纳米晶Ni-Ag合金在600-700℃的空气氧化

中国腐蚀与防护学报

2001, Vol. 21

Issue (5): 257-264

研究报告

本期目录 | 过刊浏览

纳米晶Ni-Ag合金在600-700℃的空气氧化

赵泽良;牛焱;F.Gesmundo

中科院金属所（南区）

OXIDATION BEHAVIOR OF NANOCRYSTALLINENi-Ag ALLOYS AT 600-700℃ IN AIR

;;

中科院金属所（南区）

全文: PDF(310 KB)

摘要: 利用球磨和热压致密化过程，得到富Ag和富Ni相均匀分布的纳米晶Ni-Ag双相合金.研究了含Ni分别为50 at%和75 at%的Ni-50Ag和Ni-25Ag合金在600～70 0℃空气中的氧化.Ni-50Ag合金形成了Ni内氧化结构，最外层为连续Ag层，其氧化速率大于纯Ni.相反，Ni-25Ag合金则形成了连续的NiO外氧化层且最外层为不连续的Ag层.Ni-25A g合金氧化初期服从抛物线速率常数关系，随后氧化速率显著减小甚至小于纯Ni.合金的双相结构特性以及合金中极小的晶粒尺寸导致了上述结果的产生.

关键词 ： Ni-Ag, 机械合金化, 纳米晶, 氧化, 双相合金

Abstract：Two Ni-Ag alloys, containing Ni of 50 at% and 75 at %, denoted as Ni-50Ag and Ni-25Ag were consolidated with hot pressing (HP) proce ssing after mechanical alloying (MA) for 80 hr. The nanocrystalline alloys have been oxidized in air at 600-700 ℃ for 24 hr.Ni-50Ag alloy undergoes an inte rna l oxidation of nickel associated with the formation of a continuous outermost la yer of silver metal and has oxidation rates larger than those of pure nickel. On the contrary, Ni-25Ag alloy forms a continuous NiO layer surmounted by a discon tinuous silver layer, while the internal oxidation is suppressed. These results are interpreted on the basis of the two-phase nature of the alloys and of their particularly small grain size.

Key words： mechanical alloying two-phase alloy Ni-Ag nanocryst alline oxidation

收稿日期: 2000-07-05

ZTFLH:

TG146.15

通讯作者: 赵泽良

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	赵泽良
	牛焱
	F.Gesmundo
44.8K

引用本文:

赵泽良; 牛焱; F.Gesmundo . 纳米晶Ni-Ag合金在600-700℃的空气氧化[J]. 中国腐蚀与防护学报, 2001, 21(5): 257-264 .

链接本文:

https://www.jcscp.org/CN/Y2001/V21/I5/257

[1]HadjipanayisGC ,SiegelRW ,etal.NanophaseMaterials:Synthesis,Properties,Applications[M ].London:KluwerAcademicPublishers,1994
[2]MassalskiTB ,OkamotoH ,SubramanianPR ,etalEds.BinaryAlloyPhaseDiagrams[M ].2nded.,ASMInternational,Ma terialsPark,OH ,1990,64.
[3]ZhaoZL ,ZhaoY ,NiuY ,etal.Synthesisandcharacteristicsofconsolidatednanocrystallinetwo-phaseAg50Ni50 alloybyhotpressing[J].J .All.Comp.,2000,307:254
[4]KofstadF .HighTemperatureCorrosion[M ].London:ElsevierAppliedScience,1988
[5]AtkinsonA ,RaylorRL ,HughesAE .HighTemperatureCorrosion[M ].Houston:NACE ,1983,110
[6]WagnerC .Theoreticalanalysisofthediffusionprocessdeterminingtheoxidationrateofalloys[J].J .Electrochem.Soc.,1952,99:369
[7]RappRA .Microstructuresandmechanismofinternaloxidationitseffectandpreventioninhightemperaturealloyoxidation[J].Corrosion,1965,21:382
[8]GesmundoF ,NiuY ,VianiF .Possiblescalingmodesinhigh-temperatureoxidationoftwo-phasebinaryalloys,PartII:lowoxidantpressures[J].Oxid.Metall.,1995,43:379
[9]CrankJ.TheMathematicsofDiffusion[M].Oxford:ClarendonPress,UK ,1976.
[10]WangG ,GleesonB ,DouglassDL .Adiffusionalanalysisoftheoxidationofbinarymultiphasealloys[J].Oxid.Met.,1990,35:333
[11]HartEW .Ontheroleofdislocationinbulkdiffusion[J].ActaMetall.,1957,5(5):597
[12]WangF .TheeffectofnanocrystallizationontheselectiveoxidationandadhesionofAl2O3scales[J].Oxid.Met,1997,48:215
[13]GesmundoF ,VianiF ,NiuY .Theinternaloxidationoftwo-phasebinaryalloysunderlowoxidantpressures[J].OxidMet.,1996,45:51
[14]NiuY ,GesmundoF ,VianiF .Theairoxidationoftwo-phaseCu-Crat700-900℃[J].OxidMet.,1997,48:357
[15]ChiangKT ,MeierGH ,PettitFS .MicroscopyofOxidationIII[C],NewcombeSB ,LittleJA ,Ed.London:TheInstituteofMaterials,1997,453
[16]GuruswamyS ,ParkSM ,HirthJP ,etal.InternaloxidationofAg-Inalloys:stressreliefandtheinfluenceofimposedstrain[J].OxidMet.,1986,26:77

