扰动溶液中模拟剥离涂层底部Q345钢阴极极化水平

吴志斌魏英华李京孙超

中国科学院金属研究所金属腐蚀与防护国家重点实验室沈阳 110016

Cathodic Polarization Level of Q345 Steel beneath Simulated Disbonded Coating in Agitated Solution

WU Zhibin, WEI Yinghua, LI Jing, SUN Chao

State Key Laboratory for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China

全文: PDF(1263 KB)

摘要: 利用分段电极测量了阴极保护下矩形模拟剥离涂层底部Q345钢的电位和电流分布，研究了浓度为0.5 mol/L的静态溶液及充氧动态溶液中，不同阴极保护电位、缝隙宽度以及漏点尺寸条件下缝内阴极极化水平。结果表明，充氧扰动作用减弱了缝内阴极极化水平，致使钢片在扰动溶液环境中比在静态溶液需要更高水平的阴极保护，才能有效抑制缝内金属腐蚀。缝隙宽度和漏点尺寸对充氧扰动改变缝内极化水平的影响明显。

关键词 ：充氧扰动, 阴极保护, 缝隙宽度, 漏点尺寸

Abstract：Potential and current distributions in a cathodically polarized crevice between a simulated disbonded coating and segmented Q345 steels were measured, and the cathodic polarization level in crevice was studied at various level of cathodic protection, and various size of crevice thickness and holiday. The results revealed that agitation decreased the polarization level in crevice, leading to the fact that a higher level of cathodic protection was required to inhibit the metal corrosion in crevice in agitated solution, compared with that in static solution. Crevice thickness and holiday size had significant influence on the phenomenon of agitation weakening the polarization level in crevice.

Key words： agitation cathodic protection crevice thickness holiday size

ZTFLH:

TG172

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
44.8K

引用本文:

吴志斌魏英华李京孙超. 扰动溶液中模拟剥离涂层底部Q345钢阴极极化水平[J]. 中国腐蚀与防护学报, 2013, 33(2): 104-108.
. Cathodic Polarization Level of Q345 Steel beneath Simulated Disbonded Coating in Agitated Solution. Journal of Chinese Society for Corrosion and protection, 2013, 33(2): 104-108.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2013/V33/I2/104

[1] Deflorian F, Rossi S. An EIS study of ion diffusion through organic coatings [J]. Electrochim. Acta, 2006, 51: 1736-1744
[2] Toncre A C. On achieving polarization beneath unbonded pipe coatings [J]. Mater. Performance, 1984, 23(8): 22-27
[3] Brousseau R, Qian S. Distribution of steady-state cathodic currents underneath a disbonded coating [J]. Corrosion, 1994, 50(12): 907-911
[4] Chin D T, Sabde G M. Current distribution and electrochemical environment in a cathodically protected crevice [J]. Corrosion, 1999, 55(3): 229-237
[5] Perdomo J J, Song I. Chemical and electrochemical conditions on steel under disbonded coatings: the effect of applied potential, solution conductivity, crevice thickness and holiday size [J]. Corros. Sci., 2000, 42: 1389-1415
[6] Li Z F, Gan F, Mao X . A study on cathodic protection against crevice corrosion in dilute NaCl solutions [J]. Corros. Sci., 2002, 44: 689-701
[7] Chen X, Li X G, Du C W, et al. Effect of cathodic protection on corrosion of pipeline steel under disbonded coating [J]. Corros. Sci., 2009, 51: 2242-2245
[8] Yan M C, Wang J Q, Ke W, et al. Effectiveness of cathodic protection under simulated disbonded coating on pipelines [J]. J. Chin. Soc. Corros. Prot., 2007, 27(5): 257-262
(闫茂成, 王俭秋, 柯伟等. 埋地管线剥离覆盖层下阴极保护的有效性 [J]. 中国腐蚀与防护学报, 2007, 27(5): 257-262)
[9] Chen X, Li X G, Du C W, et al. Crevice corrosion behavior of the steel X70 under cathodic polarization [J]. Acta Metall. Sin., 2008, 44(12): 1431-1438
(陈旭, 李晓刚, 杜翠薇等. 阴极极化条件下X70钢的缝隙腐蚀行为 [J]. 金属学报, 2008, 44(12): 1431-1438)
[10] Jack T R, Van Boven G, Wilmott M, et al. Cathodic protection potential penetration under disbonded pipeline coating [J]. Mater. Performance, 1994, 33: 17-21
[11] Gan F, Sun Z W, Sabde G, et al. Cathodic protection to mitigate external corrosion of underground steel pipe beneath disbonded coating [J]. Corrosion, 1994, 50(10): 804-816
[12] Fessler R R, Markworth A J, Parkins R N. Cathodic protection levels under disbonded coatings [J]. Corrosion, 1983, 39(1): 20-25

