中国腐蚀与防护学报  2012, Vol. 32 Issue (4): 322-326    
  研究报告 本期目录 | 过刊浏览 |
X80管线钢钝化膜在各种高浓度NaHCO3溶液中的电化学行为
范林,李晓刚,杜翠薇,刘智勇
北京科技大学腐蚀与防护中心 北京100083
ELECTROCHEMICAL BEHAVIOR OF PASSIVE FILMS FORMED ON X80 PIPELINE STEEL IN VARIOUS CONCENTRATED NaHCO3 SOLUTIONS
FAN Lin,LI Xiaogang,DU Cuiwei,LIU Zhiyong
Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083
全文: PDF(575 KB)  
摘要: 采用动电位极化曲线、恒电位极化曲线、电化学阻抗谱(EIS)、Mott-Schottky分析等电化学方法研究了X80管线钢在各种高浓度的NaHCO3溶液中形成钝化膜的电化学行为。结果表明, X80管线钢钝化膜的稳定性和耐蚀性会受到NaHCO3溶液浓度的影响。钝化膜电化学性质随HCO3-浓度升高而降低;内层Fe3O4的厚度不随HCO3-浓度变化,推测其形成与成膜电位有关;内外膜层厚度比随HCO3-浓度的升高而增大,钝化膜的稳定性和耐蚀性主要受外层γ-Fe2O3的影响。根据点缺陷(PDM)理论的分析认为,NaHCO3溶液浓度升高时钝化膜稳定性和耐蚀性的降低与溶液电导率的升高和HCO3-在缺陷点处吸附作用的增强有关。
关键词 X80管线钢钝化膜极化曲线电化学阻抗谱Mott-Schottky分析    
Abstract:The electrochemical behavior of the passive films formed on X80 pipeline steel in various concentrated NaHCO3 solutions was studied using potentiodynamic polarization curves, potentiostatic polarization curves, electrochemical impedance spectroscopy (EIS) as well as Mott-Schottky plots. The electrochemical test results indicated n-type semiconducting characters of the passive film, which was composed of two layers, with γ-Fe2O3 as the outer layer, and Fe3O4 as the inner layer. The properties of the passive films were influenced by the concentration of NaHCO3 solutions. The thickness of the inner layer merely remained constant, which was supposed to be dominated by the film forming polarization, whereas the thickness of the outer layer decreased with the increase of the concentration of NaHCO3 solution, which suggested that the outer layer plays a more important role to the corrosion resistance and stability of the passive film. According to the point defect model (PDM), higher donor density and lower thickness of the passive films was affected by the enhanced conductivity of the solution and the intensified adsorption of HCO3- at local defect sites with higher HCO3- concentration.
Key wordsX80 pipeline steel    passive film    polarization curve    EIS    Mott-Schottky plot
收稿日期: 2011-06-28     
ZTFLH: 

TG172

 
基金资助:

国家科技基础条件平台建设资助项目(2005DKA10-400)资助

通讯作者: 范林     E-mail: violin_fl@163.com
Corresponding author: FAN Lin     E-mail: violin_fl@163.com
作者简介: 范林,男,1982年生,博士,研究方向为管线钢的土壤腐蚀和应力腐蚀开裂行为

引用本文:

范林,李晓刚,杜翠薇,刘智勇. X80管线钢钝化膜在各种高浓度NaHCO3溶液中的电化学行为[J]. 中国腐蚀与防护学报, 2012, 32(4): 322-326.
FAN Lin, LI Xiao-Gang, DU Cui-Wei, LIU Zhi-Yong. ELECTROCHEMICAL BEHAVIOR OF PASSIVE FILMS FORMED ON X80 PIPELINE STEEL IN VARIOUS CONCENTRATED NaHCO3 SOLUTIONS. J Chin Soc Corr Pro, 2012, 32(4): 322-326.

链接本文:

https://www.jcscp.org/CN/      或      https://www.jcscp.org/CN/Y2012/V32/I4/322

[1] Fujimoto S, Tsuchiya H. Semiconductor properties and protective role of passive films of iron base alloys [J]. Corros. Sci., 2007, 49(1): 195-202

[2] Rangel C M, Silva T M, da Cunha Belo M. Semiconductor electro-chemistry approach to passivity and stress corrosion cracking susceptibility of stainless steels [J]. Electrochim. Acta, 2005, 50(25-26): 5076-5082

[3] Zeng Y M, Luo J L, Norton P R. A study of semiconducting properties of hydrogen containing passive films [J]. Thin Solid Films, 2004, 460(1-2): 116-124

[4] Bardwell J A, MacDougall B, Graham M J. Use of $^{18}$O/SIMS and electrochemical techniques to study the reduction and breakdown of passive oxide films on iron [J]. J. Electrochem. Soc., 1988, 135(2): 413-418

[5] Hamadou L, Kadri A, Benbrahim N. Characterization of passive films formed on low carbon steel in borate buffer solution (pH 9.2) by electrochemical impedance spectroscopy [J]. Appl. Surf. Sci., 2005, 252(5): 1510-1519

