服役环境条件下飞机结构铝合金材料孔蚀规律研究

张丹峰¹;谭晓明¹;马力²;陈跃良¹

1. 海军航空工程学院青岛分院航空机械系青岛 266041
2. 海军驻沈阳导弹专业军事代表室沈阳 110024

ALUMINUM PITTING CORROSION DAMAGE RULE UNDER SERVICE ENVIRONMENT

ZHANG Danfeng¹; TAN Xiaoming¹; MA Li²; CHEN Yueliang¹

1. Naval Aeronautical Engineering Academy Qingdao Branch; Qingdao 266041
2. Missile Military Representatives of Naval Equipment Department Shenyang; Shenyang 110024

全文: PDF(1342 KB)

摘要:

对某型退役飞机进行分解检查后发现其结构腐蚀十分严重，以某处不受力的铝合金结构为研究对象，进行细节结构的局部分解、清洗和检测；得到其腐蚀损伤尺寸、形态参数及其分布特性；基于统计分析获得的分布特性参数，考虑飞机结构实际服役过程中的随机性，建立服役环境条件下腐蚀损伤扩展的概率模型，经验证该模型可行。

关键词 ：铝合金, 孔蚀, 老旧飞机, 统计规律

Abstract：

A retired navy aircraft had serviced for more than twenty years in a southeast coastal airport, where the environment is high temperature, high humidity and high salt fog. The aircraft was torn down and then inspected, and it was found that its corrosion damage was serious. The aluminum structure was partly disassembled, clean and nondestructive inspected. The corrosion damage size, shape parameter and distribution characteristic were gained. Based on distribution parameter obtained through statistics analysis, a probabilistic model to predict corrosion damage growth under service environment was established, with considering of the randomness during corrosion process of aircraft structure. The results show that the theoretical model is very precise.

Key words： aluminum pitting corrosion aging aircraft statistical rule

收稿日期: 2008-11-13

ZTFLH:

V250.2

基金资助:

国家自然科学基金项目（50675221）资助

通讯作者: 谭晓明 E-mail: txm1111@sina.com

Corresponding author: TAN Xiaoming E-mail: txm1111@sina.com

作者简介: 张丹峰，女，1970年生，讲师，博士，研究方向为飞机结构腐蚀疲劳及寿命可靠性

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	张丹峰
	谭晓明
44.8K

引用本文:

张丹峰;谭晓明;马力;陈跃良. 服役环境条件下飞机结构铝合金材料孔蚀规律研究[J]. 中国腐蚀与防护学报, 2010, 30(1): 93-96.
ZHANG Dan-Feng, TAN Xiao-Meng. ALUMINUM PITTING CORROSION DAMAGE RULE UNDER SERVICE ENVIRONMENT. J Chin Soc Corr Pro, 2010, 30(1): 93-96.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2010/V30/I1/93

[1] Chen Q Z, Cheng Z H, Xi H Z, et al. Study on corrosion of aluminum alloy aircraft structure [J]. J. Chin. Soc. Corros. Prot.,2007, 27(6): 334-337
(陈群志, 程宗辉, 席慧智等. 飞机铝合金结构连接部位的腐蚀研究 [J]. 中国腐蚀与防护学报，2007, 27(6): 334-337)
[2] Brooks C L, Simpson D. Integrating real time age degradation into the structural integrity process [A]. Proceedings AGARD Workshop on Fatigue in the Presence of Corrosion [C]. Corfu,Greece, 1998: 195-207
[3] Harlow D G, Wei R P. A probability model for the growth of corrosion pits in aluminum alloys induced by constituent particles [J]. Eng. Fracture Mech.,1998, 59(3): 305-325
[4] Harlow D G, Wei R P. Probability approach for prediction of corrosion and corrosion fatigue life [J]. AIAA J. 1994, 32(10): 2073-2079
[5] Dolley E J, Wei R P. Importance of chemically short-crack-growth on fatigue life [A]. 2nd Joint NASA/FAA/DoD Conference on Aging Aircraft [C]. Williamsburg, VA,1998: 679-687
[6] Pan S, Sankaran M. Probabilistic estimation of pitting corrosion fatigue life [A]. AIAA/ASME/ASCE/ASC structure, Structural Dynamics, and Materials Conference and Exhibit 41st [C]. Atlanta,G A, 2000: 1644
[7] Pan S, Sankaran M. Damage tolerance approach for probabilistic pitting corrosion fatigue life prediction [J]. Eng. Fracture Mech., 2001,68: 1493-1507
[8] Chang H, Han E H, Wang J Q, et al. Effect of aircraft skin coating on fatigue life of LY12CZ aluminum alloy [J].J. Chin. Soc. Corros. Prot., 2006, 26(1): 34-36
(常红，韩恩厚，王俭秋等.飞机蒙皮涂层对LY12CZ铝合金腐蚀疲劳寿命的影响 [J].中国腐蚀与防护学报，2006, 26(1): 34-36)