[1]	戴明杰, 刘静, 黄峰, 胡骞, 李爽. 基于正交方法研究阴极保护电位波动下X100管线钢的点蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(5): 425-431.
[2]	梁毅, 杜艳霞. 交流干扰和阴极保护协同作用下的腐蚀评判标准与机理研究进展[J]. 中国腐蚀与防护学报, 2020, 40(3): 215-222.
[3]	解璇, 刘莉, 王福会. TiO₂的制备及表面修饰工艺对其光电化学阴极保护性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(2): 123-130.
[4]	赵书彦,童鑫红,刘福春,翁金钰,韩恩厚,郦晓慧,杨林. 环氧富锌涂层防腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 563-570.
[5]	王贵容,邵亚薇,王艳秋,孟国哲,刘斌. 阴极保护电位对破损环氧涂层阴极剥离的影响[J]. 中国腐蚀与防护学报, 2019, 39(3): 235-244.
[6]	廖彤,马峥,李蕾蕾,马秀敏,王秀通,侯保荣. Fe₂O₃/TiO₂纳米复合材料对304不锈钢的光生阴极保护性能[J]. 中国腐蚀与防护学报, 2019, 39(1): 36-42.
[7]	邱萍, 杨连捷, 宋玉, 杨鸿飞. 添加DMF对TiO₂薄膜光生阴极保护性能影响研究[J]. 中国腐蚀与防护学报, 2018, 38(3): 289-295.
[8]	寇杰, 张新策, 崔淦, 杨宝安. 储罐底板阴极保护电位分布研究进展[J]. 中国腐蚀与防护学报, 2017, 37(4): 305-314.
[9]	王晓霖, 闫茂成, 舒韵, 孙成, 柯伟. 破损涂层下管线钢的交流电干扰腐蚀行为[J]. 中国腐蚀与防护学报, 2017, 37(4): 341-346.
[10]	王廷勇,马兰英,汪相辰,张海兵,陈凯,闫永贵. 某核电站凝汽器在海水中阴极保护参数的研究及应用[J]. 中国腐蚀与防护学报, 2016, 36(6): 624-630.
[11]	杨霜,唐囡,闫茂成,赵康文,孙成,许进,于长坤. 温度对X80管线钢酸性红壤腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2015, 35(3): 227-232.
[12]	刘在健,王佳,张彭辉,王燕华,张源. 5083铝合金在海水中的腐蚀行为及其阴极保护研究[J]. 中国腐蚀与防护学报, 2015, 35(3): 239-244.
[13]	许洪梅, 柳伟, 曹立新, 苏革, 高荣杰. 304不锈钢表面ZnO/TiO₂复合薄膜的制备与光生阴极防腐蚀性能研究[J]. 中国腐蚀与防护学报, 2014, 34(6): 507-514.
[14]	范丰钦, 宋积文, 李成杰, 杜敏. 海水流速对DH36平台钢阴极保护的影响[J]. 中国腐蚀与防护学报, 2014, 34(6): 550-557.
[15]	邱景, 杜敏, 陆原, 张颖, 郭海军, 李成杰. X65碳钢在模拟油田采出水中的阴极保护研究[J]. 中国腐蚀与防护学报, 2014, 34(4): 333-338.

Viewed

Full text

Abstract

Cited

Shared

Discussed