steel mainly presents pitting corrosion character.

Key words: atomic force microscopy sulfate- reducing bacteria biofilms corrosion product film A3 steel

Received: 26 October 2005

ZTFLH:

TG172.82

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2007/V27/I2/70

[1]Binning G,Quate C,Gerber C.Atomic force microscopy[J].Phys.Rev.Lett.,1986,56:930-935
[2]Hadley R F.Microbiological anaerobic corrosion of steel pipeline[J].Oil and Gas,1939,38(19):92-96
[3]Minchin LJ.Anaerobic corrosion[J].Coke and Gas,1956,18(12):495-504
[4]Butlin K R,Vemon W H,Whiskin L.Investigation on undergroundcorrosion[J].Water.Sanit.Eng.,1952,2:468-472
[5]Kulman F F.Microbiological corrosion of buried steel pipe[J].Cor-rosion,1953,9(1):11-18
[6]Iverson W P.Research on the mechanisms of anaerobic corrosion[J].Int.Biodeterior.Biodegrad.,2001,47(2):63-70
[7]Puekorius.Recommended Practice for Biological Analysis of WaterFlood Injestion Waters.API RP-38,1959
[8]Hou B R.Corrosion Theory and Application in Marine Environment[M].Beijing:Science Publishing House,1998,6(侯保荣.海洋腐蚀环境理论及其应用[M].北京:科学出版社,1998,6)
[9]Li X B,Wang J,Wang W.The electrochemical method of biofilmmo-nitoring in seawater[J].J.Chin.Soc.Corros.Prot.,2005,25(2):84-87(李相波,王佳,王伟.海洋环境微生物附着的电化学检测技术[J].中国腐蚀与防护学报,1992,25(2):84-87)
[10]Caldwell D E,Korber D R,Lawrence J R.Imaging of bacterial cellsby fluorescence exclusion using scanning confocal laser microscopy[J].Microb.Methods,1992,2:249-261
[11]Videla H A.Corrosion products and biofilm interactions in the in-fluenced corrosion of steel[J].Corrosion,2002,2557:1-10.
[12]Zhu X R,Wang X R.Corrosion and Protection of Metals in MarineEnvironment[M].Beijing:Defence Industry Press,1993(朱相荣,王相润.金属材料的海洋腐蚀与防护[M].北京:国防工业出版社,1993)
[13]Li C X,Kwong Yu Chan.Application of atomic force microscopy inthe study of microbiologically influenced corrosion[J].Mater.Char-act,2002,48:195-203
[14]Fang Herbert HP,Kwong Yu Chan,Li C X.Quantification of bac-terial adhesion forces using atomic force microscopy[J].J.Microbi-ol.Methods,2000,40:89-97
[15]Hctor A Videla.Comparative study of the corrosion product filmsformed in biotic and abiotic media[J].Corrosion,99,163:1-12

[1]	FENG Yuqin, GUO Tonghan, YU Weihan, WU Wei, ZHANG Daquan. Influence of Sb on Corrosion Behavior of High-strength Structural Steels Exposed to Atmosphere at East Coast Region[J]. 中国腐蚀与防护学报, 2025, 45(5): 1300-1308.
[2]	WANG Xiao, LI Ming, LIU Feng, WANG Zhongping, LI Xiangbo, LI Ningwang. Effect of Temperature on Erosion-corrosion Behavior of B10 Cu-Ni Alloy Pipe[J]. 中国腐蚀与防护学报, 2023, 43(6): 1329-1338.
[3]	XING Xuesong, FAN Baitao, ZHU Xinyu, ZHANG Junying, CHEN Changfeng. Corrosion Characteristics of P110SS Casing Steel for Ultra-deep Well in Artificial Formation Water with Low H₂S and High CO₂ Content[J]. 中国腐蚀与防护学报, 2023, 43(3): 611-618.
[4]	WANG Xiao, LIU Feng, LI Yan, ZHANG Wei, LI Xiangbo. Corrosion Behavior of B10 Cu-Ni Alloy Pipe in Static and Dynamic Seawater[J]. 中国腐蚀与防护学报, 2023, 43(1): 119-126.
[5]	WANG Tong, MENG Huimin, GE Pengfei, LI Quande, GONG Xiufang, NI Rong, JIANG Ying, GONG Xianlong, DAI Jun, LONG Bin. Electrochemical Corrosion Behavior of 2Cr-1Ni-1.2Mo-0.2V Steel in NH₄H₂PO₄ Solution[J]. 中国腐蚀与防护学报, 2022, 42(4): 551-562.
[6]	WANG Jiaming, YANG Haodong, DU Min, PENG Wenshan, CHEN Hanlin, GUO Weimin, LIN Cunguo. Corrosion of B10 Cu-Ni Alloy in Seawater Polluted by High Concentration of NH₄⁺[J]. 中国腐蚀与防护学报, 2021, 41(5): 609-616.
[7]	JIA Yizheng, ZHAO Mingjun, CHENG Shijing, WANG Baojie, WANG Shuo, SHENG Liyuan, XU Daokui. Corrosion Behavior of Mg-Zn-Y-Nd Alloy in Simulated Body Fluid[J]. 中国腐蚀与防护学报, 2019, 39(6): 463-468.
[8]	Mingyu BAO, Chengqiang REN, Jingsi HU, Bo LIU, Jiameng LI, Feng WANG, Li LIU, Xiaoyang GUO. Stress Induced Corrosion Electrochemical Behavior of Steels for Oil and Gas Pipes[J]. 中国腐蚀与防护学报, 2017, 37(6): 504-512.
[9]	Di ZHANG,Ping LIANG,Yunxia ZHANG,Yanhua SHI,Hua QIN. Effect of Corrosion Product Film Formed in Artificial Solution Simulated Soil Medium at Ku'erle Area onPitting Corrosion Behavior of X80 Pipeline Steel[J]. 中国腐蚀与防护学报, 2016, 36(4): 313-320.
[10]	LIU Bin, DUAN Jizhou, HOU Baorong. MICROBIOLOGICALLY INFLUENCED CORROSION OF 316L SS BY MARINE BIOFILMS IN SEAWATER[J]. 中国腐蚀与防护学报, 2012, 32(1): 48-53.
[11]	;. Synthesis of two Quaternary Ammonium Imidazolines and Study on their Inhibition Action and Adsorption Behaviors on A3 Steel in Hydrochloric Solution[J]. 中国腐蚀与防护学报, 2008, 28(5): 291-295 .
[12]	. The effect of the sulfate reducing bacteria biofilm on phase boundary between HSn70-1AB copper alloy and solution[J]. 中国腐蚀与防护学报, 2008, 28(5): 265-270 .
[13]	. MECHANISM OF PROTECTIVE FILM FORMATION DURING CO2 CORROSION ON X65 STEEL[J]. 中国腐蚀与防护学报, 2007, 27(6): 338-341 .
[14]	;. Influence of biofilms adsorption kinetics on the open-circuit-potential changes of passive metals in seawater[J]. 中国腐蚀与防护学报, 2006, 26(2): 65-69 .
[15]	June Qv; Xingpeng Guo. Corrosion Inhibition and Adsorption Mechanism of Dodecylamine for Copper-Nickel Alloy in NaCl Solutions[J]. 中国腐蚀与防护学报, 2006, 26(1): 48-52 .

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed