CORROSION OF STAINLESS STEELS IN TIDAL ZONE-EXPOSURE TEST FOR 16 YEARS〖ST〗〖HT〗〖WT〗〖KH1D〗

J Chin Soc Corr Pro

2002, Vol. 22

Issue (6): 330-334 DOI:

Research Report

Current Issue | Archive | Adv Search

CORROSION OF STAINLESS STEELS IN TIDAL ZONE-EXPOSURE TEST FOR 16 YEARS〖ST〗〖HT〗〖WT〗〖KH1D〗

Guiqiao Huang

青岛海洋腐蚀研究所

Download:

PDF(143KB)
Export: BibTeX | EndNote (RIS)

Abstract Corrosion results of 5 types of stainless steels ex posed to tidal zone at Qingdao,Xiamen and Yulin Sea area of China were reported. Corrosion behavior and rule of stainless steels in tidal zone was summarized.The stainless steels exposed to tidal zone were attacked by pitting and crevice cor rosion.It was found that pitting rates of stainless steels in tidal zone were bi gger during 1 to 4 years,after which the pitting rate diminished.The stainless s te el that had good pitting resistance in tidal zone possessed good resistance to c revice corrosion.Corrosion rate of stainless steels increased with going up of s eawater temperature of test sites.Increasing Cr content and adding Mo can enhanc e obviously corrosion resistance of stainless steels in tidal zone.Ni improv es corrosion resistance,but its improving effect is less.Fouling organism could cause localized corrosion of stainless steels.Effect of the fouling on corrosion of stainless steels in tidal zone was notable.

Key words: seawater corrosion stainless steel tidal zone

Received: 14 March 2001

ZTFLH:

GB172.5

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	Guiqiao Huang

Cite this article:

Guiqiao Huang. CORROSION OF STAINLESS STEELS IN TIDAL ZONE-EXPOSURE TEST FOR 16 YEARS〖ST〗〖HT〗〖WT〗〖KH1D〗. J Chin Soc Corr Pro, 2002, 22(6): 330-334 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2002/V22/I6/330

[1]SouthwellCR ,BultmanJD ,AlexanderAL .Corrosionofmetalintropicalenvironment-finalreportof16yearsexposures[J].Mate rialsPerformance,1976,15(7):7
[2]SchumacherM ,SeawaterCorrosionHandbook[M ].ParkRidge,NewJersey:NoyesDataCorporation,1979,26
[3]HuangGuiqiao.Corrosionofstainlesssteelsinmarineenvironment[J].Corrosion&Protection,1999,20(7):392(黄桂桥.不锈钢在海洋环境中的腐蚀[J].腐蚀与防护,1999,20(9):392)
[4]ChengZhuoyuan,LinZhijian,SongWensang.CorrosionbehaviorandregularityofcorrosiondataforstainlesssteelsinXiamenSeaarea[J].Corrosion&Protection,1999,20(7):303(陈卓元,林志坚,宋文桑.不锈钢在厦门海域的腐蚀行为及数据规律性研究[J].腐蚀与防护,1999,20(7):303)
[5]GB5776-86,Methodforsurfaceseawaterexposurecorrosiontestsofmetallicmaterials[S].(GB5776-86,金属材料表面海水常规暴露腐蚀试验方法[S])
[6]HuangGuiqiao,JinWeixian,HouWentai.Astudyonrelationshipbetweencorrosionresistanceandcorrosionpotentialofstainlesssteelsinseawater[J].J .ChineseSocietyforCorrosionandProtec tion,2000,20(1):35(黄桂桥,金威贤,侯文泰.不锈钢在海水中的耐蚀性与腐蚀电位的关系[J].中国腐蚀与防护学报,2000,20(1):35)

