应用原子力显微镜研究硫酸盐还原菌对A3钢的腐蚀

林晶;阎永贵;陈光章;马力;钱建华

腐蚀与防护国防科技重点实验室

APPLICATION OF ATOMIC FORCE MICROSCOPY IN STUDY OF SULFATE-REDUCING BACTERIA TO A3 STEEL

;;;;

腐蚀与防护国防科技重点实验室

全文: PDF(1967 KB)

摘要: 应用原子力显微镜（AFM）研究硫酸盐还原菌（SRB）、微生物膜、腐蚀产物膜和A3钢腐蚀后的表面形貌，获得了高分辨率、清晰的图像.测得了SRB的大小，微生物膜、腐蚀产物膜的厚度和形成的点蚀孔深度.结果表明，A3钢的微生物腐蚀过程是先形成致密的硫化物膜，然后微生物在其上面聚集附着形成微生物膜；A3钢的微生物腐蚀主要以点蚀形式发生.

关键词 ：原子力显微镜, 磷酸盐还原菌, 微生物膜, 腐蚀

Abstract：The morphology of sulfate- reducing bacteria (SRB),microbial biofilms，corrosion product film and corroded A3 steel have been observed by atomic force microscopy (AFM).The results of high-resolution topographical images gave the information of the size of the cell， the thickness of biofilms and corrosion product film and the pitting corrosion depth. It can be concluded that compact sulphide films were formed on the surface of A3 steel and then microbiologically attached and formed biofilms during the process of microbiologically influenced corrosion.The corrosion of A3 steel mainly presents pitting corrosion character.

Key words： atomic force microscopy sulfate- reducing bacteria biofilms corrosion product film A3 steel

收稿日期: 2005-10-26

ZTFLH:

TG172.82

通讯作者: 林晶 E-mail: linlin681020@yahoo.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	林晶
	阎永贵
	陈光章
	马力
	钱建华
44.8K

引用本文:

林晶; 阎永贵; 陈光章; 马力; 钱建华 . 应用原子力显微镜研究硫酸盐还原菌对A3钢的腐蚀[J]. 中国腐蚀与防护学报, 2007, 27(2): 70-.

链接本文:

https://www.jcscp.org/CN/Y2007/V27/I2/70

[1]Binning G,Quate C,Gerber C.Atomic force microscopy[J].Phys.Rev.Lett.,1986,56:930-935
[2]Hadley R F.Microbiological anaerobic corrosion of steel pipeline[J].Oil and Gas,1939,38(19):92-96
[3]Minchin LJ.Anaerobic corrosion[J].Coke and Gas,1956,18(12):495-504
[4]Butlin K R,Vemon W H,Whiskin L.Investigation on undergroundcorrosion[J].Water.Sanit.Eng.,1952,2:468-472
[5]Kulman F F.Microbiological corrosion of buried steel pipe[J].Cor-rosion,1953,9(1):11-18
[6]Iverson W P.Research on the mechanisms of anaerobic corrosion[J].Int.Biodeterior.Biodegrad.,2001,47(2):63-70
[7]Puekorius.Recommended Practice for Biological Analysis of WaterFlood Injestion Waters.API RP-38,1959
[8]Hou B R.Corrosion Theory and Application in Marine Environment[M].Beijing:Science Publishing House,1998,6(侯保荣.海洋腐蚀环境理论及其应用[M].北京:科学出版社,1998,6)
[9]Li X B,Wang J,Wang W.The electrochemical method of biofilmmo-nitoring in seawater[J].J.Chin.Soc.Corros.Prot.,2005,25(2):84-87(李相波,王佳,王伟.海洋环境微生物附着的电化学检测技术[J].中国腐蚀与防护学报,1992,25(2):84-87)
[10]Caldwell D E,Korber D R,Lawrence J R.Imaging of bacterial cellsby fluorescence exclusion using scanning confocal laser microscopy[J].Microb.Methods,1992,2:249-261
[11]Videla H A.Corrosion products and biofilm interactions in the in-fluenced corrosion of steel[J].Corrosion,2002,2557:1-10.
[12]Zhu X R,Wang X R.Corrosion and Protection of Metals in MarineEnvironment[M].Beijing:Defence Industry Press,1993(朱相荣,王相润.金属材料的海洋腐蚀与防护[M].北京:国防工业出版社,1993)
[13]Li C X,Kwong Yu Chan.Application of atomic force microscopy inthe study of microbiologically influenced corrosion[J].Mater.Char-act,2002,48:195-203
[14]Fang Herbert HP,Kwong Yu Chan,Li C X.Quantification of bac-terial adhesion forces using atomic force microscopy[J].J.Microbi-ol.Methods,2000,40:89-97
[15]Hctor A Videla.Comparative study of the corrosion product filmsformed in biotic and abiotic media[J].Corrosion,99,163:1-12

[1]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[4]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[5]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[6]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[7]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[8]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[9]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[10]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[11]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[12]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[13]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[14]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[15]	艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.

Viewed

Full text

Abstract

Cited

Shared

Discussed