[1]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[2]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[3]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[4]	曹京宜, 方志刚, 陈晋辉, 陈志雄, 殷文昌, 杨延格, 张伟. 5083铝合金表面单致密微弧氧化膜的制备及其性能研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[5]	王英君, 刘洪雷, 王国军, 董凯辉, 宋影伟, 倪丁瑞. 新型高强稀土Al-Zn-Mg-Cu-Sc铝合金的阳极氧化及其抗腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 131-138.
[6]	任建平,宋仁国. 双级时效对7050铝合金力学性能及氢脆敏感性的影响[J]. 中国腐蚀与防护学报, 2019, 39(4): 359-366.
[7]	夏俊捷,牛红志,刘敏,曹华珍,郑国渠,伍廉奎. 基于卤素效应的阳极氧化技术提高Ti48Al5Nb合金抗高温氧化性能[J]. 中国腐蚀与防护学报, 2019, 39(2): 96-105.
[8]	陈高红,胡远森,于美,刘建华,李国爱. 硫酸阳极化对2E12铝合金力学性能的影响[J]. 中国腐蚀与防护学报, 2018, 38(6): 579-586.
[9]	曹敏, 刘莉, 余钟芬, 李瑛, 王福会. 2A02铝合金在模拟海洋大气环境中的剥蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 502-510.
[10]	马景灵, 通帅, 任凤章, 王广欣, 李亚琼, 文九巴. L-半胱氨酸/ZnO缓蚀剂对3102铝合金在碱性溶液中电化学性能的影响[J]. 中国腐蚀与防护学报, 2018, 38(4): 351-357.
[11]	郝利新, 贾瑞灵, 张慧霞, 张伟, 赵婷, 翟熙伟. 7A52铝合金双丝MIG焊接头的不均匀性对其表面微弧氧化膜腐蚀防护作用的影响[J]. 中国腐蚀与防护学报, 2018, 38(3): 219-225.
[12]	杨钊, 时惠英, 蒋百灵, 葛延峰, 张静, 张曼玉, 李研. 脉冲电流对1050铝合金微弧氧化过程的影响[J]. 中国腐蚀与防护学报, 2018, 38(3): 283-288.
[13]	崔晓飞, 谭晓明, 王德, 钱昂. 铝合金表面聚氨酯涂层在加速实验条件下的老化机制及规律研究[J]. 中国腐蚀与防护学报, 2018, 38(1): 74-80.
[14]	孙超, 杨潇, 文玉华. 表面溅射高含铝奥氏体不锈钢合金涂层对316不锈钢抗高温氧化性能的影响[J]. 中国腐蚀与防护学报, 2017, 37(6): 590-596.
[15]	赵苇杭, 王浩伟, 蔡光义, 董泽华. AA6061铝合金在含盐薄液膜下的局部腐蚀与缓蚀机理[J]. 中国腐蚀与防护学报, 2017, 37(4): 366-374.

Viewed

Full text

Abstract

Cited

Shared

Discussed