AZ91D镁合金微弧氧化过程中的火花放电现象研究

中国腐蚀与防护学报

2006, Vol. 26

Issue (5): 267-271

研究报告

本期目录 | 过刊浏览

AZ91D镁合金微弧氧化过程中的火花放电现象研究

王燕华;王佳;张际标

中科院海洋所

SPARK DISCHARGES DURING THE MICRO-ARCOXIDATION OF AZ91D MAGNESIUM ALLOYS

;;

中科院海洋所

全文: PDF(280 KB)

摘要: 火花放电是微弧氧化处理过程中的一种代表性现象.在电火花的影响下，镁合金氧化试样的表面形貌、元素分布以及表面电位分布等都发生了显著的变化.研究发现，火花放电能够在氧化膜中留下大量的放电微孔，并且加速电极表面的氧化以及溶液中粒子在电极表面的沉积.火花放电具有明显的成膜作用，使膜层内部更加致密，放电区域的表面电位正移. 另外，氧气的存在，对于电火花的尺寸和放电的剧烈程度具有明显的促进作用.

关键词 ：火花, 微弧氧化, 镁合金, 元素分布, 电位分布

Abstract：Spark discharge is the representative phenomenon of micro-arc oxidati on (MAO) method.Accompanied with the spark discharge,the cell voltage presents oscillations within the range of several volts,and the surface morphologies,t he element distribution as well as the surface potential distributions of the an odic layer are significantly changed.It was found that spark discharges resulte d in a great deal of discharge pores in the oxide layer,accelerated the oxidati on and the deposition of electrolytic particles.Due to the melting effect of th e sparks,compact internal layer was formed underneath the outer loose layer,an d the surface potential over the spark zone was greatly enhanced.In addition,i t was found that oxygen played a key role in determining the intensity and the s ize of sparks,and abundant oxygen resulted in intensive and larger sparks.

Key words： spark micro-arc oxidation magnesium alloy element distribution potential distribution

收稿日期: 2005-06-08

ZTFLH:

TG146.2

通讯作者: 王燕华 E-mail: wangyanhua@ms.qdio.ac.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	王燕华
	王佳
	张际标
44.8K

引用本文:

王燕华; 王佳; 张际标 . AZ91D镁合金微弧氧化过程中的火花放电现象研究[J]. 中国腐蚀与防护学报, 2006, 26(5): 267-271 .

链接本文:

https://www.jcscp.org/CN/Y2006/V26/I5/267

[1]Xue W B,Lai Y C,Deng Z W,et al.The properties of coatingformed by microplasma oxidation on magnesium alloy[J].Mater.Sci.Technol.,1997,5(2):89-92(薛文彬,来永春,邓志威等.镁合金微等离子体氧化膜的特性[J].材料科学与工艺,1997,5(2):89-92)
[2]Wei Z L,Chen Q R,Guo X C,et al.Microstructure and corrosionresistance of ceramic coating on magnesium alloy[J].Mater.Prot.,2003,36(10):21-23(卫中领,陈秋荣,郭歆聪等.镁合金微弧氧化膜的微观结构及耐蚀性研究[J].材料保护,2003,36(10):21-23)
[3]Jiang B L,Zhang S F,Wu G J,et al.The study of the corrosion re-sistance of the ceramic coatings formed by micro-arc oxidation onthe Mg-based alloy[J].J.Chin.Soc.Corros.Prot.,2002,22(5):300-303(蒋百灵,张淑芬,吴国建等.镁合金微弧氧化陶瓷层耐蚀性的研究[J].中国腐蚀与防护学报,2002,22(5):300-303)
[4]Sundararajan G,Krishna L R.Mechanisms underlying the forma-tion of thick alumina coatings through the MAO coating technology[J].Surf.Coat.Technol.,2003,167(2-3):269-277
[5]Zozulin A J,Bartak D E.Anodized coatings for magnesium alloys[J].Metal Finishing,1994,92(3):39-44
[6]Krishna L R,Somaraju K R C,Sundararajan G.The tribologicalperformance of ultra-hard ceramic composite coatings obtainedthrough microarc oxidation[J].Surf.Coat.Technol.,2003,163-164:484-490
[7]Yerokhin A L,Shatrov A,Samsonov V,et al.Fatigue properties ofKeronite coatings on a magnesium alloy[J].Surf.Coat.Technol.,2004,182(1):78-84
[8]Stratmann M.The investigation of the corrosion properties of met-als,covered with adsorbed electrolyte layers-a new experimentaltechnique[J].Corros.Sci.,1987,27(8):869-872
[9]Stratmann M,Streckel H.On the atmospheric corrosion of metalswhich are covered with thin electrolyte layers—1.Verification ofthe experimental technique[J].Corros.Sci.,1990,30(6,7):681-696
[10]Blott B H,Lee T J.A two frequency vibrating capacitor method forcontact potential difference measurements[J].J.Sci.Instrum.,1969,46(2):785-788

[1]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[2]	魏征, 马保吉, 李龙, 刘潇枫, 李慧. 镁合金表面超声滚压预处理对微弧氧化膜耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[3]	于浩冉, 张文丽, 崔中雨. 4种镁合金在Cl^--NH₄⁺-NO₃^-溶液体系中的腐蚀行为差异研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 553-559.
[4]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[5]	郏义征, 王保杰, 赵明君, 许道奎. 固溶处理制度对挤压态Mg-Zn-Y-Nd镁合金在模拟体液中腐蚀和析氢行为的影响规律研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 351-357.
[6]	曹京宜, 方志刚, 陈晋辉, 陈志雄, 殷文昌, 杨延格, 张伟. 5083铝合金表面单致密微弧氧化膜的制备及其性能研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[7]	张尧, 郭晨, 刘妍慧, 郝美娟, 成世明, 程伟丽. 挤压态Mg-2Sn-1Al-1Zn合金在模拟体液中的电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(2): 146-150.
[8]	姜冬雪,付颖,张峻巍,张伟,辛丽,朱圣龙,王福会. 钛合金表面Al₂O₃陶瓷膜制备及性能研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 469-476.
[9]	郏义征, 赵明君, 程世婧, 王保杰, 王硕, 盛立远, 许道奎. 模拟人体体液中镁合金的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 463-468.
[10]	欧阳跃军,胡婷,王佳音,谢治辉. 镁合金表面层状双氢氧化物的电化学沉积和表征[J]. 中国腐蚀与防护学报, 2019, 39(5): 453-457.
[11]	刘丽,于思荣. 添加Gd对AM60镁合金耐腐蚀性能的影响[J]. 中国腐蚀与防护学报, 2019, 39(2): 185-191.
[12]	王保杰,栾吉瑜,王士栋,许道奎. 镁合金应力腐蚀开裂行为研究进展[J]. 中国腐蚀与防护学报, 2019, 39(2): 89-95.
[13]	樊志民, 于锦, 宋影伟, 单大勇, 韩恩厚. 镁合金点蚀的研究进展[J]. 中国腐蚀与防护学报, 2018, 38(4): 317-325.
[14]	王志虎, 张菊梅, 白力静, 张国君. AZ91镁合金表面微弧氧化与化学镀铜复合处理层的微观组织与性能[J]. 中国腐蚀与防护学报, 2018, 38(4): 391-396.
[15]	郝利新, 贾瑞灵, 张慧霞, 张伟, 赵婷, 翟熙伟. 7A52铝合金双丝MIG焊接头的不均匀性对其表面微弧氧化膜腐蚀防护作用的影响[J]. 中国腐蚀与防护学报, 2018, 38(3): 219-225.

Viewed

Full text

Abstract

Cited

Shared

Discussed