[1]	魏征, 马保吉, 李龙, 刘潇枫, 李慧. 镁合金表面超声滚压预处理对微弧氧化膜耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[2]	刘晓, 王海, 朱忠亮, 李瑞涛, 陈震宇, 方旭东, 徐芳泓, 张乃强. 电站用奥氏体耐热钢HR3C与Sanicro25在超临界水中的氧化特性[J]. 中国腐蚀与防护学报, 2020, 40(6): 529-538.
[3]	谢冬柏, 洪昊, 王文, 彭晓, 多树旺. 模拟燃烧环境介质和温度对不锈钢表面氧化物形态的影响研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 358-366.
[4]	曹京宜, 方志刚, 陈晋辉, 陈志雄, 殷文昌, 杨延格, 张伟. 5083铝合金表面单致密微弧氧化膜的制备及其性能研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[5]	王廷勇, 董如意, 许实, 王辉. 石墨烯改性Ti/IrTaSnSb-G金属氧化物阳极在低温和低盐NaCl溶液中的电化学性能[J]. 中国腐蚀与防护学报, 2020, 40(3): 289-294.
[6]	方旭东, 刘晓, 徐芳泓, 李瑞涛, 朱忠亮, 张乃强. 超超临界电站国产奥氏体钢C-HRA-5在超临界水中的氧化特性[J]. 中国腐蚀与防护学报, 2020, 40(3): 266-272.
[7]	王英君, 刘洪雷, 王国军, 董凯辉, 宋影伟, 倪丁瑞. 新型高强稀土Al-Zn-Mg-Cu-Sc铝合金的阳极氧化及其抗腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 131-138.
[8]	秦越强, 左勇, 申淼. FLiNaK-CrF₃/CrF₂氧化还原缓冲熔盐体系对316L不锈钢耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(2): 182-190.
[9]	郑艳欣, 刘颖, 宋青松, 郑峰, 贾玉川, 韩培德. 含铁铜基陶瓷复合材料高温氧化行为与耐磨性研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 191-198.
[10]	范益,陈林恒,蔡佳兴,代芹芹,马宏驰,程学群. 热轧AH36船板钢在室内仓储条件下的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 10-16.
[11]	徐勋虎,何翠群,向军淮,王玲,张洪华,郑晓冬. Co-20Re-25Cr-1Si合金在0.1 MPa纯O₂中的高温氧化行为[J]. 中国腐蚀与防护学报, 2020, 40(1): 75-80.
[12]	姜冬雪,付颖,张峻巍,张伟,辛丽,朱圣龙,王福会. 钛合金表面Al₂O₃陶瓷膜制备及性能研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 469-476.
[13]	王毅,张盾. 铋系可见光催化海洋防污材料研究进展[J]. 中国腐蚀与防护学报, 2019, 39(5): 375-386.
[14]	陈嘉晨,王忠维,乔利杰,岩雨. 机械摩擦磨损与电化学腐蚀在特殊环境中的作用机制[J]. 中国腐蚀与防护学报, 2019, 39(5): 404-410.
[15]	魏欣欣,张波,马秀良. FeCr₁₅Ni₁₅单晶600 ℃下热生长氧化膜的TEM观察[J]. 中国腐蚀与防护学报, 2019, 39(5): 417-422.

Viewed

Full text

Abstract

Cited

Shared

Discussed