含N、O络合物光敏智能涂层的制备及其性能研究

中国腐蚀与防护学报

2007, Vol. 27

Issue (5): 296-302

研究报告

本期目录 | 过刊浏览

含N、O络合物光敏智能涂层的制备及其性能研究

刘建华;李兰娟

北京航空航天大学材料科学与工程学院

Preparation and performance study of light-group sensitive coating with N、O complex

;

北京航空航天大学材料科学与工程学院

全文: PDF(378 KB)

摘要: 用光敏感化合物在紫外可见光照射下能发出荧光的特性，筛选了三种光敏感材料，分别将它们添加进环氧漆中制备光敏智能涂层涂覆在含钪铝合金的表面，对铝合金的早期腐蚀进行监测预警。用荧光光谱研究了光敏材料的荧光特性。通过全浸腐蚀试验和盐雾试验研究传感涂层中光敏物质的荧光特性变化与铝合金腐蚀的对应关系，光学显微及扫描电子显微分析表明荧光特征点处即为铝合金基体腐蚀过程中发生阳极过程的区域。探讨了传感涂层对腐蚀监测的灵敏度，并对光敏智能涂层监测铝合金腐蚀的工作机理进行了分析。研究表明，所选的三种光敏材料均能有效地监测到铝合金基体的腐蚀位置及腐蚀发展过程。

关键词 ：光敏材料, 铝合金, 腐蚀监测, 传感涂层

Abstract：Three kinds of light-group sensitive materials are chosen to incorporat into primer coating, coated on the aluminum alloy surface, so as to make sure their light sensitive performance for the early prediction of corrosion of the aluminum alloy. The relation between the characteristic changes of light-group sensitive materials in coating and corrosion rate was studied. The sensitivity of light-group sensitive materials for corrosion detection was discussed. Primary connection mode between the coating and the concentration of light-group sensitive materials is set up. Finally, the mechanism of the light-group sensitive coating for detecting corrosion of the aluminum alloy is analyzed. It is found that, the three kinds of light-group sensitive materials in the coating predicted efficiently the corrosion rate of the aluminum alloy substrate.

Key words： light-group sensitive aluminum alloy corrosion detection sensitive coating

收稿日期: 2006-04-04

ZTFLH:

TG17

通讯作者: 刘建华 E-mail: liujh@buaa.edu.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	刘建华
	李兰娟
44.8K

引用本文:

刘建华; 李兰娟 . 含N、O络合物光敏智能涂层的制备及其性能研究[J]. 中国腐蚀与防护学报, 2007, 27(5): 296-302 .
. Preparation and performance study of light-group sensitive coating with N、O complex. J Chin Soc Corr Pro, 2007, 27(5): 296-302 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2007/V27/I5/296

[1]Zhu X R,Wang X R.Corrosion and Detection for Metals in SeaEnvironment[M].Beijing:National Defense Industrial Press,1999(朱相荣,王相润.金属材料的海洋腐蚀与防护[M].北京:国防工业出版社,1999)
[2]Sehgal R,Tiwari A,Sood V.Astudyon fitness-for-service assessmentfor crack-like defects and corrosion in nuclear reactor pressuretubes[J].Relia.Eng.Syst.Safe.,2005,89(2):227-235
[3]Malshe V C,Sangaj W S.A simple method for detection of the onsetof corrosion of mild steel panel[J].Prog.Org.Coat.,2005,53(4):312-318
[4]Bosch R W.Electrochemical impedance spectroscopyfor the detectionof stress corrosion cracks in aqueous corrosion system at ambientand high temperature[J].Corros.Sci.,2005,47(1):125-129
[5]Ing M,Austin S,Lyous R.Cover zone properties influencing acousticemission due to corrosion[J].Cem.Concrete.Res.,2005,35(2):284
[6]Ali J H,Wang W B,Alfano R R,et al.Detection of corrosionand cracking beneath paint using photonic techniques[J].Theoretical and Applied Fracture Mechanics,2004,41:1-6
[7]Johnson R E,Agarwala V S.Fluorescence based chemical sensorsfor corrosion detection[J].Corrosion 97,NACE,Houston,TX,1997,304
[8]Mukund P Si bi,Zhengang Zong.Determinationofcorrosiononaluminumalloy under protective coatings using fluorescent probes[J].Press Org.Coat.,2003,47:8
[9]Liu J H,Li L J,Li S Mi.Using Light-Group Sensitive Materialsas Early Warning Indicators for Corrosion of Al Alloys.MaterialScience and Engineering New Progress[M].Beijing:MetallurgyIndustry Press,2004:1393(刘建华,李兰娟,李松梅.铝合金早期腐蚀预警光基敏感涂层的研制.2004年材料科学与工程新进展[M].北京:冶金工业出版社,2004:1393)

