纳米Fe－10Cr涂层电化学腐蚀行为影响研究 Ⅱ点蚀性能

孟国哲; 李瑛; 王福会

哈尔滨工程大学材料科学与化学工程学院

CORROSION BEHAVIOR OF Fe-10Cr NANOCRYSTALLINE COATINGS Ⅱ.CORROSION BEHAVIOR OF Fe-10Cr NANOCRYSTALLINE COATINGS IN ACIDIC SOLUTION WITH Cl-

;;

哈尔滨工程大学材料科学与化学工程学院

全文: PDF(1169 KB)

摘要: 利用动电位极化曲线、电化学阻抗谱图（EIS）和Mott-Schottky分析等电化学测试手段，探讨了Fe-10Cr纳米涂层在005 mol/L H2SO4+05 mol/L NaCl溶液中的腐蚀行为.研究表明，与铸态合金相比，溅射纳米涂层表面钝化膜的化学稳定性和再钝化性能明显提高；二者的钝化膜均具有p型半导体结构特征，但溅射纳米涂层表面钝化膜的载流子密度和平带电位都比较低，导致钝化膜中金属离子的传输速度较低，纳米涂层表面钝化膜的化学稳定性增强.

关键词 ：纳米晶, 晶粒尺寸, 腐蚀行为, 钝化, 钝化膜, 点

Abstract：The corrosion behavior of Fe-10Cr sputtering coating with nanoscale grain size was investigated in 0.05 mol/L H2SO4+0.5 mol/L NaCl aqueous solution using polarization curves,EIS and Mott-Schottky analysis.The results indicated that the chemical stability and repassive ability of passive film formed on Fe-10Cr nc coating was apparently improved.The passive films on both Fe-10Cr nc coating and cast alloy have p-type semiconducting behavior.The lower acceptor density and flat-band potential of the passive film in comparison with Fe-10Cr cast alloy lead to the high chemical stability and repassive ability for the passive film on the sputtering coating.

Key words： nanocystalline grain size corrosion behavior passive passive film pitting

收稿日期: 2005-07-26

ZTFLH:

TG17.1

通讯作者: 孟国哲 E-mail: mengguozhe@hrbeu.edu.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	孟国哲
	李瑛
	王福会
44.8K

引用本文:

孟国哲; 李瑛; 王福会 . 纳米Fe－10Cr涂层电化学腐蚀行为影响研究 Ⅱ点蚀性能[J]. 中国腐蚀与防护学报, 2007, 27(1): 43-47 .

链接本文:

https://www.jcscp.org/CN/Y2007/V27/I1/43

[1]Lou HY,Wang F H,Zhu S L.Oxidation formation of K38G superal-loy and its sputtered micrograined coating[J].Surf.Coat.Tech.,1994,63:105-114
[2]Wang F H.The effect of nanocrystallization on the selective oxidationand adhesion of Al2O3scales[J].Oxid.Met.,1997,48:215-224
[3]Wang F H.,Lou HY,Zhu S L.The mechanism of scale adhesion onsputtered microcrystalline CoCrAl film[J].Oxid.Met.,1996,45:39-50
[4]Wang F H.Oxidation resistance of sputtered Ni3(AlCr)nanocrystal-lized coating[J].Oxid.Met.,1997,47:247-258
[5]Intrui R B,Szklarska-Smialowska Z.Localized corrosion of nano-crystalline 304 type stainless steel films[J].Corrosion,1992,48:398-403
[6]Meng G Z,Li Y,Wang F H.Electrochemical behavior of Fe-20Crnanocrystalline coatings[J].J.Chin.Soc.Corros.Prot.,2006,26(1):11-18(孟国哲,李瑛,王福会.Fe-20Cr纲米涂层的电化学行为[J].中国腐蚀与防护学报,2006,16(1):11-18)
[7]Meng G Z,Li Y,Wang F H.Corrosion behavior of Fe-10Cr nano-crystalline coatings I.Corrosion behavior of Fe-10Cr nanocrystallinecoating in acidic solution without Cl-[J].J.Chin.Soc.Corros.Prot.,2007,27(1):35-42(孟国哲,李瑛,王福会.纳米Fe-10Cr涂层电化学腐蚀行为影响研究Ⅰ.钝化性能[J].中国腐蚀与防护学报,2007,27(1):35-42)
[8]Calinski C,Strehblow H H.ISS depth profiles of the passive layerson Fe/Cr alloys[J].J.Electrochem.Soc.,1989,126:1328-1332
[9]Hakiki N E,Boundin S,Rondot B,et al.The electronic structure ofpassive films formed on stainless steel[J].Corros.Sci.,1995,37:1809-1822
[10]Simoes A M P,Ferrira M G S,Rondot B,et al.Study of passivefilms formed on AISI 304 stainless steel by impedance measure-ments and photoelectrochemistry[J].J.Electrochem.Soc.,1990,137:82-87
[11]Sato N.Toward a more fundamental understanding of corrosionprocesses[J].Corrosion,1989,5:354-368

[1]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[2]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[3]	张浩, 杜楠, 周文杰, 王帅星, 赵晴. 模拟海水溶液中Fe³⁺对不锈钢点蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[4]	于浩冉, 张文丽, 崔中雨. 4种镁合金在Cl^--NH₄⁺-NO₃^-溶液体系中的腐蚀行为差异研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 553-559.
[5]	李琳, 陈义庆, 高鹏, 艾芳芳, 钟彬, 伞宏宇, 杨颖. 除冰盐环境下桥梁钢的耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 448-454.
[6]	戴明杰, 刘静, 黄峰, 胡骞, 李爽. 基于正交方法研究阴极保护电位波动下X100管线钢的点蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(5): 425-431.
[7]	张欣, 杨光恒, 王泽华, 曹静, 邵佳, 周泽华. 冷拉拔变形过程中含稀土铝镁合金腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 432-438.
[8]	贺三, 孙银娟, 张志浩, 成杰, 邱云鹏, 高超洋. 20#钢在含饱和CO₂的离子液体醇胺溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 309-316.
[9]	李清, 张德平, 王薇, 吴伟, 卢琳, 艾池. L80油管钢实际腐蚀状况评估及室内电化学和应力腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 317-324.
[10]	郏义征, 王保杰, 赵明君, 许道奎. 固溶处理制度对挤压态Mg-Zn-Y-Nd镁合金在模拟体液中腐蚀和析氢行为的影响规律研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 351-357.
[11]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[12]	王新华, 杨永, 陈迎春, 位凯玲. 交流电流对X100管线钢在库尔勒土壤模拟液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(3): 259-265.
[13]	胡玉婷, 董鹏飞, 蒋立, 肖葵, 董超芳, 吴俊升, 李晓刚. 海洋大气环境下TC4钛合金与316L不锈钢铆接件腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 167-174.
[14]	张尧, 郭晨, 刘妍慧, 郝美娟, 成世明, 程伟丽. 挤压态Mg-2Sn-1Al-1Zn合金在模拟体液中的电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(2): 146-150.
[15]	刘志峰,朱志平,石纯,黄赵鑫. 载流法制备硫酸露点腐蚀模拟气体的试验研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 1-9.

Viewed

Full text

Abstract

Cited

Shared

Discussed