EPR法评价晶间腐蚀敏感性的各种判据的比较

高中平;陈范才;赵常就

湖南大学化学化工学院

COMPARING DIFFERENT CRITERIA OF EPR METHOD TO EVALUATE THE SUSCEPTIBILITY TO INTERGRANULAR CORROSION

Zhongping Gao;Fancai Chen;Changjiu Zhao

湖南大学化学化工学院

全文: PDF(146 KB)

摘要: 用电化学动电位再活化法与草酸浸蚀法研究了1Cr18Ni9Ti不锈钢的晶间腐蚀敏感性,并对动电位再活化法用于评价不锈钢晶间腐蚀敏感性的各种判据进行了综合分析.实验结果表明:各种判据与材料的敏化程度有良好的对应关系,且能灵敏定量地反映低敏化材料的晶间腐蚀敏感性的变化.各种判据中电流比ir/ia,电量比Qr/Qa的数据波动性小,重现性好;而再活化电流ir与再活化电量Qr的数据波动较大,重现性较差.电量判据(包括再活化电量Qr及电量比Qr/Qa)较电流判据(包括再活化峰峰值电流ir/ia)能更灵敏地反映材料晶间腐蚀敏感性的变化.

关键词 ：再活化, 不锈钢, 晶间腐蚀, 敏化

Abstract：The susceptibility to intergranular corrosion(IGC)for 1Cr18Ni9Ti stainless steel has been studied by the electrochemical potentiodynamic reactivation(EPR)method and the oxalic acid etch test.Different criteria used in EPR test to evaluate the tendency of IGC have been analyzed in detail.All criteria are well correlated with the degree of sensitization.With increasing sensitization time,the value of criteria increases.Furthermore all criteria can sensitively and quantitatively reflect the diffeerence of material with lower sensitization In all criteria,the current ratio ir/ia and charge ratio Qr/Qa have better repeatability than the reactive current ir or the reactive charge Qr.The criteria of charge (Qr,Qr/Qa)are more sensitive than the criteria of current(ir, ir/ia).

Key words： reactivation stainless steel intergranular corrosion sensitization

收稿日期: 1999-07-21

ZTFLH:

TG172.9

通讯作者: 高中平

Corresponding author: Zhongping Gao

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	高中平
	陈范才
	赵常就
44.8K

引用本文:

高中平; 陈范才; 赵常就 . EPR法评价晶间腐蚀敏感性的各种判据的比较[J]. 中国腐蚀与防护学报, 2000, 20(4): 243-247 .
Zhongping Gao, Fancai Chen, Changjiu Zhao. COMPARING DIFFERENT CRITERIA OF EPR METHOD TO EVALUATE THE SUSCEPTIBILITY TO INTERGRANULAR CORROSION. J Chin Soc Corr Pro, 2000, 20(4): 243-247 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2000/V20/I4/243

[1] Duffaut F, Pouzet J P, Lacombe P. Potentiostatic study of structural modifications caused in a Ni-Cr-Fe alloy by heat treatment at 650℃[J]. Corrosion Science, 1966, 6(2):83-85
[2] Clarke W L, Carlson P C. Nondestructive measurement of sensitization of stainless steel: relation to high temperature stress corrosionbehavior[J]. 1980, 19(3): 16 - 23
[3] Akashi M. Kawamoto T.The effect of molybdenum addition on SCC susceptibility of stainless steels in oxygenated high temperature water[J]. Corrosion Engineering, 1978, 27(4): 165 - 171
[4]方智,张玉林,吴荫顺,等.电化学动电位再活化法评价308L不锈钢的晶间腐蚀敏感性[J].腐蚀科学与防护技术,1996, 8(2):87-93.
[5] Cihal V. Advances in the potentiodynamic reactivation method[J] .Werkstoffe und Korrosion, 1986, 37(11):587 - 591
[6] Scully J R. Kelly R G. An electrochemical test for detecting the intergranular corrosion susceptibility of a duplex stainless steel[J].Corrosion, 1986, 42(9): 537-542
[7] Frangini S. Mignone A. Modified electrochemical potentiokinetic reactivation mothod for detecting sensitization in 12wt% Cr ferriticstainless steels[J]. Corrosion, 1992, 48(9):715 - 726
[8] ASTM Book of Standards[S] .Vol, 10, A262, ASTM, Philadelphia, Pennsylvania, 1981

[1]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[2]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[3]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[4]	张浩, 杜楠, 周文杰, 王帅星, 赵晴. 模拟海水溶液中Fe³⁺对不锈钢点蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[5]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[6]	赵柏杰, 范益, 李镇镇, 张博威, 程学群. 不同类型接触面对316L不锈钢缝隙腐蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 332-341.
[7]	胡玉婷, 董鹏飞, 蒋立, 肖葵, 董超芳, 吴俊升, 李晓刚. 海洋大气环境下TC4钛合金与316L不锈钢铆接件腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 167-174.
[8]	秦越强, 左勇, 申淼. FLiNaK-CrF₃/CrF₂氧化还原缓冲熔盐体系对316L不锈钢耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(2): 182-190.
[9]	何壮,王兴平,刘子涵,盛耀权,米梦芯,陈琳,张岩,李宇春. 316L和HR-2不锈钢在盐酸液膜环境中的钝化与点蚀[J]. 中国腐蚀与防护学报, 2020, 40(1): 17-24.
[10]	武栋才,韩培德. 中温时效处理对SAF2304双相不锈钢耐蚀性的影响[J]. 中国腐蚀与防护学报, 2020, 40(1): 51-56.
[11]	骆鸿,高书君,肖葵,董超芳,李晓刚. 磁控溅射工艺对CrN薄膜及其腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(5): 423-430.
[12]	付安庆,赵密锋,李成政,白艳,朱文军,马磊,熊茂县,谢俊峰,雷晓维,吕乃欣. 激光表面熔凝对超级13Cr不锈钢组织与性能的影响研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 446-452.
[13]	孙晓光,韩晓辉,张星爽,张志毅,李刚卿,董超芳. 超低碳奥氏体不锈钢焊接接头耐腐蚀性及环保型化学钝化工艺研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 345-352.
[14]	李雨,关蕾,王冠,张波,柯伟. 机械应力对不锈钢点蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(3): 215-226.
[15]	李兆登,崔振东,侯相钰,高丽丽,王维珍,尹建华. 核级316LN不锈钢焊接接头在高温高压水中的腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 106-113.

Viewed

Full text

Abstract

Cited

Shared

Discussed