[1]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[2]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[3]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[4]	曹京宜, 方志刚, 陈晋辉, 陈志雄, 殷文昌, 杨延格, 张伟. 5083铝合金表面单致密微弧氧化膜的制备及其性能研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[5]	王英君, 刘洪雷, 王国军, 董凯辉, 宋影伟, 倪丁瑞. 新型高强稀土Al-Zn-Mg-Cu-Sc铝合金的阳极氧化及其抗腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 131-138.
[6]	任建平,宋仁国. 双级时效对7050铝合金力学性能及氢脆敏感性的影响[J]. 中国腐蚀与防护学报, 2019, 39(4): 359-366.
[7]	夏俊捷,牛红志,刘敏,曹华珍,郑国渠,伍廉奎. 基于卤素效应的阳极氧化技术提高Ti48Al5Nb合金抗高温氧化性能[J]. 中国腐蚀与防护学报, 2019, 39(2): 96-105.
[8]	陈高红,胡远森,于美,刘建华,李国爱. 硫酸阳极化对2E12铝合金力学性能的影响[J]. 中国腐蚀与防护学报, 2018, 38(6): 579-586.
[9]	曹敏, 刘莉, 余钟芬, 李瑛, 王福会. 2A02铝合金在模拟海洋大气环境中的剥蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 502-510.
[10]	马景灵, 通帅, 任凤章, 王广欣, 李亚琼, 文九巴. L-半胱氨酸/ZnO缓蚀剂对3102铝合金在碱性溶液中电化学性能的影响[J]. 中国腐蚀与防护学报, 2018, 38(4): 351-357.
[11]	郝利新, 贾瑞灵, 张慧霞, 张伟, 赵婷, 翟熙伟. 7A52铝合金双丝MIG焊接头的不均匀性对其表面微弧氧化膜腐蚀防护作用的影响[J]. 中国腐蚀与防护学报, 2018, 38(3): 219-225.
[12]	杨钊, 时惠英, 蒋百灵, 葛延峰, 张静, 张曼玉, 李研. 脉冲电流对1050铝合金微弧氧化过程的影响[J]. 中国腐蚀与防护学报, 2018, 38(3): 283-288.
[13]	崔晓飞, 谭晓明, 王德, 钱昂. 铝合金表面聚氨酯涂层在加速实验条件下的老化机制及规律研究[J]. 中国腐蚀与防护学报, 2018, 38(1): 74-80.
[14]	孙超, 杨潇, 文玉华. 表面溅射高含铝奥氏体不锈钢合金涂层对316不锈钢抗高温氧化性能的影响[J]. 中国腐蚀与防护学报, 2017, 37(6): 590-596.
[15]	赵苇杭, 王浩伟, 蔡光义, 董泽华. AA6061铝合金在含盐薄液膜下的局部腐蚀与缓蚀机理[J]. 中国腐蚀与防护学报, 2017, 37(4): 366-374.

Viewed

Full text

Abstract

Cited

Shared

Discussed