[1]	RAN Dou, MENG Huimin, LIU Xing, LI Quande, GONG Xiufang, NI Rong, JIANG Ying, GONG Xianlong, DAI Jun, LONG Bin. Effect of pH on Corrosion Behavior of 14Cr12Ni3WMoV Stainless Steel in Chlorine-containing Solutions[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[2]	ZUO Yong, CAO Mingpeng, SHEN Miao, YANG Xinmei. Effect of Mg on Corrosion of 316H Stainless Steel in Molten Salts MgCl₂-NaCl-KCl[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[3]	WANG Xintong, CHEN Xu, HAN Zhenze, LI Chengyuan, WANG Qishan. Stress Corrosion Cracking Behavior of 2205 Duplex Stainless Steel in 3.5%NaCl Solution with Sulfate Reducing Bacteria[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[4]	ZHANG Hao, DU Nan, ZHOU Wenjie, WANG Shuaixing, ZHAO Qing. Effect of Fe³⁺ on Pitting Corrosion of Stainless Steel in Simulated Seawater[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[5]	MA Mingwei, ZHAO Zhihao, JING Siwen, YU Wenfeng, GU Yien, WANG Xu, WU Ming. Corrosion Behavior of 17-4 PH Stainless Steel in Simulated Seawater Containing SRB[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[6]	ZHAI Sixin, YANG Xingyun, YANG Jilan, GU Jianfeng. Corrosion Properties of Quenching-Partitioning-Tempering Steel in Simulated Seawater[J]. 中国腐蚀与防护学报, 2020, 40(5): 398-408.
[7]	WANG Yu, WU Jiajia, ZHANG Dun. Research Progress on Corrosion of Metal Materials Caused by Dissimilatory Iron-reducing Bacteria in Seawater[J]. 中国腐蚀与防护学报, 2020, 40(5): 389-397.
[8]	ZHAO Baijie, FAN Yi, LI Zhenzhen, ZHANG Bowei, CHENG Xuequn. Crevice Corrosion Behavior of 316L Stainless Steel Paired with Four Different Materials[J]. 中国腐蚀与防护学报, 2020, 40(4): 332-341.
[9]	HU Yuting, DONG Pengfei, JIANG Li, XIAO Kui, DONG Chaofang, WU Junsheng, LI Xiaogang. Corrosion Behavior of Riveted Joints of TC4 Ti-Alloy and 316L Stainless Steel in Simulated Marine Atmosphere[J]. 中国腐蚀与防护学报, 2020, 40(2): 167-174.
[10]	QIN Yueqiang, ZUO Yong, SHEN Miao. Corrosion Inhibition of 316L Stainless Steel in FLiNaK-CrF₃/CrF₂ Redox Buffering Molten Salt System[J]. 中国腐蚀与防护学报, 2020, 40(2): 182-190.
[11]	HE Zhuang,WANG Xingping,LIU Zihan,SHENG Yaoquan,MI Mengxin,CHEN Lin,ZHANG Yan,LI Yuchun. Passivation and Pitting of 316L and HR-2 Stainless Steel in Hydrochloric Acid Liquid Membrane Environment[J]. 中国腐蚀与防护学报, 2020, 40(1): 17-24.
[12]	WU Dongcai,HAN Peide. Effects of Moderate Temperature Aging Treatment on Corrosion Resistance of SAF2304 DuplexStainless Steel[J]. 中国腐蚀与防护学报, 2020, 40(1): 51-56.
[13]	LUO Hong,GAO Shujun,XIAO Kui,DONG Chaofang,LI Xiaogang. Effect of Magnetron Sputtering Process Parameters on CrN Films on 304 Stainless Steel and TheirCorrosion Behavior[J]. 中国腐蚀与防护学报, 2019, 39(5): 423-430.
[14]	FU Anqing,ZHAO Mifeng,LI Chengzheng,BAI Yan,ZHU Wenjun,MA Lei,XIONG Maoxian,XIE Junfeng,LEI Xiaowei,LV Naixin. Effect of Laser Surface Melting on Microstructure and Performance of Super 13Cr Stainless Steel[J]. 中国腐蚀与防护学报, 2019, 39(5): 446-452.
[15]	SUN Xiaoguang,HAN Xiaohui,ZHANG Xingshuang,ZHANG Zhiyi,LI Gangqing,DONG Chaofang. Corrosion Resistance and Environmentally-friendly Chemical Passivation of Welded Joints for Ultra-low Carbon Austenitic Stainless Steel[J]. 中国腐蚀与防护学报, 2019, 39(4): 345-352.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed