镁合金阳极氧化膜在ＮａＣｌ溶液中的腐蚀行为

中国腐蚀与防护学报

2007, Vol. 27

Issue (4): 210-214

研究报告

本期目录 | 过刊浏览

镁合金阳极氧化膜在ＮａＣｌ溶液中的腐蚀行为

钱建刚;王纯;李荻

北京航空航天大学

CORROSION BEHAVIOR OF ANODIC FILM ON MAGNESIUM ALLOY IN NaCl SOLUTION

;;

北京航空航天大学

全文: PDF(357 KB)

摘要: 利用盐水浸泡实验研究了ＡＺ９１Ｄ镁合金阳极氧化膜层在３．５％ＮａＣｌ溶液中的腐蚀行为。结果表明：ＡＺ９１Ｄ镁合金阳极氧化膜层不论封闭与否，在中性ＮａＣｌ溶液中浸泡出现第一个腐蚀点后，膜层表面均很少再出现新的腐蚀点，而是原有的腐蚀点向纵、横两个方向扩展形成腐蚀坑，表面呈"树枝"状腐蚀形貌；浸泡溶液的ｐＨ值对阳极氧化膜层的耐蚀性影响很大，酸性溶液中的腐蚀速率明显大于中、碱性溶液的；随浸泡溶液温度的升高阳极氧化膜层的腐蚀速率加快。据此，提出了ＡＺ９１Ｄ镁合金阳极氧化膜层在ＮａＣｌ溶液中腐蚀过程的模型。

关键词 ：镁合金, 阳极氧化膜, 腐蚀模型, NaCl

Abstract：The corrosion behavior of anodic film on the AZ91D magnesium alloy in 3.5% NaCl aqueous solution was investigated by the saline immersion test.The results show that new corrosion points seldom occur on the surface of the said anodic film over the immersion time in 3.5% NaCl neutral aqueous solution after the first macroscopic corrosion point appeared on the anodic film whether it was sealed or not,while the previous corrosion point extends vertically and horizontally and turns into a corrosion pit which is in form of ＂dendrite＂. The pH value and temperature of the test solution affect substantially on the corrosion resistance of the anodic film. The corrosion rate in acidic solution is obviously faster than that in neutral or alkaline solutions, and the corrosion rate increases with increasing of the immersion solution temperature.A possible model about the corrosion process of the anodic film on the AZ91D magnesium alloy is therefore proposed based on the above experimental results.

Key words： magnesium alloy anodic film corrosion model NaCl

收稿日期: 2006-01-09

ZTFLH:

TG178

通讯作者: 钱建刚 E-mail: qianjg@buaa.edu.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	钱建刚
	王纯
	李荻
44.8K

引用本文:

钱建刚; 王纯; 李荻 . 镁合金阳极氧化膜在ＮａＣｌ溶液中的腐蚀行为[J]. 中国腐蚀与防护学报, 2007, 27(4): 210-214 .

链接本文:

https://www.jcscp.org/CN/Y2007/V27/I4/210

[1]Ruden T J,Albright D L.High ductility magnesium alloys in au-tomotive applications[J].Advanced Material&Processes,1994,145(6):28-32
[2]Froes F H,liezer D.The science,technology and application of magnesium[J].J.Mine Metals and Mater Soc.,1998,5(9):30-34
[3]Wang Q D,Lu Y Z,Zeng X Q.Current application of magnesium alloy in manufacturing electronic equipment[J].Material Review,2000,14(6):22-24(王渠东,吕宜振,曾小勤.镁合金在电子器材壳体中的应用[J].材料导报,2000,14(6):22-24)
[4]Qian J G,Li D,Guo B L.Surface treatment of magnesium alloy[J].Chin.J.Nonferr.Metals,2002,12(3):32-36(钱建刚,李荻,郭宝兰.镁合金的表面处理[J].中国有色金属学报,2002,12(3):32-36)
[5]Jiang B L,Zhang X F.Growth process and corrosion resistance of ceramic coatings formed by micro-arc oxidation on magnesium al-loy[J].J.Chin.Soc.Corros.Prot.,2005,25(2):97-101(蒋百灵,张先锋.镁合金微弧氧化陶瓷层的生长过程及其耐蚀性[J].中国腐蚀与防护学报,2005,25(2):97-101)
[6]Huo H W,Li Y,Wang F H.Electroless nickel plating on AZ91D magnesium alloy[J].J.Chin.Soc.Corros.Prot.,2002,22(1):14-17(霍宏伟,李瑛,王福会.AZ91D镁合金化学镀镍[J].中国腐蚀与防护学报,2002,22(1):14-17)
[7]Song G L,Andrej A,Wu X L,et al.Corrosion behaviour of AZ21,AZ501and AZ91in sodium chloride[J].Corros.Sci.,1998,40(10):1769-1791
[8]Song G L.Corrosion and protection of magnesium alloys an overview of research undertaken by CAST[J].Mater.Sci.Forum,2005,488-489:649-652
[9]Zhang Y J,Yan C W,Wang F H,et al.Study on the environmen-tally friendly anodizing of AZ91D magnesium alloy[J].Surf.Coat.Technol.,2002,161:36-43
[10]Qian J G,Li D,Wang X L,et al.Structure,composition and corrosion resistance of Mg alloy anodized film[J].Chem.l J.Chin.Univ.,2005,26(7):1338-1341(钱建刚,李荻,王学力等.镁合金阳极氧化膜的结构、成分及其耐蚀性[J].高等学校化学学报,2005,26(7):1338-1341)
[11]Qian J G,Li D,Guo B L.The study of environment-friendly processes of the anodization for magnesium alloys[J].J.Aeronau-tical Materials,2003,23(10):109-112(钱建刚,李荻,郭宝兰.环保型镁合金阳极氧化工艺研究[J].航空材料学报,2003,23(10):109-112)
[12]Song G L,Andrej A.Corrosion mechanisms of magnesium alloys[J].Advanced Eng.Mater.,1999,1(1):11-33
[13]Qian J G,Li D,Zhang F.Process of film formation by anodizing AZ91D magnesium alloy[J].Mater.Sci.Forum,2005,475-479:3905-3908
[14]Liu Z,Zhang K,Zeng X Q.Theory Basement and Application of Magnesium Alloy[M].Beijing:China Machine Press,2002,143(刘正,张奎,曾小勤.镁基轻质合金理论基础及其应用[M].北京:机械工业出版社,2002,143)
[15]Jang J X,Zhang P F,Gao M T.Metal Corrosion Theory[M].Beijing:National Defence Industry Press,1986(蒋金勋,张佩芬,高满同.金属腐蚀学[M].北京:国防工业出版社,1986)
[16]Cao C N.Corrosion Electrochemistry[M].Beijing:Chemical In-dustry Press,1994(曹楚南.腐蚀电化学[M].北京:化学工业出版社,1994)
[17]Liu Y H,Zhang P F.Corrosion Theory of Metal[M].Beijing:Aviation Industry Press,1993(刘永辉,张佩芬.金属腐蚀学原理[M].北京:航空工业出版社,1993)
[18]Huo H W,Li Y,Wang F H.Effect of chemical conversion film plus electroless nickel plating on corrosion resistance of magne-sium alloy[J].Chin.J.Nonferr.Metals,2004,14(2):267-272(霍宏伟,李瑛,王福会.化学转化膜上沉积镍对镁合金耐腐蚀性能的影响[J].中国有色金属学报,2004,14(2):267-272),

[1]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[2]	魏征, 马保吉, 李龙, 刘潇枫, 李慧. 镁合金表面超声滚压预处理对微弧氧化膜耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[3]	于浩冉, 张文丽, 崔中雨. 4种镁合金在Cl^--NH₄⁺-NO₃^-溶液体系中的腐蚀行为差异研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 553-559.
[4]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[5]	郏义征, 王保杰, 赵明君, 许道奎. 固溶处理制度对挤压态Mg-Zn-Y-Nd镁合金在模拟体液中腐蚀和析氢行为的影响规律研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 351-357.
[6]	张尧, 郭晨, 刘妍慧, 郝美娟, 成世明, 程伟丽. 挤压态Mg-2Sn-1Al-1Zn合金在模拟体液中的电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(2): 146-150.
[7]	郏义征, 赵明君, 程世婧, 王保杰, 王硕, 盛立远, 许道奎. 模拟人体体液中镁合金的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 463-468.
[8]	欧阳跃军,胡婷,王佳音,谢治辉. 镁合金表面层状双氢氧化物的电化学沉积和表征[J]. 中国腐蚀与防护学报, 2019, 39(5): 453-457.
[9]	王保杰,栾吉瑜,王士栋,许道奎. 镁合金应力腐蚀开裂行为研究进展[J]. 中国腐蚀与防护学报, 2019, 39(2): 89-95.
[10]	刘丽,于思荣. 添加Gd对AM60镁合金耐腐蚀性能的影响[J]. 中国腐蚀与防护学报, 2019, 39(2): 185-191.
[11]	曹敏, 刘莉, 余钟芬, 李瑛, 王福会. 2A02铝合金在模拟海洋大气环境中的剥蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 502-510.
[12]	樊志民, 于锦, 宋影伟, 单大勇, 韩恩厚. 镁合金点蚀的研究进展[J]. 中国腐蚀与防护学报, 2018, 38(4): 317-325.
[13]	王志虎, 张菊梅, 白力静, 张国君. AZ91镁合金表面微弧氧化与化学镀铜复合处理层的微观组织与性能[J]. 中国腐蚀与防护学报, 2018, 38(4): 391-396.
[14]	陈琳, 钟福荣, 昝金龙. 复合电解液中AZ31B镁合金的放电特性及电压滞后[J]. 中国腐蚀与防护学报, 2018, 38(2): 197-202.
[15]	崔学军, 平静. 微弧氧化及其在镁合金腐蚀防护领域的研究进展[J]. 中国腐蚀与防护学报, 2018, 38(2): 87-104.

Viewed

Full text

Abstract

Cited

Shared

Discussed