硫脲-二乙烯三胺缩聚物对混凝土中钢筋的缓蚀作用

王胜先;林薇薇;张鉴清

同济大学混凝土材料研究国家重点实验室

Corrosion Inhibition Behavior of Diethylenetriamine/ Thiourea Adduct for Steel Reinforcements in Concrete

;;;

同济大学混凝土材料研究国家重点实验室

全文: PDF(197 KB)

摘要: 用动电位极化曲线及电化学阻抗谱研究了硫脲—二乙烯三胺缩聚物在混凝土孔隙模拟液及混凝土中对钢筋腐蚀抑制作用。结果表明它是一种混合型缓蚀剂，对钢筋的点蚀有较好的抑制作用。在模拟液中添加1%的该缓恂剂就可以使对氯离子的容忍度从0.02mol/L提高到0.1mol/L.它与NaNO3有较好的协同作用.它既能吸附于钢筋表面,又能提高混凝土的密实程度,减缓腐蚀介质向混凝土内的渗透.能谱分析的结果表明它能够富集于钢筋/混凝土界面.

关键词 ：钢筋混凝土, 腐蚀, 缓蚀剂, 聚合物

Abstract：A new polymer DETA-TU(isomolar adduct of diethylenetriamine and thiourea) was first introduced into reinforced concrete to inhibit corrosion of the embedded steel reinforcements. Its inhibition behavior and mechanism were studyied with linear polarization, Tafel polarization, EIS method either in simulated pore solution(SPS) or in real concrete. The results showed that DETA-TUwas a mixing type inhibitor. A 1% dosage was sufficient to hinder the corrosion of steel bar in SPS cntaining 0.1 mol/L NaCl. The salt endurance was increased from 0.02mol/L to 0.10mol/L. The results also showed DETA-TU and NaNO2 had a significant synergistic effect for corrosion inhibition of reinforing bar, especially at lower NaNO2 concentration. The EIS revealed the double beneficial function of DETA-TU for reinforced concrete, i.e., densifying the concrete pore structure and adsorbing on the surface of the steel reinforcement. XPS analysis showed the inhibition was concentrated at the steel/ concrete interface. The concentration gradient of DETA-TU from the steel/concrete interface and bulk concrete eas crucial for its inhibition efficiency.

Key words： concrete corrosion inhibitor polymer

收稿日期: 1998-09-02

ZTFLH:

TG174.42

通讯作者: 王胜先

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	王胜先
	林薇薇
	张鉴清
44.8K

引用本文:

王胜先; 林薇薇; 张鉴清 . 硫脲-二乙烯三胺缩聚物对混凝土中钢筋的缓蚀作用[J]. 中国腐蚀与防护学报, 2000, 20(1): 15-21 .
. Corrosion Inhibition Behavior of Diethylenetriamine/ Thiourea Adduct for Steel Reinforcements in Concrete. J Chin Soc Corr Pro, 2000, 20(1): 15-21 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2000/V20/I1/15

[1]BerkeNS .Areviewofcorrosioninhibitorinconcrete [J].Materialsperformance ,1989,2 8(10 ) :4 1～ 4 4
[2 ]WO 87/0 6 958,Corrosioninreinforcedconcrete .
[3]PingGu ,ElliottS ,HristovaR ,etal.Astudyofcorrosioninhibitorperformanceinchloridecontaminatedconcretebyelectrochemicalimpedancespectroscopy [J].ACIMaterialsJournal,1997,94 (5) :385～ 395.
[4 ]PearsonRG .Hardandsoftacidsandbases [J].JAmChemSoc ,196 3,85(2 2 ) :3533～ 3539.
[5]Go iS ,AndradeC .Syntheticconcreteporesolutionchemistryandrebarcorrosionrateinthepresenceofchlorides [J].CementandConcreteResearch ,1990 ,2 0 (4 ) :52 5～ 539.
[6 ]Rodr姫ｇｕｅｚＰ ,Ram姫ｒｅｚＥ ,Gonz lezJA .Methodsforstudyingcorrosioninreinforcedconncrete [J].MagazineofConcreteResearch ,1994 ,4 6 (6 ) :81～ 90 .
[7]McCarterWJ.TheACresponseofhardenedcementpaste [J].CementandConcreteResearch ,1990 ,2 0 (6 ) :891～90 0 .
[8]PageCL .Mechanismofcorrosionprotectioninreinforcedconcretemarinestructures [J].Nature ,1975,2 58(11) :514～ 515.

[1]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[4]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[5]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[6]	白云龙, 沈国良, 覃清钰, 韦博鑫, 于长坤, 许进, 孙成. 硫脲基咪唑啉季铵盐缓蚀剂对X80管线钢腐蚀的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[7]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[8]	王亚婷, 王棵旭, 高鹏翔, 刘冉, 赵地顺, 翟建华, 屈冠伟. 淀粉接枝共聚物对Zn的缓蚀性能[J]. 中国腐蚀与防护学报, 2021, 41(1): 131-138.
[9]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[10]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[11]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[12]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[13]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[14]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[15]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.

Viewed

Full text

Abstract

Cited

Shared

Discussed