炼油厂冷却水系统硫酸盐还原菌对316L不锈钢点腐蚀的研究

胥聪敏; 张耀亨;程光旭;朱文胜

西安交通大学

Investigation of Sulfate-Reducing Bacteria on Pitting of 316L Stainless Steel in Cooling Water System for oil refinery

;

西安交通大学

全文: PDF(1572 KB)

摘要: 用开路电位、动电位扫描、电化学阻抗技术和扫描电镜等方法，研究了316L不锈钢在硫酸盐还原菌(SRB)溶液中的腐蚀电化学行为，分析了炼油厂冷却水系统微生物腐蚀的特征及机制.结果表明，在含有SRB溶液中的自腐蚀电位(Ecorr)和点蚀电位(Epit)随浸泡时间的增加而负移，极化电阻(Rp)随浸泡时间的增加而减小；在含有SRB溶液中的腐蚀速率均大于在无菌溶液中；SRB的生长代谢活动影响了316L SS表面的腐蚀过程，使不锈钢表面的钝化膜层腐蚀破坏程度增加，加速了316L SS的腐蚀.

关键词 ：硫酸盐还原菌, 316L不锈钢, 点腐蚀, 电化学行

Abstract：Microbiological induced pitting corrosion on 316L stainless steel used in water cooling system for oil refinery was analyzed,the electrochemical features on pitting of stainless steel in sulphate-reducing bacteria (SRB)media were investigated by using of open circuit potential measure、potentiodynamic scanning、electrochemical impedance spectrum (EIS)and scanning electron microscopy(SEM).With prolonging the immersion time,the corrosion potentia l and pitting potential decreased,and polarization resistance (Rp)decreased as well.The corrosion rate of 316L SS in SRB medium is larger than those in sterile medium.The experimental results showed that the metabolic activity of SRB influenced the corrosion process,increased the corrosion damage degree of the passive film,accelerated the corrosion rate of 316L SS with the increase of immersion time.

Key words： Sulphate-Reducing Bacteria ( SRB) 316L stainless steel pitting corrosion electrochemical features

收稿日期: 2005-08-29

ZTFLH:

TG172.7

通讯作者: 胥聪敏 E-mail: xucongmin@stu.xjtu.edu.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	胥聪敏
	张耀亨，程光旭，朱文胜
44.8K

引用本文:

胥聪敏; 张耀亨;程光旭;朱文胜 . 炼油厂冷却水系统硫酸盐还原菌对316L不锈钢点腐蚀的研究[J]. 中国腐蚀与防护学报, 2007, 27(1): 48-53 .
. Investigation of Sulfate-Reducing Bacteria on Pitting of 316L Stainless Steel in Cooling Water System for oil refinery. J Chin Soc Corr Pro, 2007, 27(1): 48-53 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2007/V27/I1/48

[1]Federal Highway Administration.Corrosion Cost and PreventiveStrategies in the United States[M].New York:Plenum Press,2002
[2]Adibi N.Environmentally acceptable methods control pipeline corro-sion at lower cost[J].Material Performance,1997,36(2):71-75
[3]Remy M,Bernard C,Michel W.Effect of ferrous ion availability ongrowth of a corroding SRB[J].International Biodeterioration&Bio-degradation,2001,47(3):125-131
[4]Warren P I.Research on the mechanisms of anaerobic corrosion[J].International Biodeterioration&Biodegradation,2001,47(2):63-70
[5]Hakkarainen T J.Microbiologically influenced corrosion of stainlesssteels-What is required for pitting[J].Mater.Corros.,2003,54(4):503-509
[6]Rao TS,Sariram TN,Viswanathan B.Carbon steel corrosion by ironoxidizing and sulphate reducing bacteria in a fresh water cooling sys-tem[J].Corros.Sci.,2000,42(8):1417-1431
[7]Xu C M,Zhang Y H,Cheng G X.Research status and developmenttrends of corrosion in heat exchangers on oil refineries abroad[J].Petro-Chemical Equipment,2005,34(1):41-46(胥聪敏,张耀亨,程光旭.国外炼油厂换热设备腐蚀研究现状及发展动态[J].石油化工设备,2005,34(1):41-46)
[8]Dexter S C,Duquette D J,Siebert O W,et al.Effect of natural marinebiofilms on galvanic corrosion[J].Corrosion,1991,47(4):308-316

[1]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[3]	胡玉婷, 董鹏飞, 蒋立, 肖葵, 董超芳, 吴俊升, 李晓刚. 海洋大气环境下TC4钛合金与316L不锈钢铆接件腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 167-174.
[4]	秦越强, 左勇, 申淼. FLiNaK-CrF₃/CrF₂氧化还原缓冲熔盐体系对316L不锈钢耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(2): 182-190.
[5]	陈旭, 李帅兵, 郑忠硕, 肖继博, 明男希, 何川. X70管线钢在大庆土壤环境中微生物腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 175-181.
[6]	刘志峰,朱志平,石纯,黄赵鑫. 载流法制备硫酸露点腐蚀模拟气体的试验研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 1-9.
[7]	陈旭,马炯,李鑫,吴明,宋博. 温度与SRB协同作用下X70钢在海泥模拟溶液中应力腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 477-483.
[8]	戚鹏, 万逸, 曾艳, 郑来宝, 张盾. 海洋环境中硫酸盐还原菌的快速测定方法研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 387-394.
[9]	吴堂清,周昭芬,王鑫铭,张德闯,尹付成,孙成. 微生物致裂的热力学和动力学分析[J]. 中国腐蚀与防护学报, 2019, 39(3): 227-234.
[10]	李鑫,陈旭,宋武琦,杨佳星,吴明. pH值对X70钢在海泥模拟溶液中微生物腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(6): 565-572.
[11]	偶国富, 赵露露, 王凯, 王宽心, 金浩哲. 10^#碳钢在HCl-H₂O环境中的露点腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(1): 33-38.
[12]	管方, 翟晓凡, 段继周, 侯保荣. 阴极极化对硫酸盐还原菌腐蚀影响的研究进展[J]. 中国腐蚀与防护学报, 2018, 38(1): 1-10.
[13]	于利宝, 闫茂成, 王彬彬, 舒韵, 许进, 孙成. 酸性土壤环境中Q235钢的微生物腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(1): 10-17.
[14]	周霄骋, 崔巧棋, 贾静焕, 刘智勇, 杜翠薇. Cl^-浓度对316L不锈钢在碱性NaCl/Na₂S溶液中SCC行为的影响[J]. 中国腐蚀与防护学报, 2017, 37(6): 526-532.
[15]	梅朦, 郑红艾, 陈惠达, 张鸣, 张大全. 硫酸盐还原菌对Cu在循环冷却水中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2017, 37(6): 533-539.

Viewed

Full text

Abstract

Cited

Shared

Discussed