[6] Zeng Y M, Luo J L, Norton P R. Initiation and propagation of pitting and crevice corrosion of hydrogen-containing passive films on X70 micro-alloyed steel [J]. Electrochim. Acta, 2004, 49(5): 703-714

[7] Zeng Y M, Luo J L. Electronic band structure of passive film on X70 pipeline steel [J]. Electrochim. Acta, 2003, 48(23): 3551-3562

[8] Zhou J L, Li X G, Du C W, et al. Anodic electrochemical behavior of X80 pipeline steel in NaHCO3 solution [J]. Acta Metall. Sin., 2010, 46(2): 251-256 

      (周建龙, 李晓刚, 杜翠薇等. X80管线钢在NaHCO3溶液中的阳极电化学行为 [J]. 金属学报, 2010, 46(2): 251-256)

[9] Nagayama M, Cohen M. The anodic oxidation of iron in a neutral solution [J]. J. Electrochem. Soc., 1962, 109(9): 781-790

[10] Zhang G D, Guo W H, Yao W R. Electrochemical and photoelectrochemical measuring of the thickness of passive films formed on iron [J]. J. East Chin. Univ. Metall., 1990, 7(4): 46-50

     (张国栋, 郭万华, 姚文锐. 铁钝化膜厚度的电化学和光电化学测量 [J]. 华东冶金学院学报, 1990, 7(4): 46-50)

[11] Azumi K, Ohtsuka T, Sato N. Mott-Schottky plot of the passive film formed on iron in neutral borate and phosphate solutions [J]. J. Electrochem. Soc., 1987, 134(6): 1352-1357

[12] Ningshen S, Kamachi M U, Mittal V K, et al. Semiconducting and passive film properties of nitrogen-containing type 316LN stainless steels [J]. Corros. Sci., 2007, 49(2): 481-496

[13] Modiano S, Fugivara C S, Benedetti A V. Effect of citrate ions on the electrochemical behavior of low-carbon steel in borate buffer solutions [J]. Corros. Sci., 2004, 46(3): 529-545

[14] MacDonald D D. The point defect model for the passive state [J]. J. Electrochem. Soc., 1992, 139(12): 3434-3449

[15] Stimming U. Photoelectrochemical studies of passive films [J]. Electrochim. Acta, 1986, 31(4): 415-429

[16] MacDonald D D. Passivity-the key to our metals-based civilization [J]. Pure Appl. Chem., 1999, 71(6): 951-978

[17] Li J B, Zuo J E. The influence of temperature on the electrochemical properties of passive films formed on X80 pipeline steel [J]. J. Chin. Soc. Corros. Prot., 2009, 29(1): 40-43

     (李金波, 左剑恶. 温度对X80管线钢钝化膜电化学性能的影响 [J]. 中国腐蚀与防护学报, 2009, 29(1): 40-43)
[1] 冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[2] 白云龙, 沈国良, 覃清钰, 韦博鑫, 于长坤, 许进, 孙成. 硫脲基咪唑啉季铵盐缓蚀剂对X80管线钢腐蚀的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[3] 史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[4] 李子运, 王贵, 罗思维, 邓培昌, 胡杰珍, 邓俊豪, 徐敬明. 热带海洋大气环境中EH36船板钢早期腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 463-468.
[5] 朱丽霞, 贾海东, 罗金恒, 李丽锋, 金剑, 武刚, 胥聪敏. 外加电位对X80管线钢在轮南土壤模拟溶液中应力腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 325-331.
[6] 胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[7] 孙硕, 杨杰, 钱薪竹, 常人丽. Ni-Cr-P化学镀层的制备与电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(3): 273-280.
[8] 张瑞,李雨,关蕾,王冠,王福雨. 热处理对激光选区熔化Ti6Al4V合金电化学腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 588-594.
[9] 王霞,任帅飞,张代雄,蒋欢,古月. 豆粕提取物在盐酸中对Q235钢的缓蚀性能[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.
[10] 达波,余红发,麻海燕,吴彰钰. 等效电路拟合珊瑚混凝土中钢筋锈蚀行为的电化学阻抗谱研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 260-266.
[11] 严少坤,郑大江,韦江,宋光铃,周廉. 钝性纯Ti在人工海水中的电化学活化行为研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 123-129.
[12] 丰涵,宋志刚,吴晓涵,李惠,郑文杰,朱玉亮. 022Cr25Ni7Mo4N双相不锈钢选择性腐蚀行为与两相组织的关系研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 138-144.
[13] 达波,余红发,麻海燕,吴彰钰. 阻锈剂的掺入方式对全珊瑚海水混凝土中钢筋锈蚀的影响[J]. 中国腐蚀与防护学报, 2019, 39(2): 152-159.
[14] 刘东,向红亮,刘春育. 含Ag抗菌双相不锈钢表面腐蚀产物的XPS分析[J]. 中国腐蚀与防护学报, 2018, 38(6): 533-542.
[15] 刘明,程学群,李晓刚,卢天健. 低合金钢筋在水泥萃取液中钝化膜的耐蚀机理研究[J]. 中国腐蚀与防护学报, 2018, 38(6): 558-564.